Chlorobenzene derivative, optically isotropic liquid crystal medium, and optical element

A liquid crystal compound and liquid crystal composition technology, applied in optics, liquid crystal materials, nonlinear optics, etc., can solve the problems of lower operating voltage, unrecognizable compound characteristics, unreminiscent compounds, etc.

Inactive Publication Date: 2014-09-17
JNC CORP +1
View PDF20 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] Although there is a report (Patent Document 13) that chlorobenzene derivatives similar to the compound of the present case have large dielectric constant anisotropy and large refractive index anisotropy, there is no chlorobenzene derivative that can be thought of in the present invention. There is no description of the compound, and there is no description that can think of the excellent characteristics of the compound of this case
Moreover, in the optically isotropic polymer / liquid crystal composite materials disclosed in Patent Document 1 to Patent Document 3 and Non-Patent Document 1 to Non-Patent Document 3, the voltage required for device operation is high
In Patent Document 4 to Patent Document 9, although the optically isotropic liquid crystal composition and the polymer / liquid crystal composite material that can lower the operating voltage compared with the above are disclosed, there is nothing about the chlorine-containing Description of Optically Isotropic Liquid Crystal Composition of Benzene Moiety Compound and Polymer / Liquid Crystal Composite Material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chlorobenzene derivative, optically isotropic liquid crystal medium, and optical element
  • Chlorobenzene derivative, optically isotropic liquid crystal medium, and optical element
  • Chlorobenzene derivative, optically isotropic liquid crystal medium, and optical element

Examples

Experimental program
Comparison scheme
Effect test

example

[0322] The resulting compound is obtained by 1 The identification is performed by nuclear magnetic resonance spectrum obtained by H-NMR analysis, gas chromatogram obtained by gas chromatography (gas chromatography, GC) analysis, etc., so the analysis method will be described first.

[0323] 1 H-NMR analysis: DRX-500 (manufactured by Bruker BioSpin Co., Ltd.) was used as a measurement device. Dissolve the samples prepared in Examples etc. in CDCl 3 In the deuterated solvent in which the sample is soluble, the measurement is carried out at room temperature, 500 MHz, and the cumulative number of times is 24. In addition, in the description of the obtained nuclear magnetic resonance spectrum, s represents a singlet, d represents a doublet, t represents a triplet, q represents a quartet, and m represents a multiplet. Furthermore, tetramethylsilane (TMS) was used as a zero-point standard substance for the chemical shift 6 value.

[0324] GC analysis: A GC-14B gas chromatograph m...

example 1

[0352] Synthesis of compound (S1-11)

[0353] Compound (S1-11) is in formula (1-4-3), R 1 for C 4 h 9 , L 1 is hydrogen, L 2 , L 4 and L 5 Both are fluorine, X 1 for-CF 3 compound of. (same as compound (1-4-3-a))

[0354]

[0355] The synthesis process is shown in the figure below.

[0356]

[0357] where r.t. is room temperature.

[0358] Synthesis of compound (S1-2)

[0359] Under a nitrogen atmosphere, prepare a Grignard reagent from 11.3 g of dry magnesium and 75.0 g of 1-bromo-3-chloro-5-fluorobenzene (S1-1) using 220 ml of tetrahydrofuran (hereinafter referred to as THF), and cool it to -70°C. 200 ml of THF solution of 52.0 g of trimethyl borate was dripped there, and after stirring at this temperature for 3 hours, it heated to room temperature over 1 hour, and stirred for 12 hours. 2N-hydrochloric acid was added dropwise to the reaction solution and stirred for 1 hour, the product was extracted with ethyl acetate, was...

example 2

[0383] Synthesis of compound (S2-1)

[0384] Compound (S2-1) is in formula (1-4-3), R 1 for C 5 h 11 , L 1 is hydrogen, L 2 , L 4 and L 5 Both are fluorine, X 1 for-CF 3 compound of.

[0385]

[0386] Synthesis of compound (S2-1)

[0387] The synthesis of (S2-1) was carried out according to the synthesis method of (S1-11) in Example 1. The phase transition temperature of the obtained compound (S2-1) is shown below.

[0388] Phase transition temperature (°C): K91.4 (N34.4)I.

[0389] 1 The chemical shift δ (ppm) of the H-NMR analysis is shown below, and the obtained compound was identified as (S2-1). In addition, the determination solvent is CDCl 3 . Chemical shift δ(ppm): 7.53(m, 1H), 7.37~7.33(m, 2H), 7.12~7.07(m, 3H), 7.04~7.01(m, 3H), 2.66(t, 2H), 1.69~ 1.63(m, 2H), 1.41~1.31(m, 4H), 0.92(t, 3H).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
temperatureaaaaaaaaaa
temperatureaaaaaaaaaa
temperatureaaaaaaaaaa
Login to View More

Abstract

Provide a compound with large refractive index anisotropy, large dielectric constant anisotropy, and low melting point; and a compound with a wide temperature range of liquid crystal phase, large refractive index anisotropy, large dielectric constant A liquid crystal medium with constant anisotropy and an optically isotropic liquid crystal phase. The present invention is a liquid crystal compound having a chlorobenzene ring, and a liquid crystal medium characterized by containing the liquid crystal compound and a chiral agent and exhibiting an optically isotropic liquid crystal phase.

Description

technical field [0001] The present invention relates to liquid crystal compounds and liquid crystal media that can be used as materials for optical elements. Specifically, the present invention relates to a compound having a large dielectric constant anisotropy (permittivity anisotropy), a refractive index anisotropy (refractive index anisotropy), and a low melting point; and a compound with a wide liquid crystal phase temperature range , Liquid crystal media with large dielectric constant anisotropy and refractive index anisotropy. In addition, the present invention also relates to an optical element using the liquid crystal medium. Specifically, the present invention relates to an optical element that can be used in a wide temperature range, can be driven at low voltage, and can obtain high-speed electro-optical response. Background technique [0002] Liquid crystal display elements using liquid crystal compositions are widely used in displays such as clocks, calculators...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07C43/225C09K19/12C09K19/14C09K19/16C09K19/18C09K19/20C09K19/30C09K19/34C09K19/38C09K19/54G02F1/13
CPCC09K19/20C09K2019/0466C09K19/588C09K2019/0411Y10T428/10C09K2323/00
Inventor 长谷场康宏国信隆史
Owner JNC CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com