Environment-friendly printing platen adhesive emulsion and preparation method thereof

An adhesive and environment-friendly technology, applied in adhesive types, ester copolymer adhesives, dyeing methods, etc., can solve the problems of environmental pollution, inability to use one scrape coating for multiple times, poor water resistance, etc., and achieve Accurate printing color registration, good cohesion and stickiness, and easy to use

Inactive Publication Date: 2012-02-08
连云港百利合新材料发展有限公司
View PDF5 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese invention patent application CN1563239A has reported a kind of water-soluble acrylic printing table glue and its preparation method and application, but in its preparation process, add volatiles such as ethanol, propylene glycol methyl ether or isopropanol, use crosslinking monomer as N -Hydroxymethylacrylamide, formaldehyde will be slowly released during film formation and cross-linking, which will pollute the environment. At the same time, the platen glue is water-soluble acrylic ester, which has poor water resistance and cannot be used for multiple times by scraping at one time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly printing platen adhesive emulsion and preparation method thereof
  • Environment-friendly printing platen adhesive emulsion and preparation method thereof
  • Environment-friendly printing platen adhesive emulsion and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026]

[0027]

[0028] The preparation method of the present embodiment comprises the following steps:

[0029] A. Dissolve emulsifier sodium lauryl sulfate in 30.0% deionized water, stir, add soft monomer, hard monomer, functional monomer, stir to obtain pre-emulsion;

[0030] B, ammonium persulfate is dissolved and made into initiator solution with 3% deionized water for stand-by;

[0031] C, add surplus deionized water in the reactor, get 5% of the pre-emulsion prepared in step A and add in the reactor, be warming up to 80 ℃, add 27% of the initiator solution that makes in the step B, React for 20 minutes; start to add the remaining amount of pre-emulsion and the remaining amount of initiator solution dropwise, and the dropwise addition is completed in 4 hours. After all the dropping is completed, the temperature is raised to 86°C for 2 hours, and the temperature is lowered to below 40°C. Add ammonia water to neutralize After the pH value was 7.0-8.0, the material ...

Embodiment 2

[0033]

[0034]

[0035] The preparation method of the present embodiment comprises the following steps:

[0036] A. Dissolve emulsifier sodium lauryl sulfate in 36.0% deionized water, stir, add soft monomer, hard monomer, functional monomer, stir to obtain pre-emulsion;

[0037] B, potassium peroxide is dissolved and made into initiator solution with 3% deionized water for stand-by;

[0038] C, add surplus deionized water in the reactor, get 5% of the pre-emulsion prepared in step A and add in the reactor, be warming up to 80 ℃, add 22% of the initiator solution that makes in the step B, React for 25 minutes; start to add the remaining amount of pre-emulsion and the remaining amount of initiator solution dropwise, and the dropwise addition is completed in 4 hours. After all the dropwise addition is completed, the temperature is raised to 88°C and incubated for 1.5 hours, and the temperature is lowered to below 40°C. Add ammonia water to neutralize After the pH value wa...

Embodiment 3

[0040]

[0041]

[0042] The preparation method of the present embodiment comprises the following steps:

[0043] A. Dissolve emulsifier sodium lauryl sulfate in 32.0% deionized water, stir, add soft monomer, hard monomer, functional monomer, stir to obtain pre-emulsion;

[0044] B, potassium peroxide is dissolved and made into initiator solution with 3% deionized water for stand-by;

[0045] C, add surplus deionized water in the reactor, get 5% of the pre-emulsion prepared in step A and add in the reactor, be warming up to 80 ℃, add 21% of the initiator solution that makes in the step B, React for 15 minutes; start to add the remaining amount of pre-emulsion and the remaining amount of initiator solution dropwise, and the dropwise addition is completed in 4 hours. After all the dropwise addition is completed, the temperature is raised to 88°C and incubated for 1.5 hours, and the temperature is lowered to below 40°C. Add ammonia water to neutralize After the pH value wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly printing platen adhesive emulsion and a preparation method thereof, and the emulsion comprises the following components by weight: 25%-45% of soft monomers, 4%-10% of hard monomers, 1%-6% of functional monomers, 0.1%-0.3% of initiators, 1%-6% of emulsifiers, 45%-65% of deionized water, and 0.5%-5% of neutralizers. The adhesive of the invention is anaqueous environment-friendly product, adopts water as a solvent, does not contain any volatile solvent, is environment-friendly, does not discharge toxic substances such as formaldehyde and the like,does not contain alkylphenol additives; the adhesive has good adhesive force to various textile fabrics; fabrics are not easy to slide on the platen or be separated from the platen; printing color register is accurate; the preparation method of the invention adopts a new crosslinking monomer, and increases the water resistance and cohesive adhesion lasting force of the adhesive; the adhesive can be used repeatedly; because of the good cohesive adhesion lasting force of the adhesive, no adhesive is left at the fabric bottom during fabric removal; meanwhile the adhesive of the invention has moderate and adjustable viscosity, is convenient for using, and is easy to adhesive application by a scraper plate.

Description

【Technical field】 [0001] The invention relates to an environment-friendly printing platen adhesive emulsion and a preparation method thereof, belonging to the field of paint chemical manufacturing industry. 【Background technique】 [0002] Since the 1950s, in response to the shortcomings of traditional dyeing processes such as complex dyeing process, high pollution, high cost and long price cycle, pigment printing has emerged abroad. The process of pigment printing is simple, energy-saving, no waste water discharge, complete color spectrum, and convenient color matching and imitation. The printing outline is clear, the authenticity rate is high, and the reproducibility is strong. my country only began to import acrylic adhesives for pigment printing in the 1960s, and then began research work in this area. In the whole process of textile processing, people pursue simple process, low investment, less equipment, energy saving, and at the same time require no or a small amount o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F220/18C08F218/08C08F220/06C08F212/08C08F220/14C08F2/26C09J133/08D06P1/52
Inventor 陈万春欧继安杨剑张鲁桂
Owner 连云港百利合新材料发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products