Modification-enhanced polyether ether ketone material and preparation method thereof

A polyether ether ketone and modification technology, which is applied in the field of modified and enhanced polyether ether ketone materials and their preparation, can solve the problems of lack of modification technology, limitation of modification technology and high processing temperature, and achieve good economic benefits , the preparation process is simple, the effect of reducing the processing temperature and difficulty

Inactive Publication Date: 2012-01-25
SHENZHEN KEJU NEW MATERIAL
View PDF2 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But at present, because this material is mostly used in military industry, the modification technology of polyether ether ketone in China is very limited, and the start is very fast, and there are still many imperfections. Basically, there is no feasible and easy-to-operate method. Modification technology
Due to its molecular structure, the PEEK material itself has an ultra-high temperature resistance grade and a high molecular weight, but due to its high temperature resistance, its fluidity is poor, making processing more difficult, and the processing temperature is very high, generally at 360- Between 400 degrees

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modification-enhanced polyether ether ketone material and preparation method thereof
  • Modification-enhanced polyether ether ketone material and preparation method thereof
  • Modification-enhanced polyether ether ketone material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Weigh 50 parts of polyether ether ketone (PEEK), 8 parts of polyphenylene sulfide (PPS), 30 parts of long glass fiber 988A, 0.2 parts of antioxidants 1010 and 168, lubricant TAF and silicone Alkanes are 0.3 parts, and nucleating agent CAV102 is 0.3 parts.

[0044] Composite materials were prepared by the following methods:

[0045] a. Dry polyether ether ketone (140°C 3h) and polyphenylene sulfide (120°C 4h);

[0046] b. Add the dried polyether ether ketone and polyphenylene sulfide to the high-speed mixer, and add lubricant, nucleating agent and antioxidant, and mix at high speed for about 4 minutes;

[0047] c. Put the mixed raw materials and additives into the twin-screw extruder, add glass fiber to carry out reinforcement filling extrusion granulation.

[0048] The temperature setting of each section of the twin-screw extruder is: the temperature of the first zone is 250°C, the temperature of the second zone is 330°C, the temperature of the third zone is 330°C, th...

Embodiment 2

[0050] Weigh 57 parts of polyether ether ketone (PEEK), 10 parts of polyphenylene sulfide (PPS), 30 parts of long glass fiber 988A, 0.2 parts of antioxidants 1010 and 168, lubricant TAF and silicone Alkanes are 0.3 parts, and nucleating agent CAV102 is 0.3 parts.

[0051] Composite materials were prepared by the following methods:

[0052] a. Dry polyether ether ketone (150°C 3h) and polyphenylene sulfide (140°C 4h);

[0053] b. Add the dried polyether ether ketone and polyphenylene sulfide to the high-speed mixer, and add lubricant, nucleating agent and antioxidant, and mix at high speed for about 4 minutes;

[0054] c. Put the mixed raw materials and additives into the twin-screw extruder, add glass fiber to carry out reinforcement filling extrusion granulation.

[0055] The temperature setting of each section of the twin-screw extruder is: the temperature of the first zone is 260°C, the temperature of the second zone is 330°C, the temperature of the third zone is 340°C, t...

Embodiment 3

[0057] Weigh 57 parts of polyether ether ketone (PEEK), 10 parts of polyphenylene sulfide (PPS), 30 parts of long glass fiber T635B, 0.2 parts of antioxidant 1010 and 168, lubricant TAF and silicone Alkanes are 0.3 parts, and nucleating agent CAV102 is 0.3 parts.

[0058] Composite materials were prepared by the following methods:

[0059] a. Dry polyether ether ketone (150°C 3h) and polyphenylene sulfide (140°C 4h);

[0060] b. Add the dried polyether ether ketone and polyphenylene sulfide to the high-speed mixer, and add lubricant, nucleating agent and antioxidant, and mix at high speed for about 4 minutes;

[0061] c. Put the mixed raw materials and additives into the twin-screw extruder, add glass fiber to carry out reinforcement filling extrusion granulation.

[0062] The temperature setting of each section of the twin-screw extruder is: the temperature of the first zone is 250°C, the temperature of the second zone is 330°C, the temperature of the third zone is 330°C, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a modification-enhanced polyether ether ketone material and a preparation method thereof. The modification-enhanced polyether ether ketone material is prepared from the following components in parts by weight: 50-60 parts of polyether ether ketone, 8-15 parts of polyphenylene sulfide, 30-35 parts of filling enhancer, 0.2-0.6 part of antioxidant, 0.2-0.8 part of lubricant and 0.3-0.6 part of nucleating agent. The invention has the characteristics that: the defect of poor fluidity of polyether ether ketone is overcome by adding polyphenylene sulfide, and the processing temperature and difficulty of the polyether ether ketone are greatly reduced; because the polyether ether ketone is expensive, the production cost is greatly lowered by introducing polyphenylene sulfide; and the preparation process disclosed by the invention is simple, low in cost and high in benefit and can obtain good economic benefit.

Description

[technical field] [0001] The invention relates to the field of polymer materials, in particular to a modified and reinforced polyether ether ketone material and a preparation method thereof. [Background technique] [0002] Polyetheretherketone (PEEK) is a new type of ultra-high temperature-resistant and high-performance polyetheretherketone material successfully developed and mass-produced by Victrex Company of the United Kingdom. The trade name is VICTREX. It has the advantages of high heat resistance, high strength and excellent electrical performance. Polyetheretherketone (PEEK for short) is a new type of polyether ether ketone (PEEK) which is produced by the condensation reaction of 4,4'-difluorobenzophenone and hydroquinone in the presence of alkali metal carbonate, using diphenyl sulfone as a solvent. Semi-crystalline aromatic engineering thermoplastics. It is a high-temperature resistant thermoplastic with a high glass transition temperature (143°C) and melting poin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L61/16C08L81/02C08K13/06C08K9/06C08K7/14B29B9/06
Inventor 徐东徐永郭宇嘉
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap