Water-based crack sandstone paint and preparation method thereof

A crack and sandstone technology, which is applied in the field of water-based crack sandstone paint and its preparation, can solve the problems of poor stability, easy peeling, and non-durability, and achieve the effects of strong viscosity and adsorption, convenient and fast use, and good stability

Active Publication Date: 2013-10-23
佛山市南海万磊建筑涂料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there are more and more water-based crack paint products on the market now, most of the crack material products are single-layer paint, and the product effect is mainly based on the color contrast to produce cracking effects, and the concave-convex three-dimensional effect is not strong.
In addition, the vast majority of water-based paints still have the following problems: first, the paint needs to be used within 2-4 hours after use, otherwise it will deteriorate; Cracking, some cracking is too large; third, the paint has poor stability after curing on the surface of the substrate, it is easy to peel off, and is not durable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based crack sandstone paint and preparation method thereof
  • Water-based crack sandstone paint and preparation method thereof
  • Water-based crack sandstone paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Formula (by mass percentage):

[0032] a) Primer composition:

[0033] Arabic resin 35%, elastic emulsion 22%, nano calcium carbonate powder 12%, titanium dioxide 10%, hydroxyethyl cellulose 0.5%, dispersant 0.5%, wetting agent 1.5%, bactericidal and antifungal agent 1%, film-forming aid Agent 1%, ethylene glycol 1%, alkali-soluble thickener 2.5%, deionized water 13%.

[0034] b) Topcoat composition:

[0035] Acrylic resin 30%, quartz sand 35%, nano calcium carbonate powder 20%, titanium dioxide 4%, elastic emulsion 1.5%, hydroxyethyl cellulose 0.5%, film-forming aid 1%, ethylene glycol 0.7%, dispersant 1%, defoamer 1%, bactericide antifungal agent 0.3%, deionized water 5%.

[0036] Preparation:

[0037] 1) Preparation of the primer composition: take 80% of the deionized water in the formula in a container, put Arabic resin, nano calcium carbonate powder and titanium dioxide into the deionized water under high-speed dispersion conditions, and continue high-speed dis...

Embodiment 2

[0045] Formula (by mass percentage):

[0046] a) Primer composition:

[0047] Arabic resin 40%, elastic emulsion 20%, nano calcium carbonate powder 10%, titanium dioxide 8%, hydroxyethyl cellulose 0.3%, dispersant 2%, wetting agent 3%, bactericidal and antifungal agent 0.5%, film-forming aid Agent 2%, ethylene glycol 1.2%, alkali-soluble thickener 1.5%, deionized water 11.5%.

[0048] b) Topcoat composition:

[0049] Acrylic resin 25%, quartz sand 30%, nano calcium carbonate powder 25%, titanium dioxide 4%, elastic emulsion 3%, hydroxyethyl cellulose 0.5%, film-forming aid 1.5%, ethylene glycol 1%, dispersant 0.5%, defoamer 1%, bactericide and antifungal agent 1.5%, deionized water 7%.

[0050] Preparation:

[0051]1) Preparation of the primer composition: take 80% of the deionized water in the formula in a container, put arabic resin, nano calcium carbonate powder and titanium dioxide into the deionized water under high-speed dispersion conditions, and continue high-speed...

Embodiment 3

[0054] Formula (by mass percentage):

[0055] a) Primer composition:

[0056] Arabic resin 40%, elastic emulsion 18%, nano calcium carbonate powder 8%, titanium dioxide 10%, hydroxyethyl cellulose 0.5%, dispersant 2%, wetting agent 3%, bactericidal and antifungal agent 1%, film-forming aid Agent 3.5%, ethylene glycol 1.5%, alkali-soluble thickener 2.5%, deionized water 10%.

[0057] b) Topcoat composition:

[0058] Acrylic resin 28%, quartz sand 33%, nano calcium carbonate powder 22%, titanium dioxide 2%, elastic emulsion 2%, hydroxyethyl cellulose 0.3%, film-forming aid 1.5%, ethylene glycol 0.7%, dispersant 1%, defoamer 0.5%, bactericidal antifungal agent 2%, deionized water 7%.

[0059] Preparation:

[0060] 1) Preparation of the primer composition: take 80% of the deionized water in the formula in a container, put Arabic resin, nano-calcium carbonate powder and titanium dioxide into the deionized water under the condition of high-speed dispersion, and continue high-spe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses water-based crack sandstone paint and a preparation method thereof. Water-soluble resin, nano calcium carbonate powder and titanium white are added into deionized water firstly, dispersing at high speed is carried out, then elastic emulsion, hydroxyethylcellulose, auxiliary material and residual deionized water are added, and dispersing at medium speed is carried out to obtain priming coat composition; and another container is taken, deionized water is added, firstly the auxiliary material is added under the condition of low-speed stirring, and acrylic resin, quartz sand, the nano calcium carbonate powder, the titanium white, the elastic emulsion and the hydroxyethylcellulose are continuously added under the condition of low-speed stirring, thus a top coat composition is prepared. The paint disclosed by the invention has the advantages of good stability, reusability, use convenience and the like; no cracking or irregular cracking is not caused after the paint disclosed by the invention is coated onto base material; and the paint disclosed by the invention can be well adhered onto the surface of the base material, and the paint is waterproof, durable and resistant to scrubbing.

Description

technical field [0001] The invention relates to the technical field of architectural coatings, in particular to a water-based cracked sandstone coating and a preparation method thereof. Background technique [0002] Paint, traditionally called paint in China, is a solid film that can be coated on the surface of an object by different construction techniques to form a solid adhesion, certain strength, and continuity. There are three main functions of traditional coatings: protection, decoration and concealment of product defects. With the development of the industry and the improvement of people's demand for use, people have higher and higher requirements for the decorative function of coatings. Crackle paint came into being as the times require. [0003] Crackle paint, that is, it can produce cracks after being painted on the surface of the wall. It has an elegant aesthetic feeling and belongs to the art type paint. High-end decorative craft works. Although there are mor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D105/00C09D133/04C09D133/00C09D7/12C09D5/28
Inventor 陈哈仔陈仲平
Owner 佛山市南海万磊建筑涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com