A nickel-based welding rod

A technology of nickel-based welding rod and welding rod, which is applied in the direction of welding medium, welding equipment, welding/cutting medium/material, etc., and can solve problems such as arc stability and slag coverage, low content of diffusible hydrogen, poor weld formation, etc. , to achieve the effect of good slag removal, excellent operation performance and moderate plasticity

Inactive Publication Date: 2011-11-30
LUOYANG SHUANGRUI SPECIAL ALLOY MATERIALS
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This coating type electrode has good slag removal and low diffusible hydrogen content, but the arc stability and slag coverage are poor, the weld shape is not good, and the weld bead is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A nickel-based welding rod
  • A nickel-based welding rod

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The components of the coating used in the electrode of the present invention and their mass fractions are as follows: rutile: 50%, titanium dioxide: 2%, fluorite: 23%, cryolite 8%, phlogopite: 2%, zircon sand: 3% %, soda ash 1.5%, metal manganese: 5%, ferro-titanium: 3.5%, ferro-niobium: 2%. Among them, Ti in ferro-titanium: 25-35%, and Nb in ferro-niobium: 50-60%.

[0032] The mechanical property requirements of weld core deposited metal are: R P0.2 ≥360MPa, Rm≥550Mpa, A≥27%; the mass percentage of the chemical composition of the welding core deposited metal is: C: 0.017, S: 0.0081, P: 0.005, Si: 0.821, Mn: 5.10, Cr: 15.1, Ni : 68.93, Fe: 7.83, Cu: 0.040, Ti0.142, Nb: 1.37.

[0033] After mixing the raw materials of the drug skin evenly, pulverize the particle size below 40 mesh, add potassium sodium water glass of 43-48Be (20° C.) accounting for 25-30% of the mass content of the solid component, and prepare a paste for the drug skin. Using the deposited metal with ...

Embodiment 2

[0036] The components of the drug skin and their mass parts are as follows: rutile: 36%, titanium dioxide: 7%, fluorite: 30%, cryolite 5%, phlogopite: 4%, zircon sand: 2%, soda ash 1% , Manganese metal: 10%, ferro-titanium: 2%, ferro-niobium: 3%.

[0037] Other conditions are identical with embodiment 1.

[0038] The electrode produced according to the above process has smooth surface, high yield and stable eccentricity; stable arc during welding, good slag removal, and excellent operating performance of the electrode; beautiful weld shape, moderate bead height, and moderate weld penetration angle; Metal strength and plasticity are moderate.

Embodiment 3

[0040] The components of the coating and their mass parts are as follows: rutile: 45%, titanium dioxide: 6%, fluorite: 20%, cryolite 3%, phlogopite: 3.5%, zircon sand: 4%, soda ash 0.5% , Manganese metal: 10%, ferro-titanium: 4%, ferro-niobium: 4%.

[0041] Other conditions are identical with embodiment 1.

[0042] The electrode produced according to the above process has smooth surface, high yield and stable eccentricity; stable arc during welding, good slag removal, and excellent operating performance of the electrode; beautiful weld shape, moderate bead height, and moderate weld penetration angle; Metal strength and plasticity are moderate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a welding material technology, and specifically introduces a nickel-based electrode. The electrode uses SNi6062 welding wire as the welding core, and the mass content of the solid component of the coating is: rutile: 36-50%, titanium dioxide: 2-7%, Fluorite: 20-30%, cryolite 3-8%, phlogopite: 2-4%, zircon sand: 2-4%, soda ash 0.5-1.5%, metal manganese: 5-10%, Ti 25- 35% ferro-titanium: 2-4%, ferro-niobium containing 50-60% Nb: 2-4%. The nickel-based electrode of the present invention has excellent production process performance, smooth electrode surface, high yield, and stable eccentricity; stable arc during welding, basically no spatter, good slag removal, and excellent electrode operability; beautiful weld shape and moderate bead height , moderate weld wetting angle; moderate strength and plasticity of deposited metal.

Description

technical field [0001] The present invention N relates to a technology in the field of welding materials, in particular to a nickel-based welding rod. Background technique [0002] With the development of industry, nickel-based alloys are used more and more widely. Nickel-based alloys refer to alloys based on nickel (Ni≥50%), containing other alloying elements, and resistant to corrosion in some media. There are mainly nickel, nickel-molybdenum (nickel-molybdenum-iron) alloy, nickel-chromium (nickel-iron) alloy, nickel-chromium-molybdenum and nickel-iron-chromium and so on. For example, nickel-based superalloys mainly used in the manufacture of aero-engine blades and high-temperature parts on rocket engines, nuclear reactors, and energy conversion equipment; nickel-based corrosion-resistant alloys used in the manufacture of various corrosion-resistant parts; through surfacing and spraying It is a nickel-based wear-resistant alloy that is coated on the surface of other base...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/36B23K35/40
Inventor 张宝伟黄连涛郭敬杰
Owner LUOYANG SHUANGRUI SPECIAL ALLOY MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com