Preparation method for pentadiene petroleum resin

A technology for petroleum resin and pentadiene, applied in the field of synthesizing piperylene petroleum resin, can solve the problems of affecting the quality and application of the resin, high labor intensity, pollution of the three wastes, etc., and achieves easy continuous production, easy production control, The effect of improving economic efficiency

Active Publication Date: 2014-04-02
PETROCHINA CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned catalytic method has a fast reaction rate and mild conditions, and is currently the most widely used production process in industry. Its disadvantage is that the catalyst needs to be removed after the polymerization reaction is completed, but the removal of the catalyst is very critical, and if the removal is not clean, it will seriously affect Resin quality and application
Catalyst removal mainly includes alcohol washing method, water washing method, and liquid ammonia neutralization method. The common disadvantages of these methods are that the "three wastes" are seriously polluted, the amount of waste water is large, and the labor intensity is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for pentadiene petroleum resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Add solvent and boron trifluoride complex catalyst in proportion in reactor, then slowly drop piperylene concentrate (composition is shown in Table 1), catalyst and piperylene consumption ratio (weight) are 0.6, Control the rate of addition so that the reaction temperature is within 20°C. After the dropwise addition, the temperature was raised slowly, the reaction temperature was controlled at 20° C., and the reaction time was 10 h. After the reaction, deactivate with water, filter and use air stripping method to obtain the product piperylene petroleum resin, the resin yield reaches 82%, the hue (Fe—Co) can be obtained≤5, and the softening point is 89°C.

Embodiment 2

[0022] The experimental process and raw materials are the same as in Example 1, the catalyst to piperylene dosage ratio (weight) is 0.8, the reaction temperature is changed to 40° C., and the reaction time is 5 hours. After the reaction, unpolymer and solvent are flashed off to obtain the product piperylene petroleum resin with a resin yield of 84%, a hue (Fe-Co)≤4, and a softening point of 95°C.

Embodiment 3

[0024] The experimental process and raw materials are the same as in Example 1, the catalyst to piperylene dosage ratio (weight) is 0.5, the reaction temperature is changed to 50° C., and the reaction time is 6 hours. After the reaction is finished, unpolymer and solvent are flashed off to obtain the product piperylene petroleum resin with a resin yield of 88%, a hue (Fe-Co)≤4, and a softening point of 100°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method for pentadiene petroleum resin. The method comprises the following step of: synthesizing pentadiene petroleum resin by taking a pentadiene concentrate as a raw material and taking a boron trifluoride complex as a catalyst, wherein the catalyst consists of boron trifluoride and a complexing agent; the complexing agent consists of C1-C10 alcohol and benzene alkyl ether C6H5-OR; in the formula, R is methyl, ethyl or butyl; the molar ratio of the C1-C10 alcohol to the benzene alkyl ether is 2-8; the molar ratio of the boron triflouride to the complexing agent is 0.5-0.8; and a preparation method for the boron triflouride complex serving as the catalyst comprises the following steps of: adding the C1-C10 alcohol and the benzene alkyl ether into a reactor; cooling the materials in the reactor to 0 DEG C to 30 DEG C below zero while stirring; introducing boron triflouride gas into a container within 2-6 hours; and controlling the reaction temperature at -15+ / -5 DEG C. The color phase (Fe-Co) of the pentadiene petroleum resin produced with the method is less than or equal to 5, and the softening point is 89 DEG C.

Description

technical field [0001] The present invention relates to a kind of preparation method of piperylene petroleum resin with higher softening point, especially boron trifluoride (BF 3 ) complex is the method for catalyst synthesis piperylene petroleum resin. Background technique [0002] Piperylene petroleum resin is generally prepared by cationic polymerization, usually using Lewis acid catalysts such as metal or non-metal halides. Among these Lewis acids, the most widely used is AlCl 3 , because the single-component Lewis acid catalyst itself has certain limitations in the control of the reaction during the polymerization process. At this time, the polymerization reaction is a heterogeneous reaction, which makes the polymerization reaction difficult to control and the product quality is unstable. Therefore, in the reaction system The introduction of a composite catalyst can regulate the polymerization reaction and improve the performance of the resin. [0003] Patent US441950...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F240/00C08F4/14
Inventor 李正姜丹蕾周遵石付学红周亚婷王芳宋尚德刘玲石大川
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com