Profile modification agent for epoxy resin emulsion

A technology of epoxy resin emulsion and profile control water blocking agent, which is applied in the direction of drilling compositions, chemical instruments and methods, etc., can solve the problems of poor selectivity and achieve suitable particle size, high viscosity and small particle size Effect

Inactive Publication Date: 2012-05-09
NORTHEAST GASOLINEEUM UNIV
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide an epoxy resin emulsion profile control water blocking agent, which solves the problem of poor selectivity of conventional organic resin water blocking agents, and the water blocking agent is temperature-resistant, salt-resistant, and the emulsion system is stable. Good water blocking performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Profile modification agent for epoxy resin emulsion
  • Profile modification agent for epoxy resin emulsion
  • Profile modification agent for epoxy resin emulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] 1. Optimal design of epoxy resin emulsion profile control and water blocking agent formula:

[0025] 1. Establishment of epoxy resin concentration:

[0026] Because the concentration of epoxy resin is an important factor for whether the crosslinking system can form an emulsion, it is first necessary to establish the concentration of epoxy resin and measure the viscosity of the system after crosslinking different concentrations of epoxy resin and acrylic acid for different times. Experimental data Such as figure 1 and figure 2 shown.

[0027] Depend on figure 1 and figure 2 Shown: the viscosity of the crosslinking system increases with the increase of the epoxy resin concentration after the reaction is carried out for 1 hour. When the epoxy resin concentration is greater than 600mg / L, there is no obvious shear thinning phenomenon. When the rate is very large, it shows the behavior of shear thickening. During the reaction, the cross-linking system with epoxy resin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Salinityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a profile modification agent for an epoxy resin emulsion, which is used for solving the problem of poor selectivity of the conventional organic resin plugging agent. The profile modification agent for an acrylic monomer grafted epoxy resin emulsion is obtained by polymerizing epoxy resin with an acrylic monomer, neutralizing with N,N-dimethylethanolamine and emulsifying with deionized water, wherein the concentration of the epoxy resin in an emulsion system is 300-600 mg / L, the concentration of the N,N-dimethylethanolamine is 3,000-5,000 mg / L, and the crosslinking ratio is 10:1 or 20:1 or 40:1. When the profile modification agent is in use, a large quantity of gel particles of the emulsion enter large pore canals while a small quantity of or no gel particle enterssmall pore canals, the resistance coefficients of the large pore canals are increased, and the resistance coefficients of the small pore canals are increased at a lower frequency in comparison to thelarge pore canals, so that selective plugging can be realized; and moreover, the profile modification agent has high temperature resistance and high salt resistance, and the emulsion system is stable.

Description

technical field [0001] The invention relates to an oilfield additive used in the exploitation process of oilfields with high water cut period, in particular to a profile control and water shutoff agent. Background technique [0002] With the continuous development of the oil field, entering the stage of high water cut or ultra-high water cut water injection development, the contradictions in the plane, interlayer and intralayer of the oil layer become more prominent, and the injected water often breaks into the oil well along the high permeability layer, resulting in a decline in the productivity of the oil well, which seriously affects the water flooding development effect, thereby affecting the oil recovery efficiency of the oil field. In order to solve this problem, people usually adopt the method of shutting off water during the period of high water content. The key of the method is to use the corresponding shutoff agent according to different environments. [0003] Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F283/10C08F220/06C09K8/42C09K8/588
Inventor 刘庆旺范振忠王继刚万家瑰娄艳敏叔贵新赵恒
Owner NORTHEAST GASOLINEEUM UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com