600-MPa grade vanadium-containing high-strength hot-rolled steel bar and production method thereof

A production method and technology for steel bars, applied in the field of metallurgical steelmaking and processing, can solve the problems of large energy consumption, rising connection costs, large alloy consumption, etc., and achieve the effects of reducing costs, reducing the density of reinforcement, and saving resources.

Active Publication Date: 2012-03-21
HEBEI IRON AND STEEL
View PDF2 Cites 60 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, PSB785 steel bars are usually used for steel bars above 590MPa, resulting in large alloy consumption, high cost, complicated process, and large energy consumption. At the same time, due to the high carbon equivalent, only mechanical connections can be used instead of welding, resulting in increased connection costs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 600-MPa grade vanadium-containing high-strength hot-rolled steel bar and production method thereof
  • 600-MPa grade vanadium-containing high-strength hot-rolled steel bar and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The mass percentage of each component in steel is: 0.23%C, 0.42%Si, 1.42%Mn, 0.091%V, 0.0137%N, 0.021%S, 0.030%P, and the rest is Fe and inevitable impurities. 100-ton converter vanadium extraction, 100-ton converter and LF refining process for vanadium slag alloying and vanadium nitride alloy addition, nitrogen blowing throughout, billet continuous casting, soaking, high-pressure water phosphorus removal, bar unit rolling (rolling temperature 990 ℃, finish rolling temperature 910℃), light water penetration, natural cooling in cooling bed, shearing.

[0022] The mechanical properties, formability and microstructure of the obtained steel bars are shown in Table 1.

[0023]

[0024]

Embodiment 2

[0026]The mass percentage of each component in the steel is: 0.22%C, 0.47%Si, 1.40%Mn, 0.103%V, 0.0159%N, 0.027%S, 0.032%P, and the rest is Fe and inevitable impurities. 100-ton converter vanadium extraction, 100-ton converter and LF refining process for vanadium slag alloying and adding ferrovanadium nitride and manganese nitride alloy, nitrogen blowing throughout, billet continuous casting, soaking, high-pressure water phosphorus removal, bar rolling (starting rolling temperature 1020°C, finish rolling temperature 950°C), light water penetration, natural cooling in cooling bed, shearing.

[0027] The mechanical properties, formability and microstructure of the obtained steel bars are shown in Table 2.

[0028]

[0029]

Embodiment 3

[0031] The mass percentage of each component in steel is: 0.24%C, 0.53%Si, 1.47%Mn, 0.112%V, 0.0174%N, 0.025%S, 0.023%P, and the rest is Fe and inevitable impurities. 100-ton converter vanadium extraction, 100-ton converter and LF refining process for vanadium slag alloying and adding ferrovanadium, ferrovanadium and manganese nitride alloy, nitrogen blowing in the whole process, billet continuous casting, soaking, high-pressure water phosphorus removal, Bar rolling (starting rolling temperature 1060°C, finishing rolling temperature 970°C), light water penetration, natural cooling in cooling bed, shearing.

[0032] The mechanical properties, formability and microstructure of the obtained steel bars are shown in Table 3.

[0033] .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a 600-MPa grade vanadium-containing high-strength hot-rolled steel bar and a production method thereof, and belongs to the technical field of metallurgical steel-making and processing; the technical scheme is that the steel bar is prepared by the following components by mass: 0.21-0.25% of C, 0.35-0.60% of Si, 1.35-1.55% of Mn, 0.08-0.12% of V, 0.005-0.04% of N, not more than 0.040% of S, not more than 0.040% of P, and the balance of Fe and inevitable impurities; by adopting vanadium-increasing, nitrogen-increasing, and nitrogen-fixing processes during the smelting process, and by decreasing the initial rolling temperature and the finish rolling temperature during the rolling process, fine-grain, solid-solution and precipitation strengthening are realized at a lowtemperature and a high pressure, so the strength is increased; the hot-rolled steel bar contains a dual-phase structure of ferrite and pearlite, wherein the pearlite accounts for 25-50%; good cooperation of strength and toughness can be reached by controlling ratios, forms and sizes of the phases.

Description

technical field [0001] The invention relates to a 600MPa grade vanadium-containing high-strength hot-rolled steel bar and a production method thereof, in particular to a vanadium-containing high-strength hot-rolled steel bar with a yield strength above 600MPa and a production method thereof, belonging to the technical field of metallurgical steelmaking and processing. Background technique [0002] In 2010, my country produced about 800 million tons of steel products, including about 130 million tons of steel bars, which played an important role in the development of the national economy. Hot-rolled steel bars are the main reinforcement materials for reinforced concrete building structures. With the emergence of multi-functional building structures such as high-rise, long-span, earthquake-resistant, low-temperature resistant, and fire-resistant, steel bars are required to have higher strength, toughness, and better weldability. and other comprehensive performance. Now some h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/12C22C33/04C21D8/08
Inventor 田鹏白瑞国张兴利国富兴韩春良高海张俊粉
Owner HEBEI IRON AND STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com