Acid-resisting complex phase ceramic coating and preparation method thereof

A technology of multiphase ceramics and ceramic coatings, applied in the field of acid-resistant multiphase ceramic coatings and their preparation

Inactive Publication Date: 2010-08-25
NORTH CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Research in this area has not been reported at home and abroad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acid-resisting complex phase ceramic coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0017] Firstly, 2wt% adhesive and 2wt% dispersant are used to make a concentrated solution, and then 25.4wt% water is added to make a premixed solution. Mix 25wt% aluminum oxide, 10wt% silicon dioxide, and 35wt% silicon carbide micropowder (200 mesh sieve 2 o 3 / SO 2 / SiC acid-resistant composite ceramic coating.

example 2

[0019] Firstly, 3wt% adhesive and 3wt% dispersant are used to make a concentrated solution, and then 26.3wt% water is added to make a premixed solution. Mix 22wt% aluminum oxide, 12wt% silicon dioxide, and 33wt% silicon carbide micropowder (200 mesh sieve 2 o 3 / SO 2 / SiC acid-resistant composite ceramic coating.

example 3

[0021] Firstly, 5wt% adhesive and 3wt% dispersant are used to make a concentrated solution, and then 27.5wt% water is added to make a premixed solution. Mix 23wt% aluminum oxide, 11wt% silicon dioxide, and 30wt% silicon carbide micropowder (200 mesh sieve 2 o 3 / SO 2 / SiC acid-resistant composite ceramic coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention belongs to an acid-resisting complex phase ceramic coating and a preparation method thereof. Firstly, 2-5 wt% of adhesive and 2-4 wt% of dispersing agent are prepared into concentrated solution, and then 25-30 wt% of water is added to prepare premixing solution; alumina, silica and silicon carbide micro powder are mixed at ratio and are added into premixing solution and the mixture is carried out ball milling for 2 hours; 0.5-1 wt% of catalyst is added for ball milling for 0.5 hour; after slurry viscosity is suitable, the slurry is brushed or sprayed by a spray gun on the surface of materials, such as cement, concrete and the like to form an even coating; and after heat treatment, Al2O3 / SO2 / SiC series anti-reversion complex phase ceramic coating is obtained. The complex phase ceramic coating not only can be applied on the surface of cement, concrete and the like, but also can be used for the anti-corrosion of metal surface. The coating surface is even and compact, has no cracks and has favorable abrasion performance and favorable acid resistant erosiveness.

Description

technical field [0001] The invention relates to an acid-resistant multiphase ceramic coating and a preparation method thereof, belonging to the field of inorganic non-metallic materials. Background technique [0002] my country is a big coal storage country, and coal is the main energy consumed. Especially after joining the WTO, my country's industrial production scale has continued to expand, and industries such as electric power, steel, and cement have continued to rise, causing my country's coal consumption to increase day by day. In 2007, the total coal consumption reached 1,191.53 million tons, ranking first in the world. It is nearly twice the 567.26 million tons of the United States, which ranks second, and even the per capita consumption has reached 0.91 tons per person, ranking 15th in the world. One of the biggest problems with burning coal is sulfur corrosion. Standard coal contains about 1wt% sulfur, which mainly exists in four forms: pyrite, organic sulfur, sul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/85
Inventor 沈毅沈巍李锋锋张明熹李红生李大鹏
Owner NORTH CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com