Zinc-plating additive and preparation method thereof

A technology of additives and chloride additives, applied in the field of galvanizing additives and its preparation, can solve problems such as the gap in galvanizing quality

Inactive Publication Date: 2011-10-12
HUBEI DE MEI TECH
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is still some gap between the existing chloride galvanizing and cyanide galvanizing in terms of galvanizing quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zinc-plating additive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] Below by example the present invention is further described.

[0013] We took the additives to Jilin Jidian Equipment Factory for acid galvanizing solution electroplating (5 tons of bath solution for electroplating), and the results are shown in the table:

[0014]

[0015] According to the above data, it can be seen that when other conditions are the same but the content of additives is different, the coatings to be plated are slightly different. The optimal value should be controlled at 1g / L of agent A and 20 g / L of agent B, so that the crystallization of the electroplated zinc layer is fine and smooth, and the brightness is high.

[0016] The main technical and performance indicators of the acidic chloride galvanizing additive of the present invention are as follows:

[0017] Agent A Agent B

[0018] Appearance dark yellow light yellow

[0019] PH 5.0~5.5 5.0~5.5

[0020] Galvanizing bath temperature 10~40℃ 10~40℃

[0021] After trial and error, add 1 ml / L of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an acidic chloride zinc-plating additive and a preparation method thereof. The additive consists of a brightening agent A and a softening agent B, wherein the brightening agent A is prepared by dissolving 20 to 30 weight parts of benzalacetone into 100 weight parts of alkylphenol ethoxylates with stirring at room temperature under normal pressure at the rotate speed of between 10 and 100 revolutions / minute, and the softening agent B is prepared by dissolving 1.8 to 5.8 weight parts of nicotinic acid 100 weight parts of dodecanol polyoxyethylene ether with stirring at the room temperature under the normal pressure at the rotate speed of between 10 and 100 revolutions / minute. The additive is prepared from 0.6 to 1.6 grams / liter of brightening agent A, 10 to 30 grams / liter of softening agent B and a proper amount of water. The additive is added into acidic zinc-plating solution, so that a zinc coating which is high in brightness and flattening, small in internal force and high in current efficiency can be obtained.

Description

technical field [0001] The invention relates to an additive for an acidic chloride galvanizing solution and a preparation method thereof. Background technique [0002] Chloride galvanizing has developed rapidly in my country since the 1980s. The plating solution of this process is a single-salt plating solution without complexing agents, and the wastewater is easy to handle. The dispersion ability and deep plating ability of the plating solution are second only to cyanide galvanizing. , high current efficiency, fast deposition speed, and at the same time, the plating solution has little corrosion on the equipment, stable and safe. However, there is still some gap between the existing chloride galvanizing and cyanide galvanizing in terms of galvanizing quality. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an acidic chloride galvanizing additive with strong impurity resistance, high stability and wide process ra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D3/22
Inventor 瞿德勤
Owner HUBEI DE MEI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com