Cement foaming insulation board, preparation method and application thereof

A cement foaming and thermal insulation board technology, applied in the field of building thermal insulation materials, can solve the problems of high overall quality, troublesome production, and difficult construction, etc., to improve the overall strength and hardness, the service life of no slag, and the enhanced bonding effect Effect

Inactive Publication Date: 2012-03-14
天津得全集成房屋有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The fireproof and thermal insulation boards provided by the above patents all have ideal fireproof or heat insulation effects, or both, but there are the following disadvantages: first, the structure is complicated, which brings certain troubles to the production; second, the gap between the fireproof layer and the insulation layer The bonding effect between them is difficult to guarantee, and separation is easy to occur; the third is that the overall quality is high, and it is not easy to construct; the fourth is that the polymer material has poor anti-aging performance and short service life. Therefore, it is necessary to improve the existing technology.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A cement foam insulation board, which is formed by pouring slurry into a mold and adding a curing agent to solidify. The main raw material of the slurry includes Portland cement (sulfoaluminate cement or Portland cement and sulfoaluminate cement) mixture) and hydrogen peroxide, Portland cement (sulfoaluminate cement or a mixture of Portland cement and sulfoaluminate cement), hydrogen peroxide and curing agent in parts by weight of Portland cement (sulfoaluminate cement or Portland cement and sulfoaluminate cement mixture) 4 parts, hydrogen peroxide 0.15 part, curing agent 1 part.

Embodiment 2

[0029] A cement foam insulation board, which is formed by pouring slurry into a mold and adding a curing agent to solidify. The main raw material of the slurry includes Portland cement (sulfoaluminate cement or Portland cement and sulfoaluminate cement) mixture) and hydrogen peroxide, Portland cement (sulfoaluminate cement or a mixture of Portland cement and sulfoaluminate cement), hydrogen peroxide and curing agent in parts by weight of Portland cement (sulfoaluminate cement or Portland cement and sulfoaluminate cement mixture) 6 parts, hydrogen peroxide 1.6 parts, curing agent 3 parts.

Embodiment 3

[0031] A cement foam insulation board, which is formed by pouring slurry into a mold and adding a curing agent to solidify. The main raw material of the slurry includes Portland cement (sulfoaluminate cement or Portland cement and sulfoaluminate cement) mixture) and hydrogen peroxide, Portland cement (sulfoaluminate cement or a mixture of Portland cement and sulfoaluminate cement), hydrogen peroxide and curing agent in parts by weight of Portland cement (sulfoaluminate cement or Portland cement and sulfoaluminate cement mixture) 6 parts, hydrogen peroxide 0.8 parts, curing agent 3 parts.

[0032] The Portland cement or sulphoaluminate cement or the mixture of Portland cement and sulphoaluminate cement in Examples 1 to 3 is one of the acid cements, and the curing agent is gypsum powder and mixed with water. of slurry.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a cement foaming insulation board, a preparation method and application thereof; the cement foaming insulation board is prepared by adopting the steps of: uniformly mixing 4-6 parts by weight of acidic cement, 0.15-1.6 parts by weight of hydrogen peroxide by adding proper dosage of water, adding 1-3 parts by weight of curing agent in a mould, and uniformly stirring and curing, wherein the total forming duration is less than 25 min. According to the cement foaming insulation board provided by the invention, a fireproof and environmental-friendly material is used as a raw material of a building insulation board, so that the material has the advantages of small mass, sound insulation, environmental protection, high toughness, non-deformation, non-slag dropping and long service life; the curing agent is adopted in the preparation process to reinforce the adhesion effect and improve the integral strength and hardness of the board, and the board is firmer; and the cement foaming insulation board can be applied on outer walls, interior walls and partition walls of buildings.

Description

technical field [0001] The invention relates to the technical field of building thermal insulation materials, in particular to a cement foam thermal insulation board, its preparation method and application. Background technique [0002] At present, the use of wall insulation to achieve building energy saving is receiving more and more attention. Directly pasting decorative materials such as marble or other similar materials on the wall (external wall) of the building only serves as a decorative embellishment effect, but cannot provide heat insulation. The function of heat preservation and fire prevention. [0003] With the continuous improvement of people's awareness of energy saving in buildings and the awareness of fire protection in buildings, EPS boards (expandable polystyrene boards), which were commonly used in the past, have gradually received cold reception. The fire showed that the root cause of the rapid spread of the fire and the death and injury of dozens of peo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/00C04B28/14E04B1/80
Inventor 张得全白坤
Owner 天津得全集成房屋有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products