Sea-island ultrafine fiber, polyurethane leather and base fabric thereof and preparation method

A technology of ultra-fine fiber and polyurethane, applied in the direction of fiber processing, conjugated synthetic polymer rayon, non-woven fabric, etc., can solve the problems of increased production cost and difficulty in recycling, and achieves reduced production cost, easy removal, and effective good effect

Active Publication Date: 2012-05-02
HUAFON MICROFIBER SHANGHAI
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the defects that the water-soluble modified polyester is used as the "sea" phase in the existing island-fixing type sea-island microfiber, and when it involves the preparation process of synthetic leather, it is difficult to recycle and increase the production cost. Provided is a kind of Dingdao superfine fiber, polyurethane synthetic leather and its base cloth, which can recycle the marine materials involved and has low production cost, and the preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Preparation of sea-island microfibers: The sea-component low-density polyethylene chips and the island-component polycaprolactam chips are heated by their respective screw extruders according to the mass ratio of the island component to the sea component of 70:30. The temperature of the PA6 screw is 290°C, and the temperature of the PE screw is 180°C. After being extruded and melted, it becomes a spinnable melt. After the silk is produced, it is cooled and shaped by the surrounding air, and then processed through the processes of winding, bunching, drawing, crimping, shaping and cutting to obtain sea-island ultra-fine fibers. Wherein, the density of the sea component low-density polyethylene is 0.915g / cm 3 , the melt index is 4.3g / min; the relative viscosity of the island component polycaprolactam is 2.76η.γ.

[0034] After testing, the prepared island-in-the-sea microfibers are 4.4-denier fixed-island type sea-island ultrafine fibers.

[0035] Preparation of polyuret...

Embodiment 2

[0042] Preparation of sea-island microfibers: The sea-component low-density polyethylene chips and the island-component polycaprolactam chips are heated according to the mass ratio of the island component to the sea component of 75:25, respectively, through their respective screw extruders, Among them, the temperature of PA6 screw is 290°C, and that of PE screw is 180°C. After being extruded and melted, it becomes a spinnable melt. After the silk is produced, it is cooled and shaped by the surrounding air, and then processed through the processes of winding, bunching, drawing, crimping, shaping and cutting to obtain sea-island ultra-fine fibers. Wherein, the density of the sea component low-density polyethylene is 0.940g / cm 3 , the melt index is 5.7g / min; the relative viscosity of the island component polycaprolactam is 2.84η.γ.

[0043] After testing, the prepared island-in-the-sea microfibers are 4.4-denier fixed-island type sea-island ultrafine fibers.

[0044] Preparatio...

Embodiment 3

[0051] Preparation of sea-island microfibers: The sea-component low-density polyethylene chips and the island-component polycaprolactam chips are heated according to the mass ratio of the island component to the sea component of 75:25, respectively, through their respective screw extruders, The temperature of the PA6 screw is 275°C, and the temperature of the PE screw is 225°C. After being extruded and melted, it becomes a spinnable melt. After the silk is produced, it is cooled and shaped by the surrounding air, and then processed through the processes of winding, bunching, drawing, crimping, shaping and cutting to obtain sea-island ultra-fine fibers. Wherein, the density of the sea component low-density polyethylene is 0.925g / cm 3 , the melt index is 5.0g / min; the relative viscosity of the island component polycaprolactam is 2.80η.γ.

[0052] After testing, the prepared island-in-the-sea microfibers are 4.4-denier fixed-island type sea-island ultrafine fibers.

[0053] Pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sea-island ultrafine fiber, polyurethane leather and base fabric thereof and preparation method. The sea-island ultrafine fiber is composed of sea component and island component; wherein the sea component is low density polyethylene, the island component is polycaprolactam, and the mass ratio of the sea component and the island component is 70:30 to 75:25. The preparation method includes that the sea-island ultrafine fiber is composed of the components by the mass ratio and is prepared by conventional technology. The polyurethane leather and base fabric thereof related by the invention are all prepared by the sea-island ultrafine fiber of the invention, and conventional preparation technology is adopted. The sea-island ultrafine fiber of the invention can recyclerelated sea phase material and reduce production cost when being used for preparing polyurethane leather and base fabric thereof.

Description

technical field [0001] The invention belongs to the technical field of synthetic leather, in particular to a Dingdao superfine fiber, polyurethane synthetic leather and its base cloth, and a preparation method. Background technique [0002] At present, sea-island microfibers used in the production of synthetic leather in China can be divided into indefinite island-type sea-island microfibers and fixed-island-type sea-island microfibers according to the different production technologies adopted. The islands in the indeterminate island-type sea-island microfibers are uncontrollable and discontinuous on the longitudinal axis. After solvent treatment, ultrafine fibers with thick and thin, irregular lengths and short lengths are formed; while the fixed-island-type sea-island ultrafine fibers The fiber is continuous on the longitudinal axis, and is a uniform ultrafine fiber with a fixed number of islands, a uniform fineness, and a consistent length. The number of islands in the f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/12D01F8/06D01D5/28D04H1/46D04H1/4382D06N3/14
CPCY02P70/62
Inventor 王克亮李文刚刘文辉孙向浩胡忠杰吴义根王贺玲
Owner HUAFON MICROFIBER SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com