Automotive V-ribbed belt and manufacture method thereof

A technology for multi-ribbed belts and automobiles, used in belts, transmission belts, other household appliances, etc., can solve the problems of affecting the overall performance of automobiles, short aging service life, unfavorable physical and mental health, etc., and achieve high tensile strength and stable friction coefficient. , Good effect of high and low temperature resistance

Inactive Publication Date: 2010-04-14
绍兴上虞宝来同步带有限公司
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The raw material of the V-ribbed belt currently used in automobile engines is composed of neoprene and related additives, which has poor resistance to high and low temperatures, is not stable enough, and has a short service life due to aging
In addition, the biggest disadvantage is that there is a lot of noise during transmission. When used at low speeds or with rapid changes in angular velocity, and after a period of use, the wedge surface is worn, hardened or the tension is loose, or after being exposed to water in rainy days, it will emit harsh sharp noises during transmission. The sound affects the overall performance of the car and is also detrimental to the physical and mental health of the human body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Automotive V-ribbed belt and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] A volumetric 35L internal mixer was used for mixing.

[0064]One-stage mixing, take the main raw material 25kg neoprene rubber and masticate for 55 seconds, add 1kg magnesium oxide, 0.5kgODA, 0.125kg stearic acid, 1.875kg reinforcing agent PFM-C and 9.375kg carbon black 774, 0.25kg accelerator DM , 0.5kg dispersant AT-C, 1.5kg aromatic hydrocarbon oil, mixed for 120 minutes to sweep the powder, then added 5kg of aramid fibers with a length of 3mm, mixed for 110 seconds, the temperature was less than 100 ° C, and after cooling for 4 hours, the mixture was obtained Rubber mixing.

[0065] Two-stage mixing, take the mixed rubber obtained in the above-mentioned one-stage mixing and account for 2 / 3 of the total weight, then add 1.25kg zinc oxide, 0.5kg adhesive RA, 0.25kg anti-aging agent 4020, and then add the remaining 1 / 3 3 The weight of the mixed rubber is mixed for 110 seconds, the temperature is raised to 80°C, and the material is discharged, and it is pressed into pi...

Embodiment 2

[0081] A volumetric 35L internal mixer was used for mixing.

[0082] One-stage mixing, take 25kg neoprene rubber as the main raw material and masticate for 55 seconds, add 0.89kg magnesium oxide, 0.53kg anti-aging agent BLE, 0.1kg stearic acid, 1.67kg reinforcing agent PFM-C, 8.33kg carbon black 774, 0.15 kg Accelerator M, 0.15kg Accelerator DM, 0.45kg Dispersant AT-C, 0.875kg Aromatic Oil, 0.875kg Dioctyl Ester, mixed for 120 minutes to sweep powder, then added 4.5kg length of 6mm BPO fiber, mixed Refining for 130 seconds, the temperature is less than 100°C, and after cooling for 4 hours, carry out two-stage mixing.

[0083] Two-stage mixing, take the mixed rubber obtained from the above-mentioned one-stage mixing, accounting for 2 / 3 of the total weight, and then add 1.11kg zinc oxide, 0.028kg binder HMM, 0.028kg binder RA, 0.42kg white carbon black , 0.27kg anti-aging agent 4020, then add the remaining 1 / 3 weight of the mixed rubber and knead for 110 seconds, the temperatur...

Embodiment 3

[0098] A volumetric 35L internal mixer was used for mixing.

[0099] One-stage mixing, taking 25kg neoprene rubber as the main raw material and masticating for 55 seconds, adding 1.11kg magnesium oxide, 0.58kg anti-aging agent BLE, 0.2kg stearic acid, 1.46kg reinforcing agent PFM-C, 7.29kg carbon black 774, 0.375 kg accelerator DM, 0.55kg dispersant AT-C, 2kg dioctyl ester, knead for 120 minutes to sweep the powder, then add 5.25kg of aramid fibers with a length of 5mm, knead for 110 seconds, the temperature is less than 100°C, cool for 4 After 1 hour, the second-stage mixing was carried out.

[0100] Two-stage mixing, take the mixed rubber obtained from the above-mentioned one-stage mixing and account for 2 / 3 of the total weight, add 1.39kg of zinc oxide, 0.575kg of adhesive RA, 0.29kg of anti-aging agent 4020, and then add the remaining 1 / 3 3 weights of mixed rubber were mixed for 110 seconds, the temperature was raised to 80°C for discharge, and the mill was pressed to for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses an automotive V-ribbed belt and a manufacture method thereof. The automotive V-ribbed belt comprises a belt body, wherein the belt body comprises the following raw materials in parts by weight: 100 parts of neoprene, 2.8-3.5 parts of age inhibitor, 35-45 parts of strengthening agent, 6-8 parts of softening agent, 8-12 parts of vulcanizing agent, 1-1.5 parts of promoting agent, 1.5-2.5 parts of dispersant, 15-25 parts of chopped fiber and 1.5-2.5 parts of adhesive. The invention also discloses a manufacture method of the automotive V-ribbed belt. The automotive V-ribbed belt has the characteristics of favorable high and low temperature resistance, wear resistance, high tensile strength and long service life; and through the rib milling technique, fiber floss with the length of 1-3 mm is exposed on the rib surface to enable the friction factor of the automotive V-ribbed belt to be stable, thereby greatly reducing the noise produced when the V-ribbed belt is driven.

Description

technical field [0001] The invention relates to a transmission component, in particular to an automobile V-ribbed belt and a manufacturing method thereof. Background technique [0002] Chinese invention patent 200610049670.8 discloses an elastic V-ribbed belt, including a belt body, a belt wedge and a back. There is a nylon skeleton in the belt body, and a layer of high-modulus low-shrinkage HMLS is added to the back. For the calendered polyester cord fabric, the patent also specifically designs the rubber formula, so that the elongation of the belt body and belt wedge matches the elongation of the skeleton material, and has a certain degree of resilience. [0003] The raw material of the V-ribbed belt currently used in automobile engines is composed of neoprene and related additives, which is poor in high and low temperature resistance, not stable enough, and has a short service life due to aging. In addition, the biggest disadvantage is that there is a lot of noise during...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F16G1/10B29D29/10
Inventor 沈建荣
Owner 绍兴上虞宝来同步带有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap