Inflaming retarding reinforcing polyolefin material and preparation method thereof

A polyolefin and flame retardant technology, applied in the field of polyolefin materials and their preparation, can solve the problems of fire and fire prevention, and achieve the effect of light weight and many times of reuse

Inactive Publication Date: 2012-07-18
HEFEI GENIUS NEW MATERIALS
View PDF2 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, bamboo fences, wooden templates, or temporarily unused square logs on the construction site can be used as platforms for workers to stand and store tools; among them, bamboo fences are used the most, and their main disadvantage is that they cannot be fireproof, so when building a building frame, if The high-temperature welding slag dripping from electric welding often causes fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inflaming retarding reinforcing polyolefin material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) The distribution ratio of each group is as follows:

[0037] Polypropylene: 40.6 parts

[0038] Talc powder: 30 parts

[0039] Ethylene-octene copolymer 5 parts

[0040] Decabromodiphenylethane: 18 parts

[0041] Sb 2 0 3 6 servings

[0042] Antioxidant 1010: 0.2 parts

[0043] Lubricant EBS: 0.2 parts.

[0044] (2) The above-mentioned mixture is fed into the twin-screw extruder by a feeder with precise metering, and is sheared and mixed at a high speed by the twin-screw, extruded by the machine head, drawn, air-cooled, pelletized, dried and packaged .

[0045] The process parameters of the twin-screw extruder are as follows: the temperature of each section of the screw should be controlled between 190-220°C, preferably between 190-210°C.

Embodiment 2

[0047] (1) The distribution ratio of each group is as follows:

[0048] Polypropylene: 32.6 parts

[0049] Fiberglass: 45 parts

[0050] Maleic anhydride grafted PP:: 5 parts

[0051] Decabromodiphenylethane: 17 parts

[0052] Sb 2 0 3 : 5 servings

[0053] Antioxidant 1010: 0.1 parts

[0054] Antioxidant 168: 0.1 parts

[0055] Lubricant EBS: 0.2 parts.

[0056] (2) The above-mentioned mixture is sent into the twin-screw extruder by a feeder with precise metering, and glass fiber is added through the glass fiber inlet at the same time;

[0057] (3) After twin-screw high-speed shearing and mixing, extruding from the machine head, drawing, air cooling, pelletizing, drying and packaging.

[0058] The process parameters of the twin-screw extruder are as follows: the temperature of each section of the screw should be controlled between 190-220°C, preferably between 190-210°C.

Embodiment 3

[0060] (1) The distribution ratio of each group is as follows:

[0061] Polypropylene: 40.6 parts

[0062] Fiberglass: 15 parts

[0063] Ethylene-octene copolymer: 2 parts

[0064] Mica Powder: 15

[0065] Maleic anhydride grafted PP:: 3 parts

[0066] Decabromodiphenylethane: 18 parts

[0067] Sb 2 0 3 : 6 servings

[0068] Antioxidant 1010: 0.2 parts

[0069] Lubricant EBS: 0.2 parts.

[0070] (2) The above-mentioned mixture is sent into the twin-screw extruder by a feeder with precise metering, and glass fiber is added through the glass fiber inlet at the same time;

[0071] (3) After twin-screw high-speed shearing and mixing, extruding from the machine head, drawing, air cooling, pelletizing, drying and packaging.

[0072] The process parameters of the twin-screw extruder are as follows: the temperature of each section of the screw should be controlled between 190-220°C, preferably between 190-210°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an inflaming retarding reinforcing polyolefin material and a preparation method thereof. The inflaming retarding reinforcing polyolefin material comprises the following components by weight: 30 to 80 parts of polyolefin, 0 part to 10 parts of flexibilizer, 0 part to 45 parts of glass fiber, 0 part to 30 parts of filler, 2 to 30 parts of fire retardant, 0 part to 10 parts of graft, 0.1 to 0.4 part of antioxygen and 0.1 to 0.4 part of lubricant. The inflaming retarding reinforcing polyolefin material has good mechanical performance and processing performance, can achieve V-0 grade inflaming retarding, has a fireproof function and is suitable for extruding molding. The inflaming retarding reinforcing polyolefin material can be continuously extruded through an extruder to form boards for building external wall scaffolds and has the advantages of being low in cost, light in weight, good in rigidity balance, large in recycle times, variable in size, fireproof and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a polyolefin material and a preparation method thereof. Background technique [0002] In addition to the main role of building formwork in the construction process, exterior wall scaffolding is also essential, and the supporting systems of the two are also different. Exterior wall scaffolding is mainly used to build templates for construction workers, tie bolts, build reinforced slab walls and column steel structures, and walk on them or temporarily place construction tools when removing formwork. The exterior wall scaffolding is mainly divided into a steel pipe support system and a platform for workers to stand and store tools. At present, bamboo fences, wooden templates, or temporarily unused square logs on the construction site can be used as platforms for workers to stand and store tools; among them, bamboo fences are used the most, and their main disadvantage is tha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/06C08L51/06C08L23/08C08K13/02C08K13/04C08K7/14C08K3/26C08K3/34C08K5/03C08K5/06C08K3/22
Inventor 杨桂生石允慧孙利明
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap