A kind of configuration and coating method of aluminum foil pre-coated nano conductive carbon primer

A technology of nano-conduction and primer liquid, which is applied in the direction of surface coating liquid devices, conductive adhesives, coatings, etc., which can solve the problem of unimproved conductivity of active materials and current collector aluminum foil, lithium iron phosphate active materials and Poor bonding of current collector aluminum foil, affecting battery rate performance, cycle performance and other issues, to achieve the effect of high compaction density, good conductivity and low internal resistance

Active Publication Date: 2011-12-28
JIANGSU LENENG BATTERY INC
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the poor conductivity of lithium iron phosphate, it is necessary to dope some conductive agents in lithium iron phosphate to improve the conductivity of the material, and to improve the conductivity of ions between the active materials, while the active material and the current collector aluminum foil Conductivity did not improve
Since the particle diameter of the lithium iron phosphate primary particle is generally between 10nm and 2000nm, its contact with the surface of the aluminum foil is point contact, and the lithium iron phosphate active material is poorly bonded to the current collector aluminum foil, resulting in an increase in the internal resistance and polarization of the battery. And affect the rate performance and cycle performance of the battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of configuration and coating method of aluminum foil pre-coated nano conductive carbon primer
  • A kind of configuration and coating method of aluminum foil pre-coated nano conductive carbon primer
  • A kind of configuration and coating method of aluminum foil pre-coated nano conductive carbon primer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The configuration of the aluminum foil pre-coated nano-conductive carbon water-based primer, in terms of mass percentage.

[0025] Take by weighing 1000 grams of double distilled water aqueous solvent and 200 grams of water-based binder A and carry out mechanical stirring for 2 hours to obtain a uniform and stable binder system; add 25 grams (total mass) every 30 minutes in three times under ultrasonic dispersion conditions (75 g) powder nano-conductive carbon composite conductive agent, and then ultrasonically dispersed for 2 hours to obtain a water-based primer with a viscosity of 8000 cps. The nano conductive carbon composite conductive agent here is a mixture of 20 grams of nano conductive carbon and 5 grams of Supper P composite conductive agent. The combination of nano conductive carbon and Spper P can not only increase the conductivity of the primer solution, but also improve the flatness of the coated surface.

Embodiment 2

[0027] The configuration of the aluminum foil pre-coated nano-conductive carbon water-based primer, in terms of mass percentage.

[0028] Take by weighing 1000 grams of alcohol water-based solvent and 200 grams of water-based binder A and carry out mechanical stirring for 1 hour to obtain a uniform and stable binder system; add 18 grams every 30 minutes in three times under ultrasonic dispersion conditions (total mass is 54 g) powder nano-conductive carbon composite conductive agent, and then ultrasonically disperse for 2 hours, and finally obtain a water-based primer with a viscosity of 2000cps. The nano conductive carbon composite conductive agent here is a mixture of 15 grams of nano conductive carbon and 3 grams of Supper P composite conductive agent.

[0029] The aqueous solvent is double distilled water or alcohol / IPA with a concentration of 10%~80%. Since double distilled water or alcohol, IPA contains hydroxyl groups, it can be better compatible with the hydroxyl group...

Embodiment 3

[0032] The configuration of the aluminum foil pre-coated nano-conductive carbon oil-based primer, in mass percent.

[0033] Weigh 1000 grams of N-methylpyrrolidone NMP with a purity greater than 98% as an oily solvent, 35 grams of polyvinylidene fluoride PVDF as a binder B, and mechanically stir for 6 hours under high-speed stirring to obtain a uniform and stable bond After that, add 20 grams (total mass is 60 grams) of powder nano-conductive carbon composite conductive agent system every 30 minutes for three times, and then use ultrasonic ultrasonic dispersion for 2 hours, and finally add 300 grams of NMP to adjust the viscosity. And finally obtain the oily primer with a viscosity of 3000 cps. The nano conductive carbon composite conductive agent is formed by mixing 10 grams of nano conductive carbon and 5 grams of Supper P composite conductive agent.

[0034] The binder B is selected as polyvinylidene fluoride (PVDF), and its molecular weight is between 1 million and 1.1 mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

A preparation process of nano-conductive carbon primer for precoating aluminum foil and a coating method thereof are provided. The preparation process comprises the following steps: i) preparing aqueous or oily primer, wherein the aqueous primer comprises 1 part of aqueous solvent, 0.05-0.6 parts of adhesive agent A, and 0.05-0.6 parts of powder nano-conductive composite conductive agent, and the oily primer comprises 1 part of oily solvent, 0.03-0.6 parts of adhesive agent B, and 0.03-0.6 parts of powder nano-conductive composite conductive agent; and ii) ultrasonically dispersing. The battery coated with the primer has low internal resistance, strong adhesive force, good conductive property, and high compacted density.

Description

technical field [0001] The invention relates to the technical field of lithium ion battery undercoatings, in particular to a method for configuring and coating an undercoating liquid in an undercoating layer of a lithium iron phosphate cathode material. Background technique [0002] Lithium iron phosphate is a new type of energy storage battery developed in recent years, and has become a new type of power battery due to its high safety performance, long cycle life, and environmental friendliness. However, due to the poor conductivity of lithium iron phosphate, it is necessary to dope some conductive agents in lithium iron phosphate to improve the conductivity of the material, and to improve the conductivity of ions between the active materials, while the active material and the current collector aluminum foil Conductivity was not improved. Since the particle diameter of the lithium iron phosphate primary particle is generally between 10nm and 2000nm, its contact with the su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J9/02C09J11/04C09J133/02C09J133/20C09J127/16B05C11/10B05D7/24H01M4/1397
CPCC09J11/04Y02E60/12C09J133/02C09J127/16H01M4/667B05D7/24H01M4/5825H01M4/661C09J9/02C09J133/20H01M4/1397B05C11/10Y02E60/122Y02E60/10
Inventor 丁建民
Owner JIANGSU LENENG BATTERY INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com