Multiple-aperture carbon granule air purification agent and preparation method thereof

An air purifier, multi-pore technology, applied in chemical instruments and methods, separation methods, gas treatment and other directions, can solve the problems of weak plant carbon activity and poor meteorological adsorption function, and achieve high adsorption capacity and reasonable design.

Active Publication Date: 2011-01-19
ZHEJIANG JIANZHONG BAMBOO IND
View PDF4 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the activity of plant charcoal is very weak, and the meteorological adsorption function is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 1) Weigh 30 parts of 325 mesh bamboo charcoal powder, 40 parts of attapulgite, 25 parts of sepiolite, 5 parts of chabazite, 0.5 part of 1227 surfactant, 2 parts of pore-forming agent sodium sulfate and 5 parts of bamboo vinegar, and set aside , the above-mentioned attapulgite, sepiolite and chabazite have a purity greater than 80%;

[0029] 2) mixing and pulverizing the attapulgite, sepiolite and zeolite of the weight ratio to below 200 mesh;

[0030] 3) adding the carbon powder in the weight ratio to the mixture obtained in step 2), and stirring evenly;

[0031] 4) adding the pore-forming agent sulfate aqueous solution containing the weight ratio to the mixture obtained in step 3), carrying out granulation and pore making, while spraying the surfactant aqueous solution and the bamboo vinegar liquid containing the weight ratio;

[0032] 5) Then dry at 100°C until the water content in the mixture reaches 10-15%;

[0033] 6) Finally, roast at 300° C. for 3 hours to prod...

Embodiment 2

[0036] 1) Weigh 40 parts of 400 mesh bamboo charcoal powder, 30 parts of attapulgite, 20 parts of sepiolite, 5 parts of clindenite, 5 parts of chabazite, 3 parts of 1227 surfactant, 12 parts of pore-forming agent aluminum sulfate and bamboo vinegar 8 parts of liquid, set aside;

[0037] 2) mixing and pulverizing the attapulgite, sepiolite and zeolite of the weight ratio to below 200 mesh;

[0038] 3) adding the carbon powder in the weight ratio to the mixture obtained in step 2), and stirring evenly;

[0039] 4) Add the pore-forming agent sulfate aqueous solution containing the weight ratio to the mixture obtained in step 3), the concentration of the pore-forming agent sulfate solution is 50%, carry out granulation and pore making, and spray the pore-forming agent containing the weight ratio at the same time. Ratio surfactant aqueous solution and bamboo vinegar;

[0040] 5) Then carry out drying treatment at 90°C until the water content in the mixture reaches 10-15%;

[004...

Embodiment 3

[0044] 1) Weigh 70 parts of 200 mesh bamboo charcoal powder, 10 parts of attapulgite, 10 parts of sepiolite, 10 parts of clindenite, 1 part of 1227 surfactant, 5 parts of pore-forming agent potassium sulfate and 10 parts of bamboo vinegar, and set aside ;

[0045] 2) mixing and pulverizing the attapulgite, sepiolite and zeolite of the weight ratio to below 200 mesh;

[0046] 3) adding the carbon powder in the weight ratio to the mixture obtained in step 2), and stirring evenly;

[0047] 4) Add the pore-forming agent sulfate aqueous solution containing the weight ratio to the mixture obtained in step 3), the concentration of the pore-forming agent sulfate solution is 50%, carry out granulation and pore making, and spray the pore-forming agent containing the weight ratio at the same time. Ratio surfactant aqueous solution and bamboo vinegar;

[0048] 5) Then carry out drying treatment at 80°C until the water content in the mixture reaches 10-15%;

[0049]6) Finally, roast at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a multiple-aperture carbon granule air purification agent and a preparation method thereof, belonging to the technical field of air purification agents. The multiple-aperture carbon granule air purification agent is prepared from carbon powder, attapulgite, sepiolite, zeolite, cationic surfactant, pore-forming material and bamboo vinegar. The multiple-aperture carbon granule air purification agent has reasonable design. After the carbon powder (containing plant charcoal and active carbon), and nanometer mineral matters of attapulgite, sepiolite, zeolite, and the like are treated, the adsorptive capacity of the original plant charcoal is improved by more than 5 times, the adsorptive capacity of the active carbon is improved by more than twice, and the added cationic surfactant and bamboo vinegar increase the effects of sterilization and bacteriostasis. Compared with other adsorbents in the prior art, the air purification agent still has higher adsorption capacity even in higher temperature and lower adsorbate partial pressure, and remains the functions of releasing negative ions and far infrareds of the plant charcoal at the same time, and the prepared granule has rigid characters without dust and does not pollute contactants and a human body.

Description

technical field [0001] The invention belongs to the technical field of air purifiers, and in particular relates to a porous carbon particle air purifier and a production method thereof. Background technique [0002] Plant charcoal, especially bamboo charcoal, has a certain moisture absorption function, and also has the function of generating far infrared rays and negative ions. Therefore, it is a relatively good environmental protection and fitness functional material. However, their adsorption capacity, or the ability to adsorb organic pollutants such as toluene and xylene present in the air, and chemical pollutants such as ammonia, sulfur dioxide, and carbon monoxide, are very weak. This limits their range of application. Especially in the state of serious air pollution in the world today, people put forward higher requirements for the adsorption materials for indoor environmental pollution control. [0003] Compared with activated carbon, the ability of activated carbo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/20B01J20/30B01D53/04
CPCB01D53/02B01J20/20B01D2253/102B01J2220/42B01J20/3064B01D2257/406B01D2258/06B01D2257/502B01J20/3021B01J20/16B01D2257/302B01J20/12B01D2257/7027B01J2220/485B01J20/3078B01D53/04B01J20/30
Inventor 丁建中李沧海丁梦瑶
Owner ZHEJIANG JIANZHONG BAMBOO IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com