Glue-free PVC (polyvinyl chloride) limited slip floor tile of ring structure and preparation method thereof
A ring-shaped structure and floor tile technology, applied in the field of plastic flooring, can solve the problems of low anti-slip coefficient of plastic flooring, unreasonable texture design and combination, and inability to further improve
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0025] The preparation method of PVC non-slip floor tile comprises the following steps:
[0026] (1) The first hot pressing combination process: if figure 1 1. The PVC anti-slip layer 10, the PVC base material layer 20, and the PVC middle material layer 30 are stacked sequentially from bottom to top, and then hot-pressed to form a support body 70. The hot pressing process adopts segmented pressurization, and its specific pressurization parameters are as follows:
[0027]
[0028] The heating temperature is 130° C. for 24 minutes.
[0029] Among them, the material formula of the PVC anti-slip layer is: in parts by weight, including: 58.5% of PVC with a degree of polymerization of 1000, 38.8% of plasticizer, 2.1% of stabilizer, 0.52% of toner, and 0.08% of calcium carbonate of 800 mesh , the sum of the total amount of the aforementioned substances is 100%;
[0030] (2) Secondary hot embossing texture process: such as figure 2 , the PVC wear-resistant layer 50 and the PVC...
Embodiment 2
[0039] The preparation method of PVC non-slip floor tile comprises the following steps:
[0040] (1) The first hot pressing combination process: if figure 1 1. The PVC anti-slip layer 10, the PVC base material layer 20, and the PVC middle material layer 30 are stacked sequentially from bottom to top, and then hot-pressed to form a support body 70. The hot pressing process adopts segmented pressurization, and its specific pressurization parameters are as follows:
[0041]
[0042] The heating temperature is 130° C. for 24 minutes.
[0043] Among them, the material formula of the PVC anti-slip layer is: in parts by weight, including: 63.5% of PVC with a degree of polymerization of 1000, 34.9% of plasticizer, 1.0% of stabilizer, 0.54% of toner, and 0.06% of calcium carbonate of 800 mesh , the sum of the total amount of the aforementioned substances is 100%;
[0044] (2) Secondary hot embossing texture process: such as figure 2 , the PVC wear-resistant layer 50 and the PVC...
Embodiment 3
[0053] The preparation method of PVC non-slip floor tile comprises the following steps:
[0054] (1) The first hot pressing combination process: if figure 1 1. The PVC anti-slip layer 10, the PVC base material layer 20, and the PVC middle material layer 30 are stacked sequentially from bottom to top, and then hot-pressed to form a support body 70. The hot pressing process adopts segmented pressurization, and its specific pressurization parameters are as follows:
[0055]
[0056] The heating temperature is 130° C. for 24 minutes.
[0057] Among them, the material formula of the PVC anti-slip layer is: in parts by weight, including: 61.5% of PVC with a degree of polymerization of 1000, 36.5% of plasticizer, 1.3% of stabilizer, 0.64% of toner, and 0.06% of 800-mesh calcium carbonate , the sum of the total amount of the aforementioned substances is 100%;
[0058] (2) Secondary hot embossing texture process: such as figure 2 , the PVC wear-resistant layer 50 and the PVC pr...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com