Grease for anti-weathering protection of stone

A weatherproof and grease-proof technology, applied in the direction of coating, can solve the problems of long-term regret, loss of load-bearing or decorative performance of building materials, etc., and achieve the effect of strong acid and alkali resistance and air permeability.

Inactive Publication Date: 2012-07-04
候世益
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The emergence of these diseases makes the load-bearing or decorative performance of building materials such as stone disappear, causing regret for a long time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A kind of grease used for stone anti-weather protection, take the following raw materials in weight fraction: polyorganosiloxane 42%, silane 38%, organic silicon 8%, refined quartz sand 8%, the above raw materials are mixed according to the proportion and then reacted Nano-processing is carried out in the kettle until the particle size is in the range of 0.1-100 nanometers. The invention has strong acid and alkali resistance, air permeability and water resistance, and is suitable for mineral substrates with adsorption properties, such as natural hard laterite, unglazed sintered bricks and stone materials for protective surfaces, asbestos cement boards, stucco, Mortar, natural stone, prefabricated stone, concrete, etc.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a grease for anti-weathering protection of stone, which is prepared from the following raw materials in percentage by weight: 40-45% of polyorganosiloxane, 35-40% of silane, 5-10% of organosilicon and 5-10% of refined quartz sand. The raw materials are proportionally mixed, and subjected to nano treatment in a reaction kettle until the particle size is 0.1-100nm. After the material is applied onto a substrate by dip coating, no trace can be left on the surface of the coated brick, ash mud, natural stone or concrete; and due to the non-drooping characteristic and the longer detention time on the substrate surface, the grease can permeate into the low-porosity building material more deeply. The grease has high acid / alkali resistance, high air permeability and favorable water resistance, and is applicable to adsorptive mineral substrates, such as natural hard laterite, glaze-free vitrified bricks, surface-protecting stone, asbestos cement boards, ash mud, glue mud, natural stone, prefabricated stone, concrete and the like.

Description

technical field [0001] The invention relates to the technical field of anticorrosion materials, in particular to a grease used for weathering protection of stone materials. Background technique [0002] Building materials, especially stone, are widely used. However, during the use of stone, it is often caused by its own water absorption characteristics and atmospheric environmental pollution, chemical corrosion, erosion of moss and lichen, frost cracking, long-term sunlight exposure, alternating cold and hot in winter and summer, and rainwater. Scouring and other natural factors are damaged, resulting in rust spots, water stains, oil stains and even cracks. The emergence of these diseases makes the load-bearing or decorative performance of building materials such as stone disappear, causing regret for a long time. The protection of stone needs to have the characteristics of water resistance, oil resistance and anti-fouling after one-time treatment. When it is used for outdo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D7/12
Inventor 候世益
Owner 候世益
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products