Guar gum surface sizing agent and preparation method thereof
A technology of surface sizing agent and guar gum, which is applied in water-repellent addition, textile and papermaking, fiber raw material treatment, etc., can solve problems such as unstable sizing agent concentration, heavy workload, and poor printing strength of paper, and achieve Improve printing performance and printing strength, reduce paper fiber consumption, and reduce labor intensity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] In a four-necked flask equipped with a thermometer, a mechanical stirrer, a nitrogen device and a dropping device, add 200 parts of ethanol, start stirring, add 200 parts of guar gum under stirring, and disperse for 10 minutes. 10 parts of prepared 20wt% peroxosulfuric acid aqueous solution was added dropwise in a four-necked flask, and the dropwise addition time was 20 minutes. After the dropwise addition, it was reacted at this temperature for 5 hours, and the pH of the reaction process system was 2.0. to room temperature to obtain oxidized guar gum;
[0019] Add 0.5 parts of vinyl acetate to the above reaction system, adjust the pH value of the solution to 8.0 with a 30% sodium hydroxide solution by weight, raise the temperature to 40°C, react for 1 hour, cool to 25°C, filter with suction, Wash, dry, and sieve to obtain the product of the present invention.
Embodiment 2
[0021] In a four-neck flask equipped with a thermometer, a mechanical stirrer, a nitrogen device and a dropping device, add 300 parts of ethanol, start stirring, add 200 parts of guar gum under stirring, and disperse for 10 minutes. 5 parts of prepared 25wt% aqueous solution of peracetic acid were added dropwise to a four-necked flask, and the time for adding was 30 minutes. After the addition was completed, the reaction was carried out at this temperature for 3 hours. The p H of the system during the reaction process was 3.0, cooled to room temperature to obtain oxidized guar gum;
[0022] Add 2 parts of sodium tripolyphosphate to the above reaction system, adjust the pH value of the solution to 6.5 with 20% sodium hydroxide solution by weight, raise the temperature to 40°C, react for 2 hours, cool to 25°C, and filter with suction , washing, drying, and sieving to obtain the product of the present invention;
Embodiment 3
[0024] In a four-neck flask equipped with a thermometer, a mechanical stirrer, a nitrogen device, and a dropping device, add 400 parts of ethanol, start stirring, add 200 parts of guar gum under stirring, and disperse for 5 minutes. 15 parts of the prepared 30wt% phosphoric acid peroxygen solution were added dropwise in a four-necked flask, and the time for adding was 45 minutes. After the addition was completed, the reaction was carried out at this temperature for 5 hours. Cool to room temperature to obtain oxidized guar gum;
[0025] Add 5 parts of succinic anhydride to the above reaction system, adjust the pH value of the solution to 7.0 with a 30% sodium hydroxide solution by weight, raise the temperature to 50°C, react for 1 hour, cool to 25°C, filter and wash with suction , drying, and sieving to obtain the product of the present invention.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com