Preparation method for super macroporous polyurethane reticulated foam plastic

A technology of foamed plastics and polyurethane, which is applied in the field of preparation of super-large-porous polyurethane reticulated foamed plastics, can solve problems such as large-pored polyurethane reticulated foamed plastics, and achieve high safety effects

Active Publication Date: 2012-03-14
深圳市国志汇富高分子材料股份有限公司
View PDF1 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, it is impossible to make a very large, stable and uniform polyurethane reticulated foam with the existing common polyurethane reticulated foam process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The present invention will be described in detail below in conjunction with specific embodiments, where the exemplary embodiments and descriptions of the present invention are used to explain the present invention, but are not intended to limit the present invention.

[0020] Follow the steps below to prepare ultra-large pore polyurethane reticulated foam:

[0021] (1) Prepare raw materials consisting of the following components:

[0022] Polyols, isocyanates, silicone foam stabilizers, water, auxiliary blowing agents, crosslinking agents, cell openers, gel catalysts, colorants;

[0023] (2) The raw material is stored in a storage tank equipped with a constant temperature freezing device, and the temperature is kept constant;

[0024] (3) Add raw materials other than isocyanate to the mixing device at the same time and mix evenly within 3 seconds to obtain a mixed material;

[0025] (4) Open the isocyanate feeding valve, add the isocyanate to the mixture in the mixing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a preparation method for a super macroporous polyurethane reticulated foam plastic. The method comprises the following steps: (1) preparing raw materials, wherein the raw materials comprise the following components: polyol, isocyanate, a silicone foam stabilizer, water, an auxiliary foaming agent, a cross-linking agent, a cell opening agent, a gel catalyst and a colorant; (2) storing the raw materials by a storage tank with a constant temperature freezing device; (3) concurrently adding the raw materials excluding the isocyanate to a mixing device, and uniformly stirring in 3 seconds to obtain a mixed material; (4) opening a isocyanate feeding valve, adding the isocyanate to the mixed material, carrying out high-speed stirring to obtain a mixture; (5) injecting the mixture into a foaming chamber to carry out foaming, closing the foaming chamber after 150-200 seconds, then opening a gas valve to carry out vacuum pumping; (6) removing the formed super macroporous polyurethane reticulated foam body with a reflection-like membrane from the foaming chamber, carrying out a reticulation treatment for the super macroporous polyurethane reticulated foam bodyto form the super macroporous polyurethane reticulated foam plastic. With the present invention, the super macroporous polyurethane reticulated foam plastic can be prepared.

Description

technical field [0001] The invention relates to a preparation method of super-large-pore polyurethane reticulated foam plastic. Background technique [0002] At present, ordinary polyurethane reticulated foam plastics are limited by the formulation process and equipment conditions, and the average diameter of the produced material mesh is generally only 2mm or less. Since the pores of polyurethane reticulated foam are formed by the bubbles generated during the chemical reaction of the liquid mixture from liquid to solid, it can be seen from theory that the larger the bubble, the easier it is to break, and the process is difficult. and the greater the risk. Therefore, it is impossible to make a very large, stable and uniform polyurethane reticulated foam with the existing common polyurethane reticulated foam process. Contents of the invention [0003] The purpose of the present invention is to provide a method for preparing super-large-pore polyurethane reticulated foam p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J9/00C08J9/02C08G18/08C08L75/04C08G101/00
Inventor 汪洋
Owner 深圳市国志汇富高分子材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products