Adhesive for automobile adhesive film and preparation method thereof

An automotive film and adhesive technology, applied in the direction of adhesive types, ester copolymer adhesives, etc. It can not compete with the performance of the agent, and cannot enter the high-end market, etc., to achieve the effect of good compactness, improved transparency and small dispersion coefficient.

Inactive Publication Date: 2010-10-20
NANTONG GAOMENG NEW MATERIAL
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the prosperity of the domestic auto market, the car film industry has gradually formed a scale. Thousands of domestic film adhesive suppliers have been unable to enter the high-end market due to technical defects.
At present, the high-performance, solvent-based special adhesive technology for automotive film is mainly monopolized by multinational giants such as Rohm and Haas and 3M. still unable to compete with the aforementioned multinational giants
[0003] The defect of most adhesive products in the market at present is that the acrylic system as the main body cannot meet the comprehensive balance of high stickiness, high peel strength and high transparency, weather resistance and heat resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] This embodiment provides a kind of adhesive for automobile film, which is a kind of high-strength adhesive, which can be used for automobile glass film. The adhesive is composed of the following components by mass percentage:

[0030] Acrylic soft monomer: 25-45%

[0031] Hard monomer: 5~10%

[0032] Acrylic functional monomer: 3-10%

[0033] Solvent type free radical initiator: 0.1~2.0%

[0034] Organic solvent: 40~50%

[0035] Mercaptan chain transfer agent: 0.05~0.5%

[0036] Silane coupling agent: 0.5~5%

[0037] The preparation method of this adhesive is as follows:

[0038] Mix the acrylate soft monomer, hard monomer, acrylic functional monomer, solvent-based radical initiator accounting for 2 / 3 of the total mass of the solvent-based radical initiator, and mercaptan chain transfer agent in the above formula evenly To form a monomer mixed solution, the monomer mixed solution accounting for 2 / 3 to 3 / 4 of the total mass of the monomer mixed solution is mixed wi...

Embodiment 2

[0047] This embodiment provides a kind of adhesive for automobile film, which is a kind of high-strength adhesive, which can be used in automobile film. The components and consumption of the adhesive are as follows:

[0048] raw material

parts by weight

Butyl acrylate

13

2-Ethylhexyl Acrylate

18

Ethyl methacrylate

10

[0049] raw material

parts by weight

acrylic acid

4

Hydroxyethyl Acrylate

3

Glycidyl acrylate

2

Benzoyl peroxide

0.5

dodecyl mercaptan

0.1

ethyl acetate

36

Toluene

12

γ-Aminopropyltrimethoxysilane

1.4

[0050] The preparation method of this adhesive is as follows:

[0051]Mix butyl acrylate, 2-ethylhexyl acrylate, ethyl methacrylate, acrylic acid, hydroxyethyl acrylate, glycidyl acrylate with 0.4 parts of benzoyl peroxide and all dodecanethiol to form Monomer mixture, the monomer mixture accou...

Embodiment 3

[0053] This embodiment provides a kind of adhesive for automobile film, which is a kind of high-strength adhesive, which can be used in automobile film. The components and consumption of the adhesive are as follows:

[0054] raw material

parts by weight

ethyl acrylate

8

2-Ethylhexyl Acrylate

27

Methyl acrylate

7

Methacrylate

2

[0055] raw material

parts by weight

Hydroxyethyl Acrylate

5

Glycidyl methacrylate

1

Azobisisobutyronitrile

0.3

Benzoyl peroxide

0.4

dodecyl mercaptan

0.1

ethyl acetate

24

Toluene

24

γ-Aminopropyltriethoxysilane

1.2

[0056] The preparation method of this adhesive is as follows:

[0057] Butyl acrylate, 2-ethylhexyl acrylate, methyl acrylate, methacrylic acid, hydroxyethyl acrylate, glycidyl methacrylate and 0.4 parts by weight of benzoyl peroxide and azobisisobutyronitril...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an adhesive for an automobile adhesive film and a preparation method thereof, and belongs to the field of adhesives. The adhesive consists of 25-45% of acrylate soft monomers, 5-10% of hard monomers, 3-10% of acrylic acid series functional monomers, 0.1-2.0% of solvent initiator, 40-50% of organic solvent, 0.05-0.5% of thiol chain transfer agent, 0.5-5% of silane coupling agent and the like. The adhesive is mainly used as a protective film for automobile glass, and is formed by polymerizing monomers with similar refraction coefficients. The film formed by the adhesive polymer has the advantages of favorable transparence, outstanding weatherability and high yellowing resistance, and can satisfy the demands of adhesives for the automobile adhesive film.

Description

technical field [0001] The invention relates to the field of adhesives, in particular to a high-strength solvent-based adhesive for automobile film and a preparation method thereof. Background technique [0002] With the prosperity of the domestic automobile market, the automobile film industry has gradually formed a scale. Thousands of domestic film adhesive suppliers have been unable to enter the high-end market due to technical defects. At present, the high-performance, solvent-based special adhesive technology for automotive film is mainly monopolized by multinational giants such as Rohm and Haas and 3M. Still unable to compete with the above-mentioned multinational giants. [0003] The defect of most adhesive products in the market at present is that the acrylic system as the main body cannot meet the comprehensive balance of high stickiness, high peel strength and high transparency, weather resistance and heat resistance. Contents of the invention [0004] The purp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08
Inventor 李岗沈峰邓煜东
Owner NANTONG GAOMENG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap