Method for preparing aromatic hydrocarbons by methanol-containing raw materials
A technology of methanol and raw materials, applied in the field of aromatics preparation, which can solve the problems of difficult removal of heat, overheating of catalysts, deactivation, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0015] According to the present invention, the preparation method of the metal-modified MFI structure and / or MEL structure silicoaluminite molecular sieve includes the following steps:
[0016] (1) The raw powder of zeolite molecular sieve is NH 4+ Ion exchange and roasting to prepare acidic zeolite molecular sieve;
[0017] (2) Use a soluble non-rare earth metal solution and / or a soluble rare earth metal salt solution to impregnate the acidic zeolite molecular sieve, the time of dipping and the concentration of the metal salt in the soluble non-rare earth metal salt solution and / or soluble rare earth metal salt solution as long as the catalyst is satisfied The content of the metal components is sufficient; after drying and roasting, a non-rare earth metal and / or rare earth metal modified zeolite molecular sieve is obtained;
[0018] (3) The modified catalyst prepared in step (2) is compressed into tablets, dried and shaped.
[0019] Among them, in step (1), the zeolite molecular siev...
Embodiment 1
[0024] This example is used to illustrate the preparation of fixed bed catalyst
[0025] (1) 500 grams of ZSM-5 zeolite molecular sieve powder (Nankai University Catalyst Factory) SiO 2 / Al 2 O 3 =50 (molar ratio) roasting at 550°C to remove the template, exchange 4 times with 0.5 molar equivalent of ammonium nitrate solution in a water bath at 80°C, drying in the air at 120°C, and roasting at 550°C for 3 hours to obtain HZSM-5 zeolite molecular sieve.
[0026] (2) Press the 20 grams of HZSM-5 zeolite molecular sieve prepared in step (1) into a tablet shape. After crushing and sieving to obtain a 40-60 mesh sample, divide it into two parts, and use the concentration at room temperature (25℃) Is 3% by weight and 9% by weight of zinc nitrate Zn(NO 3 ) 2 The solution is immersed for 4 hours, dried at 120°C, and calcined in air at 550°C for 6 hours to obtain a non-rare earth metal modified catalyst;
[0027] (3) La(NO) with a concentration of 10% by weight 3 ) 3 Aqueous solution impregn...
Embodiment 2
[0029] This example is used to illustrate the preparation of fixed bed catalyst
[0030] (1) 500 grams of ZSM-5 zeolite molecular sieve powder (Nankai University Catalyst Factory) SiO 2 / Al 2 O 3 =50 (molar ratio) roasting at 550°C to remove the template, exchange 4 times with 0.5 molar equivalent of ammonium nitrate solution in a water bath at 80°C, drying in the air at 120°C, and roasting at 550°C for 3 hours to obtain HZSM-5 zeolite molecular sieve.
[0031] (2) Press the 20 grams of HZSM-5 zeolite molecular sieve prepared in step (1) into a tablet shape. After crushing and sieving to obtain a 40-60 mesh sample, divide it into two parts, and use the concentration at room temperature (25℃) Is 3.7% by weight and 11.1% by weight of molybdenum nitrate Mo(NO 3 ) 3 The solution is immersed at room temperature for 4 hours, dried at 120°C, and calcined in air at 550°C for 6 hours to obtain a non-rare earth metal modified catalyst;
[0032] (3) La(NO) with a concentration of 10% by weight...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com