Preparation method for nano hydroxylapatite doped with metal ions

A technology of nano-hydroxyapatite and metal ions, which is applied in the fields of biomedicine and nano-material preparation, can solve the problems of complex operation, long preparation cycle, and complex sol-gel process, and achieve easy control of dosage and uniform doping Effect

Inactive Publication Date: 2013-04-10
SHAANXI UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the methods for preparing this kind of material are mainly sol-gel method, hydrothermal synthesis method and co-precipitation method, etc. Among them, the hydrothermal synthesis method requires a high temperature and high pressure reaction environment, and the co-precipitation method does not require a high pressure environment but must strictly control the reaction conditions. The operation is more complicated, the preparation cycle is long, and the sol-gel method also has the disadvantages of complicated process and long preparation cycle.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for nano hydroxylapatite doped with metal ions

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1, at first, prepare respectively the Ca(NO 3 ) 2 and (NH 4 ) 2 HPO 4 solution, and by Ca(NO 3 ) 2 and (NH 4 ) 2 HPO 4 The volume ratio is 1.67 mixed with HNO 3 Adjust the pH of the mixed solution to 3 , where AgNO 3 Mass: The volume of solution A is 1×10 -4 (g): 1 (ml), then use HNO 3 Adjust the pH of the mixed solution 2 ) 2 Obtain solution C, wherein, CO(NH 2 ) 2 Quality: The volume of solution B is 0.06 (g): 1 (ml); Finally, under magnetic stirring, the solution C was heated and refluxed at 100°C for 4 hours. After the reaction, it was naturally cooled to room temperature, then vacuum filtered and water After washing, it was dried at 100° C. for 24 hours to finally obtain Ag ion-doped nano-hydroxyapatite crystals. see figure 1 , the results show that the obtained sample is a pure nano-hydroxyapatite crystal, and the grain size calculated by the Sherri formula based on the (002) crystal plane is 28.7nm. There is no silver and its compound c...

Embodiment 2

[0015] Embodiment 2, at first, prepare respectively the Ca(NO 3 ) 2 and (NH 4 ) 2 HPO 4 solution, and by Ca(NO 3 ) 2 and (NH 4 ) 2 HPO 4 The volume ratio is 1.67 mixed with HNO 3 Adjust the pH of the mixed solution 3 ) 3 , where La(NO 3 ) 3 Mass: The volume of solution A is 3×10 -4 (g): 1 (ml), then use HNO 3 Adjust the pH of the mixed solution 2 ) 2 Obtain solution C, wherein, CO(NH 2 ) 2 Quality: The volume of solution B is 0.03 (g): 1 (ml); Finally, under magnetic stirring, solution C was heated and refluxed at 100°C for 3 hours. After the reaction, it was naturally cooled to room temperature, then vacuum filtered and water After washing, it was dried at 100° C. for 24 hours, and finally La ion-doped nano-hydroxyapatite crystals were obtained.

Embodiment 3

[0016] Embodiment 3, at first, prepare respectively the Ca(NO of 0.2mol / L 3 ) 2 and (NH 4 ) 2 HPO 4 solution, and by Ca(NO 3 ) 2 and (NH 4 ) 2 HPO 4 The volume ratio is 1.67 mixed with HNO 3 Adjust the pH of the mixed solution 3 ) 2 , where Cu(NO 3 ) 2 Mass: The volume of solution A is 5×10 -4 (g): 1 (ml), then use HNO 3 Adjust the pH of the mixed solution 2 ) 2 Obtain solution C, wherein, CO(NH 2 ) 2 Quality: The volume of solution B is 0.05 (g): 1 (ml); Finally, under magnetic stirring, solution C was heated and refluxed at 100°C for 5 hours. After the reaction, it was naturally cooled to room temperature, then vacuum filtered and water After washing, it was dried at 100° C. for 24 hours to finally obtain Cu ion-doped nano-hydroxyapatite crystals.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of nano hydroxylapatite doped with metal ions, which comprises the following steps of: firstly, respectively preparing Ca(NO3)2 and (NH4)2HPO4 solution, mixing the Ca(NO3)2 and (NH4)2HPO4 solution, and obtaining clear and transparent solution A; adding metal nitrate into solution A and obtaining clear and transparent solution B; adding CO(NH2)2 into solution B, and obtaining solution C; finally heating and backflowing the solution C for 3 to 5 hours with the temperature of 100 DEG C under the magnetic force stirring; after the reaction is end, naturally cooling to room temperature; then vacuum-filtering, cleaning with water, drying for 24 hours under the temperature of 100 DEG C; and finally, obtaining nano hydroxylapatite crystal doped with metal ions. The preparation method adopts a metal salt solution heating even precipitation method, and takes inorganic salts containing calcium and phosphate group as raw materials; urea is acidity of a control reaction system of an additive; metal salts are added according to the doped proportion of 1 percent to 5 percent; reaction is carried out under the magnetic force stirring and heating conditions; and the backflowing of reaction liquid is adopted to synthesize nanoscale metal-doped nano hydroxylapatite crystal by one step. The method is obviously characterized by even doping and easy control for added amount.

Description

technical field [0001] The invention belongs to the fields of biomedicine and nanometer material preparation, and in particular relates to a preparation method of metal ion-doped nano-hydroxyapatite. Background technique [0002] Hydroxyapatite (Hydroxyapatite, referred to as HAP) is the main inorganic component of natural bone, its structure is similar to natural bone, so it has good biological activity and biocompatibility (L.HENCH L.Bioceramics[J].Journal of the American Ceramic Society, 1998, 81(7): 1705-1728.). It can induce the formation of new bone in a short time after it is implanted in the body, can form osseointegration with the original damaged bone, and is non-toxic and non-carcinogenic, so it is widely used in the field of biomedical engineering as a good biomaterial. However, the infection caused by the implant material often causes premature loosening and falling off of the implant, and causes infection or even necrosis of adjacent tissues and organs, leadin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/12
Inventor 杨辉王栋蔡日强
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com