Hot rolled plate hydrochloric acid pickling corrosion inhibition accelerator

A technology of accelerator and hot-rolled plate, which is applied in the field of electrochemical and chemical metal cleaning, can solve the problems of substrate corrosion, process incompatibility, poor surface quality, etc., and achieve good corrosion inhibition and promotion performance, excellent corrosion inhibition performance , good effect of promoting performance

Inactive Publication Date: 2009-11-25
武钢集团有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, the annual output of new acid rolling mills and reformed original acid rolling mills in China has reached more than one million tons, and the newly installed continuous acid rolling mills and technically improved continuous acid rolling mills all have technological incompatibility. The key points are The pickling speed and board surface quality cannot meet the demand
For example, the quality of some pickling low-carbon steel plates is good, but the surface quality of pickling high-carbon steel and special steel is poor, the substrate is severely corroded, and the speed is extremely low; Spots; some pickling turbulent flow system processes have negative effects, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1: Get 5% of TX-10 surfactant by weight percentage, carboxy cellulose salt 5%, divalent tin salt 90%, after these raw materials are uniformly mixed, be mixed with desalted water concentration and be 30% concentrated solution . The concentration of hydrochloric acid in the pickling solution is 15%, and the corrosion inhibitor accelerator of the present invention is added in the pickling solution, and its weight percentage concentration range is maintained at 1%. When the pickling temperature is 60°C, it can obviously promote the removal of iron oxide scale and Improve the pickling quality of the board surface, and the corrosion inhibition efficiency reaches more than 95%.

Embodiment 2

[0024] Embodiment 2: Get 5% of TX-10 surfactant by weight percentage, 10% of carboxy cellulose salt, 85% of divalent tin salt, after these raw materials are uniformly mixed, be mixed with desalted water concentration and be 30% concentrated solution . The concentration of hydrochloric acid in the pickling solution is 15%, and the corrosion inhibitor accelerator of the present invention is added in the pickling solution, and its weight percent concentration range is maintained at 1%. When the pickling temperature is 70°C, it can obviously promote the removal of iron oxide scale and Improve the pickling quality of the board surface, and the corrosion inhibition efficiency reaches more than 95%.

Embodiment 3

[0025] Embodiment 3: Get 7% of TX-10 surfactant by weight percentage, 8% of carboxy cellulose salt, 85% of divalent tin salt, after these raw materials are uniformly mixed, be mixed with desalinated water and be 30% concentrate . The concentration of hydrochloric acid in the pickling solution is 15%, and the corrosion inhibitor accelerator of the present invention is added in the pickling solution, and its weight percentage concentration range is maintained at 1%. When the pickling temperature is 80°C, it can obviously promote the removal of iron oxide scale and Improve the pickling quality of the board surface, and the corrosion inhibition efficiency reaches more than 90%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hot rolled plate hydrochloric acid pickling corrosion inhibition accelerator in which the compositions and weight percentages thereof are as follows: the weight percentage of surface active agent TX-10 that is octyl phenol polyethylene glycol (10) ether is 5% to 10%, the weight percentage of carboxylic cellulose salt is 5% to 10%, and the weight percentage of stannous salt reducing agent is 80% to 90%; the weight percentage of surface active agent TX-10 that is octyl phenol polyethylene glycol (10) ether is 5% to 10%, the weight percentage of carboxylic cellulose salt is 5% to 10%, and the weight percentage of stannous salt reducing agent is 85% to 90%. The composition weight percentage concentration range of corrosion inhibition accelerator in pickling working fluid keeps between 0.5% and 1%. The hot rolled plate hydrochloric acid pickling corrosion inhibition accelerator in the invention has not only good corrosion inhibition performance but also good acceleration performance, and still has good corrosion inhibition and acceleration performances within a certain range of pickling temperature and hydrochloric acid concentration.

Description

technical field [0001] The invention relates to a hydrochloric acid pickling corrosion inhibitor for hot-rolled plates. The invention belongs to the technical field of electrochemical and chemical method metal cleaning. Background technique [0002] Hydrochloric acid has a strong ability to remove iron scale from hot-rolled plates, and the dissolution rate of iron salt is high. There are very few powdery precipitates in the hydrochloric acid pickling solution. The surface condition after pickling is good, and the effect of hydrogen permeation is small. During the hydrochloric acid pickling process of the hot-rolled plate, it can be seen that a large number of air bubbles emerge from the surface of the steel plate, and at the same time, the oxide scale peels off. A large number of air bubbles are hydrogen released from the acid corrosion of the iron base. The base is also more serious. With the expansion of the scale of iron and steel enterprises, it is more and more requir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23G1/06C23G1/08
Inventor 黄先球石争鸣涂元强柳长福蔡捷刘建容张万灵白会平
Owner 武钢集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products