Thermal insulation sheet material and preparation method thereof

The technology of thermal insulation board and fly ash floating beads is applied in the field of building materials, which can solve the problems of short service life of organic thermal insulation materials, and achieve the effects of enhancing thermal insulation effect, good thermal insulation, and enhancing thermal insulation effect.

Active Publication Date: 2012-04-18
安徽瑞蒙科技有限公司
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, the technical problem to be solved by the present invention lies in the short service life of organic thermal insulation materials in the prior art, and further provides a thermal insulation board with light weight, fire prevention and heat insulation functions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The insulation board described in this example is prepared from the following components by weight: 8.5 parts of fly ash floating beads, 38 parts of closed-cell perlite, 43 parts of sulphoaluminate cement, 8.5 parts of bentonite, cellulose 0.04 part of ether, 0.09 part of short fiber, 0.04 part of wood fiber and 0.4 part of rubber powder.

[0050] The closed-cell rate of the closed-cell perlite is above 97%, and the closed-pore rate of the fly ash floating beads is above 90%.

[0051] The viscosity of the cellulose ether is 80000cps.

[0052] The insulation board of the present invention is prepared through the following steps:

[0053] (1) Select closed-cell perlite, fly ash floating beads, sulphoaluminate cement, bentonite, cellulose ether, short fiber, wood fiber and rubber powder according to the selected parts by weight and mix evenly;

[0054] (2) Add water to the mixed material obtained in step (1) according to the water-cement ratio of 1.3:1, and while stirrin...

Embodiment 2

[0059] The insulation board described in this example is prepared from the following components by weight: 10.5 parts of fly ash floating beads, 30 parts of closed-cell perlite, 52 parts of ferric aluminate cement, 7 parts of bentonite, cellulose 0.06 part of ether, 0.07 part of short fiber, 0.06 part of wood fiber and 0.3 part of rubber powder.

[0060] The closed-cell rate of the closed-cell perlite is above 97%, and the closed-pore rate of the fly ash floating beads is above 90%.

[0061] The viscosity of the cellulose ether is 90000 cps.

[0062] The insulation board of the present invention is prepared through the following steps:

[0063] (1) According to the selected parts by weight, select closed-cell perlite, fly ash floating beads, aluminate cement, bentonite, cellulose ether, short fiber, wood fiber and rubber powder and mix evenly;

[0064] (2) Add water to the mixed material obtained in step (1), and pass in a small amount of air to stir evenly while stirring to p...

Embodiment 3

[0069] The insulation board described in this example is prepared from the following components by weight: 9.5 parts of fly ash floating beads, 34 parts of closed-cell perlite, 48 parts of sulphoaluminate cement, 7.8 parts of bentonite, cellulose 0.05 part of ether, 0.08 part of short fiber, 0.05 part of wood fiber and 0.34 part of rubber powder.

[0070] The closed-cell rate of the closed-cell perlite is above 97%, and the closed-pore rate of the fly ash floating beads is above 90%.

[0071] The viscosity of the cellulose ether is 100000 cps.

[0072] The insulation board of the present invention is prepared through the following steps:

[0073] (1) Select closed-cell perlite, fly ash floating beads, sulphoaluminate cement, bentonite, cellulose ether, short fiber, wood fiber and rubber powder according to the selected parts by weight and mix evenly;

[0074] (2) Add water to the mixed material obtained in step (1) according to the water-cement ratio of 1:1, and while stirri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention, belonging to the field of building materials, particularly relates to a lightweight thermal insulation sheet material for building walls. The thermal insulation sheet material comprises the following ingredients: 8.5-10.5 weight portions of fly ash floating bead, 30-38 weight portions of closed cell perlite, 43-52 weight portions of cement, 7-8.5 weight portions of bentonite, 0.04-0.06 weight portions of cellulose ether, 0.07-0.09 weight portions of short fiber, 0.04-0.06 weight portions of wood fiber, and 0.3-0.4 weight portions of gelatine powder. The thermal insulation sheetmaterial is prepared by using organic materials, and has the characteristics of no toxicity, good thermal insulation property, high temperature resistance, low temperature resistance, non-inflammableproperty, high efficiency, and aging resistance. When the thermal insulation sheet material is used for building walls, the thermal insulation property of the sheet material can not be reduced with time, and the sheet material has the same service life with the building.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a light-weight thermal insulation board used for thermal insulation of building walls and a preparation method thereof. Background technique [0002] Building energy conservation is the main content of implementing the national environmental protection and energy conservation policies, and is an important part of implementing the sustainable development of the national economy. my country attaches great importance to building energy conservation. Under the guidance of a series of national energy conservation policies, regulations, standards and mandatory provisions, the energy conservation work in residential construction in my country has been continuously deepened, energy conservation standards have been continuously improved, and it is mandatory that the energy conservation rate of buildings should not be lower than 50%, and relevant data show that the energy loss ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B14/18
Inventor 陈延新
Owner 安徽瑞蒙科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More