Method for preparing pine-like cadmium sulfide from ethylenediamine type ionic liquid

An ethylenediamine-type, ionic liquid technology, applied in the direction of cadmium sulfide, etc., can solve the problems of high cost, complicated preparation procedures, and unfavorable industrialization of nanomaterials, and achieve the effects of low cost, high purity, and simple procedures

Inactive Publication Date: 2011-04-27
LIAONING UNIVERSITY OF PETROLEUM AND CHEMICAL TECHNOLOGY
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the preparation of these nanomaterials, ionic liquids in which the cation is imidazole are mostly used. The preparation procedure of this ionic liquid is complicated and the cost is high, which is not conducive to the industrialization of the preparation of nanomaterials with ionic liquids.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing pine-like cadmium sulfide from ethylenediamine type ionic liquid
  • Method for preparing pine-like cadmium sulfide from ethylenediamine type ionic liquid
  • Method for preparing pine-like cadmium sulfide from ethylenediamine type ionic liquid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Take 30ml of ethylenediamine-type ionic liquid and mix with 10ml of deionized water, add 0.3g of thiourea and 0.3g of cadmium chloride dihydrate and stir until a transparent solution is formed. Then it was transferred to a 50ml autoclave and heated at 180°C to 200°C for 12h. After the reaction, the product was isolated, washed to remove impurities, and dried at 80°C for 6h.

[0021] observed directly under a field emission scanning electron microscope. figure 1 , it can be seen from the figure that the overall shape of the product is pine-like, the purity is very high, and there is no other shape. Each branch is a rod-shaped structure, and the top of the rod is sharper, but the length and thickness of the rods are quite different.

[0022] figure 2 is the XRD pattern of the sample. After calibration, all diffraction peaks are consistent with the standard spectrum (PDF.No 41-4019), and no other impurity peaks are found. After analysis, the obtained product be...

Embodiment 2

[0024] Take 30ml of ethylenediamine-type ionic liquid and mix with 10ml of deionized water, add 0.3g of thiourea and 0.3g of cadmium chloride dihydrate and stir until a transparent solution is formed. Then transfer to a 50ml autoclave and heat at 180°C to 200°C for 14h. After the reaction, the product is isolated, washed to remove impurities, and dried at 80°C for 6h.

[0025] The morphology and figure 1 basically the same.

Embodiment 3

[0027] Take 30ml of ethylenediamine-type ionic liquid and mix with 10ml of deionized water, add 0.3g of thiourea and 0.3g of cadmium chloride dihydrate and stir until a transparent solution is formed. Then transfer to a 50ml autoclave and heat at 180°C to 200°C for 16h. After the reaction, the product is isolated, washed to remove impurities, and dried at 80°C for 6h.

[0028] The morphology and figure 1 basically the same.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of preparation methods of cadmium sulfide (CdS) as an inorganic material, in particular to a method for preparing pine-like cadmium sulfide, which comprises the following steps of: (1) dissolving ethylenediamine into deionized water, then adding fluoboric acid, steaming water in the mixed liquid to obtain an ethylenediamine type ionic liquid; (2) mixing the ethylenediamine type ionic liquid prepared in the step (1) with the deionized water, adding a sulfide and cadmium chloride dihydrate to form a transparent solution; and (3) heating in a high-pressure autoclave to react, and then separating to obtain the target product. The heating temperature in the step (3) is 180-200 DEG C; the volume ratio of the ethylenediamine type ionic liquid to the deionized water in the step (2) is 3:1; and the sulfide in the step (2) is sulfourea. In the invention, the pine-like cadmium sulfide is prepared with a hydrothermal synthesis method with simple and easy operation, low cost, high product purity and possibility for mass production.

Description

technical field [0001] The invention relates to the field of preparation methods of inorganic material cadmium sulfide (CdS), in particular to the preparation method of pine dendritic cadmium sulfide. Background technique [0002] As an important semiconductor material, cadmium sulfide is widely used in photocatalysts, gas sensors, laser and infrared detectors, solar cells, light-emitting diodes and other optical devices. At present, its preparation methods mainly include template method, thermal evaporation method, Chemical solution method, etc. The chemical synthesis method is simple and effective, and it is the most widely used method for the synthesis of cadmium sulfide nanomaterials. When synthesizing nanomaterials, some toxic reagents, such as ethylenediamine, are often used. Although many novel nanomaterials have been synthesized by using ethylenediamine, from the perspective of green chemistry, extreme conditions such as high temperature, anhydrous and oxygen-free,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G11/02
Inventor 赵荣祥李秀萍
Owner LIAONING UNIVERSITY OF PETROLEUM AND CHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com