Wear-resistant artificial turf fiber

A technology of artificial turf and fiber, applied in rayon manufacturing, heat treatment of artificial filament, single-component polyolefin artificial filament, etc. Unsatisfactory abrasive performance, uneven surface dispersion of artificial turf fibers, etc., to achieve the effects of reducing friction coefficient, reducing adhesion, and improving wear resistance

Active Publication Date: 2012-06-13
TAISHAN SPORTS IND GRP +1
View PDF5 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, people's research on the wear resistance of grass silk is mainly focused on changing the shape of grass silk, such as patent 200920101996.X, but there are few studies on improving the wear resistance of grass silk by modifying grass silk raw materials. CN101476174A discloses a kind of enhanced artificial turf, by adding inorganic nanoparticles to improve the strength of artificial turf, if it is produced according to the production process announced by it, inorganic nanoparticles form a reinforced masterbatch through high mixing, then the agglomeration of inorganic nanoparticles is relatively Seriously, it leads to uneven dispersion of inorganic nanoparticles on the surface of artificial turf fibers, which increases the wear rate of artificial turf fibers and greatly reduces the function of inorganic nanomaterials to strengthen grass fibers, especially for improving the wear resistance of artificial turf fibers. Unsatisfactory effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant artificial turf fiber
  • Wear-resistant artificial turf fiber
  • Wear-resistant artificial turf fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] (1) Preparation of wear-resistant masterbatch

[0040] LDPE (1F7B) 50kg,

[0041] Silicone powder 30kg,

[0042] Zinc stearate 1kg,

[0043] PE wax 8kg,

[0044] Put LDPE, PE wax, silicone powder, and zinc stearate into a high-speed mixer and mix evenly. The mixing temperature is controlled at 75°C, and the mixing time is 25 minutes; The first to seventh zones of discharge temperature are 150°C, 150°C, 160°C, 170°C, 180°C, 180°C, 180°C respectively, and the screw speed is 30r / min;

[0045] (2) Preparation of wear-resistant artificial turf fiber

[0046] Mix the prepared wear-resistant masterbatch with LLDPE (7042), color masterbatch and anti-aging agent according to the following weight ratio:

[0047] LLDPE (7042): 89%

[0048] Wear-resistant masterbatch: 2%

[0049] Masterbatch: 6%

[0050] Anti-aging agent: 3%

[0051] Put it into the single-screw hopper, the temperature of each section of the screw extruder is 200°C, 210°C, 220°C, 220°C, 220°C, 220°C, the s...

Embodiment 2

[0055] (1) Preparation of wear-resistant masterbatch

[0056] LDPE(1F7B)55kg

[0057] Silicone powder 40kg

[0058] Zinc stearate 1kg

[0059] PE wax 8kg

[0060] Put LDPE, PE wax, silicone powder, and zinc stearate into a high-speed mixer and mix evenly. The mixing temperature is controlled at 75°C, and the mixing time is 30 minutes; The first to seventh zones of discharge temperature are 150°C, 150°C, 160°C, 170°C, 180°C, 180°C, 180°C respectively, and the screw speed is 30r / min;

[0061](2) Preparation of wear-resistant artificial grass fiber

[0062] Mix wear-resistant masterbatch, LLDPE(7042), color masterbatch and anti-aging agent according to the following weight ratio, add LLDPE(7042): 87%

[0063] Wear-resistant masterbatch: 4%

[0064] Masterbatch: 6%

[0065] Anti-aging agent: 3%

[0066] into the single-screw hopper, the temperature of each section of the screw extruder is 210°C, 220°C, 230°C, 235°C, 235°C, 235°C, and the screw speed is 42.9r / min. Cool in ...

Embodiment 3

[0070] (1) Preparation of wear-resistant masterbatch

[0071] LDPE(1F7B)60kg

[0072] Silicone powder 50kg

[0073] Zinc stearate 2kg

[0074] PE wax 10kg

[0075] Put LDPE, PE wax, silicone powder, and zinc stearate into a high-speed mixer and mix evenly. The mixing temperature is controlled at 78°C, and the mixing time is 35 minutes; The first to seventh zones of discharge temperature are 150°C, 150°C, 160°C, 170°C, 180°C, 180°C, 180°C respectively, and the screw speed is 30r / min;

[0076] (2) Preparation of wear-resistant artificial turf fiber

[0077] Mix wear-resistant masterbatch, LLDPE (7042), color masterbatch, anti-aging agent, processing aid masterbatch according to the following proportions, add

[0078] LLDPE (7042): 85%

[0079] Wear-resistant masterbatch: 6%

[0080] Masterbatch: 6%

[0081] Anti-aging agent: 3%

[0082] In the single-screw hopper, the temperature of each section of the screw extruder is 220°C, 225°C, 230°C, 235°C, 235°C, 235°C. The scre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to a wear-resistant artificial turf fiber made of the following raw materials by weight: 60 to 95 parts of matrix resin, 1 to 10 parts of wear-resistant masterbatch, 1 to 10 parts of color masterbatch, and 2 to 5 parts of age resister; and the wear-resistant masterbatch contains silicone powder. The wear-resistant artificial turf fiber has a greatly improved wear resisting property, thereby being suitable for places such as schools and the like where the wear-resistant artificial turf fiber is required to be used frequently for a long time. The wear-resistant artificial turf fiber has the advantages that the preparation method is simple; and the cost is low.

Description

technical field [0001] The invention relates to an artificial turf fiber, in particular to an artificial turf fiber with good abrasion resistance. Background technique [0002] At present, artificial turf has been widely used in various sports venues and leisure venues. Artificial turf fiber is the core material of artificial sports turf, and its performance determines the sports mechanics, sports safety and sports comfort of the lawn. At present, the main material used in artificial turf is polymer, which is due to the excellent physical, chemical and mechanical properties of polymer composite materials, such as light weight, high specific strength, large specific modulus, good corrosion resistance, convenient molding, etc. features. However, the surface hardness of polymer materials is low, the bearing capacity is poor, and it is easy to wear; while the artificial turf is frequently used and wears heavily, which makes the artificial turf prone to split ends, hair loss, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/46D01F1/10D01D5/08D01D5/088D01D5/14D01D5/00D01D10/02
CPCE01C13/08D01F1/10D01F6/04D01F6/46D01F1/04D01F1/106D01D5/426D01D5/08
Inventor 时延虎季兴德王新涛陈新春
Owner TAISHAN SPORTS IND GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com