Methods of fabricating graphene using alloy catalyst

A technology of alloy catalyst and graphene, which is applied in the direction of catalyst activation/preparation, graphene, chemical instruments and methods, etc., and can solve problems such as difficulty in synthesizing graphene single layer

Active Publication Date: 2011-05-11
SAMSUNG ELECTRONICS CO LTD
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in this method, graphene and graphite are mixed during the fabrication process, making it difficult to synthesize a uniform graphene monolayer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Methods of fabricating graphene using alloy catalyst
  • Methods of fabricating graphene using alloy catalyst
  • Methods of fabricating graphene using alloy catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] Example embodiments will now be described more fully with reference to the accompanying drawings, in which example embodiments are shown. Example embodiments may, however, be embodied in many different forms and should not be construed as limited to only the embodiments set forth herein; The concept is fully conveyed to those skilled in the art. In the drawings, the thicknesses of layers and regions are exaggerated for clarity. Like reference numerals refer to like elements in the drawings, and thus their descriptions will be omitted.

[0014] It will be understood that when an element is referred to as being "connected" or "coupled" to another element, it can be directly connected or coupled to the other element or intervening elements may also be present. In contrast, when an element is referred to as being "directly connected" or "directly coupled" to another element, there are no intervening elements present. Like reference numerals refer to like elements through...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Methods of fabricating graphene using an alloy catalyst may include forming an alloy catalyst layer including nickel on a substrate and forming a graphene layer by supplying hydrocarbon gas onto the alloy catalyst layer. The alloy catalyst layer may include nickel and at least one selected from the group consisting of copper, platinum, iron and gold. When the graphene is fabricated, a catalyst metal that reduces solubility of carbon in Ni may be used together with Ni in the alloy catalyst layer. An amount of carbon that is dissolved may be adjusted and a uniform graphene monolayer may be fabricated.

Description

technical field [0001] Exemplary embodiments relate to methods of manufacturing graphene using alloy catalyst layers. Background technique [0002] Graphene is a single layer structure of carbon in which the carbon atoms are arranged in a chemically stable hexagonal (honeycomb) lattice. The electrical properties of graphene are semimetallic because its conduction and valence bands overlap only at the Dirac point. The electron transport mechanism of graphene is ballistic, and the effective mass of electrons is zero. Thus, graphene can be used as a channel with high electron mobility to fabricate field effect transistors. 10 8 A / cm 2 A current density of 100 times that of copper (Cu) can flow in graphene. Since a single layer of graphene has a visible light absorption level of about 2%, the graphene layer is transparent. Furthermore, graphene is considered a rigid material given its Young's modulus of about 1 Pa. [0003] Due to the above physical, optical and mechanica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/04
CPCB01J23/755B01J37/347B82Y30/00B82Y40/00C01B2204/04C23C16/0281C23C16/26C01B32/186
Inventor 禹轮成戴维·徐徐顺爱郑现钟姜世拉许镇盛
Owner SAMSUNG ELECTRONICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap