Normal temperature spraying detergent for aluminum alloy and preparation method thereof

An aluminum alloy and cleaning agent technology, applied in the field of rust prevention and chemical cleaning, can solve the problems of the workpiece not reaching the cleaning quality, affecting the cleaning quality, corrosion of the parts, etc., to increase the cleaning power at room temperature, easy to use, and low consumption Effect

Inactive Publication Date: 2011-08-17
华阳新兴科技(天津)集团有限公司
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the cleaning industry, especially for the cleaning of aluminum alloy workpieces, the parts will be corroded soon after cleaning, especially if the commonly used water-based aluminum alloy cleaning agent is used, the cleaned workpieces cannot meet the cleaning quality standards, and the oil stains cannot be washed away. , that is, the workpiece is corroded; and most workpieces begin to change color after being placed for a period of time after cleaning, which seriously affects the cleaning quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Normal temperature spraying detergent for aluminum alloy and preparation method thereof
  • Normal temperature spraying detergent for aluminum alloy and preparation method thereof
  • Normal temperature spraying detergent for aluminum alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: a kind of aluminum alloy room temperature spray cleaning agent, its constituent raw material and its weight percent are respectively:

[0023]

[0024] A preparation method of an aluminum alloy room temperature spray cleaning agent, the steps are as follows:

[0025] (1) Add the reaction amount of water into the reaction kettle, add the reaction amount of sodium metasilicate pentahydrate, sodium gluconate, and disodium edetate at 25-40°C and stir, and keep the reaction for 20 minutes.

[0026] (2) Add isomeric alcohol ether and surfactant RQ-129B (fatty alcohol polyoxyethylene ether) to the reaction kettle and stir until completely dissolved, then add solubilizer RQ-130E (dipropylene glycol methyl ether), and continue stirring for 30 Minutes until the solution is clear and transparent, keep the temperature of the reactor at 35-40°C during the reaction.

[0027] (3) After the reaction is completed, it is naturally cooled to room temperature, and after s...

Embodiment 2

[0029] A kind of aluminum alloy room temperature spray cleaning agent, its constituent raw material and weight percentage thereof are respectively (taking 1000g water-based antirust agent as example):

[0030]

[0031] The steps of the preparation method are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a normal temperature spraying detergent for aluminum alloy and a preparation method thereof. The detergent comprises the following raw materials in percentage by weight: 1 to 5 percent of ethylene diamine tetraacetic acid, 0.5 to 1.5 percent of sodium metasilicate pentahydrate, 5 to 8 percent of sodium gluconate, 5 to 10 percent of heterogeneous alcohol ether, 2 to 7 percent of solubilizing agent, 3 to 8 percent of surfactant, and the balance of water. The detergent can be used at normal temperature, and does not need heating so as to save the energy; the detergent does not corrode the treated aluminum alloy parts, does not leave white spots on the surfaces of the parts, and can increase the brightness of the parts; and the detergent has long service life and low using concentration, is safe and environment-friendly, saves the working time, and improves the working efficiency.

Description

technical field [0001] The invention relates to the fields of chemical cleaning and antirust, in particular to an aluminum alloy room temperature spray cleaning agent and a preparation method thereof. Background technique [0002] In the cleaning industry, especially for the cleaning of aluminum alloy workpieces, the parts will be corroded soon after cleaning, especially if the commonly used water-based aluminum alloy cleaning agent is used, the cleaned workpieces cannot meet the cleaning quality standards, and the oil stains cannot be washed away. , that is, the workpiece is corroded; and most of the workpieces begin to change color after being placed for a period of time after cleaning, which seriously affects the cleaning quality. [0003] By searching, there are two following patent documents related to this patent application, which are respectively: 1. A cleaning agent for aluminum and aluminum alloys (CN101012411), which consists of alkylphenol polyoxyethylene ether (...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/22
Inventor 赵国胜王振国
Owner 华阳新兴科技(天津)集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com