Steel ladle slag reducing agent with high calcium oxide content, and preparation method thereof

A technology of high calcium oxide and reducing agent, which is applied in the field of converter steelmaking, can solve problems such as imperfections, and achieve the effect of improving cleanliness and good slag-gold reaction

Active Publication Date: 2013-12-25
BAOSHAN IRON & STEEL CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] The ladle slag reducing agent disclosed in the above prior art is not yet perfect in terms of reducing ability, rapid slagging, and sufficient removal of impurities

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel ladle slag reducing agent with high calcium oxide content, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A ladle slag reducing agent with high calcium oxide content, Al 42wt%, CaO 28wt%, SiO 2 0.5wt%, Al 2 o 3 15wt%, CaF 2 8wt%, MgO 4wt%, other balance.

[0036] The amount of ladle slag added is 4kg / t.s, the T-Fe content in the ladle slag is 23.6% before adding the ladle slag reducing agent, and the T-Fe content in the ladle slag is 1.5% after adding the ladle slag reducing agent. Other indicators of molten steel after refining are shown in Table 2.

Embodiment 2

[0038] A ladle slag reducing agent with high calcium oxide content, Al 48wt%, CaO 21.6wt%, SiO 2 1.0wt%, Al 2 o 3 20wt%, CaF 2 5.5wt%, MgO 1.0wt%, other balance.

[0039] The amount of ladle slag added is 2kg / t.s, the T-Fe content in the ladle slag is 25.7% before adding the ladle slag reducing agent, and the T-Fe content in the ladle slag is 3.2% after adding the ladle slag reducing agent. Other indicators of molten steel after refining are shown in Table 2.

Embodiment 3

[0041] A ladle slag reducing agent with high calcium oxide content, Al 46.5wt%, CaO 18wt%, SiO 2 2.0wt%, Al 2 o 3 22wt%, CaF 2 3.0wt%, MgO 3.1wt%, other balance.

[0042] The amount of ladle slag added is 2.5kg / t.s, the T-Fe content in the ladle slag is 24.9% before adding the ladle slag reducing agent, and the T-Fe content in the ladle slag is 1.8% after adding the ladle slag reducing agent. Other indicators of molten steel after refining are shown in Table 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a steel ladle slag reducing agent with high calcium oxide content, which comprises the components by mass percent: 42-48% of Al, 18-28% of CaO, 0.5-2.0% of SiO2, 15-22% of Al2O3, 3-8% of CaF2 and 1-4% of MgO. The steel ladle slag reducing agent has high calcium oxide content, and other components are synthesized at the same time, so that the steel ladle slag reducing agent is good in a metal-slag reaction and rapid in slagging, and is capable of realizing the reduction on steel ladle slag and giving full play to the desulfuration and deoxidation functions of steel ladle slag on molten steel as well as the adsorption function of the steel ladle slag on impurities; therefore, the cleanliness of the molten steel can be improved.

Description

technical field [0001] The invention relates to the field of converter steelmaking, in particular to a reducing agent for modifying ladle slag and a modification method using the reducing agent. Background technique [0002] The smelting of low-carbon ultra-low sulfur steel generally adopts the process of molten iron pretreatment - converter blowing - ladle furnace (LF) refining + RH vacuum refining. The molten iron that has been pretreated by desiliconization and desulfurization is added to the converter for blowing. After reaching the appropriate temperature and carbon content, the molten steel is tapped from the converter and enters the ladle. During the tapping process of the converter, a large amount of oxidizing converter slag will enter the ladle. In the subsequent LF and RH vacuum refining processes, these oxidative ladle slags will pollute the molten steel, form inclusions, and affect the quality of molten steel. It reacts as follows: [0003] y(FeO)+x[M]=M x o ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/04C21C7/06
Inventor 马志刚黄宗泽
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com