Method for reinforcing ZK60 magnesium alloy by adding Sc

A magnesium alloy and alloy technology, applied in the field of adding Sc to strengthen ZK60 magnesium alloy, can solve the problems of low strength and plasticity, speed up the industrial application of ZK60 magnesium alloy, etc. Effect of yield strength

Inactive Publication Date: 2012-07-04
CHONGQING UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem that the application of the existing ZK60 magnesium alloy is limited due to its low strength and plasticity, and proposes to improve its mechanical properties by adding rare earth Sc elements, thereby speeding up the industrial application of ZK60 magnesium alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for reinforcing ZK60 magnesium alloy by adding Sc
  • Method for reinforcing ZK60 magnesium alloy by adding Sc
  • Method for reinforcing ZK60 magnesium alloy by adding Sc

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The Sc-containing ZK60 magnesium alloy of this embodiment includes the following components by weight percentage: Zn 5.9%, Zr 0.5%, Sc 0.1%, and the balance is Mg.

Embodiment 2

[0021] The Sc-containing ZK60 magnesium alloy of this embodiment includes the following components by weight percentage: Zn 6.0%, Zr 0.6%, Sc 0.2%, and the balance is Mg.

Embodiment 3

[0023] The Sc-containing ZK60 magnesium alloy of this embodiment includes the following components by weight percentage: Zn 6.0%, Zr 0.8%, Sc 0.4%, and the balance is Mg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for reinforcing a ZK60 magnesium alloy by adding Sc, which is realized by adding a rare-earth element Sc into the ZK60 magnesium alloy. The method comprises the following concrete steps of: smelting and ingot making, homogenizing, hot-extruding, heat treatment and the like. Because of the addition of the Sc, crystalline grains of the ZK60 magnesium alloy is effectively refined, intergranular reticular precipitated phases become thin with uniform distribution, and thin and diffused particle-shaped precipitated phases are formed at a crystal boundary, and after the intergranular reticular precipitated phases and thin and diffused particle-shaped precipitated phases are subjected to homogenization, extrusion and heat treatment, the tensile strength of the alloy can reach 364MPa, the yield strength can reach 352MPa and the yield ratio is close to 1. Compared with the common ZK60 alloy, a product in the method has the tensile strength and the yield strengthwhich are respectively improved by 39MPa and 67MPa, and thus, the tensile strength and the yield strength of the ZK60 magnesium alloy are obviously improved and the industrial application range of the ZK60 magnesium alloy is widened.

Description

technical field [0001] The invention relates to a method for strengthening ZK60 magnesium alloy by adding Sc, which belongs to the field of metal materials and metallurgy. Background technique [0002] Magnesium and magnesium alloys are the lightest materials in metal structural materials for engineering applications. They have low density, high specific strength, high specific stiffness, good casting performance, good shock absorption, good anti-magnetic properties, easy cutting and stable dimensions. It has the advantages of high stability and has good application prospects in the fields of aviation, transportation and electronics. [0003] Among wrought magnesium alloys, ZK60 magnesium alloy, as a typical representative of Mg-Zn-Zr wrought magnesium alloy, has a good combination of strength, plasticity and corrosion resistance, and its specific strength has exceeded some high-strength aluminum alloys, but Its strength and plasticity still cannot meet the requirements in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C23/04C22C1/03C22F1/06
Inventor 潘复生刘婷婷王维青吴璐张喜燕杨明波
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com