Automobile hot-melt lamp adhesive

A hot-melt and lamp technology, applied in the direction of adhesives, etc., can solve the problems of poor bonding effect of glass lamps, complicated production process of hot-melt adhesive, high melting viscosity of hot-melt adhesive, etc., to achieve improved wettability and low styrene content , Good colloidal flexibility

Active Publication Date: 2011-05-18
中国航天科技集团公司第四研究院第四十二所
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The production process of the hot melt adhesive is complicated, the equipment requirements are high, the production cost is increased, the glue is inconvenient to use, and the bonding effect on the glass lamp is not good.
[0004] Chinese invention patent application publication CN1887999A provides a hot-melt adhesive formulation, including styrene-isoprene-styrene block copolymer (SIS), ethylene-vinyl acetate copolymer (EVA), ethylene-acrylic acid ethyl Ester copolymer (EEA), tackifying resin, organic montmorillonite, antioxidant, etc., produced by twin-screw extruder under high temperature heating, used for repairing and bonding polyethylene pipes, the hot melt adhesive has a high melting viscosity , it is inconvenient to apply glue, and the effect on metal bonding is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Automobile hot-melt lamp adhesive
  • Automobile hot-melt lamp adhesive
  • Automobile hot-melt lamp adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1, automobile hot-melt lamp glue component ratio (mass %)

[0024]

[0025]

[0026] SIS, SEBS, TOTM and Antioxidant 1010 were weighed in proportion and added to a horizontal kneader that had been preheated for 60 minutes (wall temperature 180°C), kneaded for 40 minutes and then added proportionally weighed terpene resin and hydrogenated rosin Pentaerythritol ester, C 5 Petroleum resin, polyethylene wax, Fischer-Tropsch wax, light calcium carbonate and thermoelectric blast furnace fly ash were kneaded at high temperature (175°C) for 60 minutes. Pour into a 25cm×15cm×7cm cube box (lined with high-temperature release paper) in a molten state, and wrap it with release paper after cooling.

Embodiment 2

[0027] Embodiment 2, automobile hot-melt lamp glue component ratio (mass %)

[0028]

[0029] SIS, SEBS, TOTM and antioxidant 1010 were weighed in proportion and added to a horizontal kneader that had been preheated for 80 minutes (wall temperature 190°C), kneaded for 50 minutes, and then added in proportion to terpene resin, C 5 Petroleum resin, polyethylene wax, Fischer-Tropsch wax, light calcium carbonate and thermoelectric blast furnace fly ash were kneaded at high temperature (185°C) for 80 minutes. Pour into a 25cm×15cm×7cm cube box (lined with high-temperature release paper) in a molten state, and wrap it with release paper after cooling.

Embodiment 3

[0030] Embodiment 3, automobile hot-melt lamp glue component ratio (mass %)

[0031]

[0032]

[0033] SIS, SEBS, TOTM and antioxidant 1010 were weighed in proportion and added to a horizontal kneader that had been preheated for 60 minutes (wall temperature 200°C), kneaded for 40 minutes and then added hydrogenated rosin pentaerythritol ester, C 5 Petroleum resin, polyethylene wax, Fischer-Tropsch wax, light calcium carbonate and thermoelectric blast furnace fly ash were kneaded at high temperature (180°C) for 65 minutes. Pour into a 25cm×15cm×7cm cube box (lined with high-temperature release paper) in a molten state, and wrap it with release paper after cooling.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

An automatic hot-melt lamp adhesive for plastic, metal and glass automobile lamps comprises the following components in percent by mass: 20-30% of styrene-isopentadiene-styrene block copolymer with styrene content of 14-16%, 2030% of styrene-ethylene-butene-styrene block copolymer with styrene content of 30-33%, 25-35% of tackifying resin, 5-10% of light calcium carbonate, 5-10% of thermoelectric blast furnace fly ash, 3-8% of process additive, 2-5% of plasticizer and 0.5-1% of antioxidant. The materials sequentially added into a horizontal kneading machine according to a proportion for heating and kneading, injected in a square mould for molding and encapsulated by using release paper after cooled to demould. The automatic hot-melt lam lamp adhesive has the advantages of high bonding strength, good vibration resistance, low cost and environmental protection, and the like.

Description

technical field [0001] The invention relates to a hot-melt adhesive for bonding and sealing automobile plastic, metal and glass lamps. Background technique [0002] The adhesives used in the production of automotive lamps are mostly two-component epoxy adhesives and polyurethane reactive hot melt adhesives. Two-component epoxy glue is low in cost and widely used in low-end lamps, but after curing, the colloid has high hardness, is prone to brittleness and chapping, has poor vibration resistance, poor weather resistance, long curing time, and low production efficiency; polyurethane reactive hot melt The glue has high bonding strength and excellent vibration resistance. It is widely used in high-end automotive lighting products, but the cost is high, the curing time is long, and it is easy to block the sizing spray gun. Therefore, providing adhesives with low cost, good vibration resistance, good weather resistance, short production time and convenient operation is the goal o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J153/02C09J153/00C09J11/00
Inventor 左向阳刘振宇蔡彦
Owner 中国航天科技集团公司第四研究院第四十二所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com