PU self-drying paint having strong adhesive force for metal glass surface

A technology with strong adhesion and metallic glass, applied in the field of paint, can solve problems such as unsatisfactory bonding between the coating film and the substrate, uneven adhesion of the coating film, and peeling off of the paint layer, and achieve good storage and use effects, fullness The effect of good degree and strong adhesion

Inactive Publication Date: 2009-08-05
广东大中三联科技有限公司
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The application utilizes that acrylate phosphate is a highly active photopolymerizable monomer, and monomer polymerization occurs under ultraviolet irradiation to form a polymer with high adhesion to metals. However, the application formula is general, and the coating film obtained by using this formula The combination with the substrate is not ideal, and UV coatings can form a good paint surface for plate-shaped profiles, but for irregular-shaped daily necessities or handicrafts, because ultraviolet rays cannot be fully and uniformly irradiated to all sides of the product, the formed The adhesion of the coating film to the surface of the product is not uniform, which will cause some paint layers to be firmly bonded to the product, and some paint layers are easy to fall off.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] White PU self-drying metal glass paint

[0027] 1. Preparation of white semi-finished color paste:

[0028] Ingredients and ratio: 44.5% silicone modified epoxy acrylic resin

[0029] Titanium dioxide 40%

[0030] Polycarboxylate amine salt dispersant 0.5%

[0031] Xylene 15%

[0032] According to the above amount, put the silicone modified epoxy acrylic resin into the stirring container, put the titanium dioxide, polycarboxylate amine salt dispersant and toluene into the stirring container under slow stirring, then stir at high speed for half an hour, and put it into the sand mill Grind 2 times until the fineness is 15 microns and set aside;

[0033] 2. Preparation of component A:

[0034] Composition and weight percentage: silicone modified epoxy acrylic resin 57.5%

[0035] Methoxysilane coupling agent 1.5%

[0036] Silicone polyether copolymer wetting agent 1.0%

[0037] White color paste (semi-finished p...

Embodiment 2

[0048] Black PU self-drying metallic glass paint

[0049] 1. Preparation of black semi-finished color paste:

[0050] Ingredients and ratio: 74.5% silicone modified epoxy acrylic resin

[0051] Carbon black 10%

[0052] Polycarboxylate amine salt dispersant 0.5%

[0053] Xylene 15%

[0054]According to the above amount, put the silicone modified epoxy acrylic resin into the stirring container, put the carbon black, polycarboxylate amine salt dispersant and toluene into the stirring container under slow stirring, then stir at high speed for half an hour, and put it into the sand mill Grind 2 times until the fineness is 12 microns and set aside;

[0055] 2. Preparation of component A:

[0056] Composition and weight percentage: silicone modified epoxy acrylic resin 72.5%

[0057] Methoxysilane coupling agent 1.5%

[0058] Silicone polyether copolymer wetting agent 1.0%

[0059] Blac...

Embodiment 3

[0070] Blue PU self-drying metal glass paint

[0071] 1. Preparation of blue semi-finished color paste:

[0072] Ingredients and ratio: silicone modified epoxy acrylic resin 64.5%

[0073] Phthalocyanine Blue 15%

[0074] Polycarboxylate amine salt dispersant 0.5%

[0075] Xylene 20%

[0076] According to the above amount, put the silicone modified epoxy acrylic resin into the stirring container, put the phthalocyanine blue, polycarboxylate amine salt dispersant and toluene into the stirring container under slow stirring, then stir at high speed for half an hour, and then put it into the sand mill Machine grinding 2 times until the fineness is ----, set aside;

[0077] 2. Preparation of component A:

[0078] Composition and weight percentage: silicone modified epoxy acrylic resin 67.5%

[0079] Methoxysilane coupling agent 1.5%

[0080] Silicone polyether copolymer wetting agent 1.0%

[0081] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides PU air-dried paint which needs only one-time construction and has strong adhesive force to a metal or glass surface. The PU air-dried paint contains component A, component B and component C, wherein the component A is main paint, the component B is solidifying agent and the component C is solvent containing active monomer respectively, and the component A, the component B and the component C are mixed together according to the weight percent of 2:1-1.5:2-3. The main paint takes epoxy acrylic resin as film forming matter, the solidifying agent is HDI-TDI composite solidifying agent with a solid content of 50 percent, and the active monomer is acrylate phosphate ester. The PU air-dried paint has high paint film gloss and good paint film fullness, can be strongly adhered to the stainless steel or glass surface, has good water resistance, acid and alkali resistance, wear resistance and the like, can be rapidly dried at a low temperature of 50-80 DEG C and can also be dried by air at normal temperature, is especially suitable for being painted on the surfaces of daily necessities and craftworks which take stainless steel or glass as substrates.

Description

technical field [0001] The present invention relates to a kind of paint, especially to a kind of polyurethane paint (PU self-drying paint) that can be dried by itself at normal temperature, more specifically to a kind of metal substrate such as stainless steel or smooth glass substrate surface with strong adhesion PU self-drying paint. Background technique [0002] Due to the corrosion-resistant and anti-oxidation properties of stainless steel, glass and other materials, there are more and more products based on stainless steel and glass in the daily necessities and handicraft markets. In order to decorate the surface of these products or make the product have better wear resistance and weather resistance, it is usually necessary to paint the surface of the formed product. The surface of stainless steel and glass is inert, and the adhesion of general paint to its surface is not ideal. At present, there are two solutions, one is to use baking paint, and the other is to pre-t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D4/06C09D175/04C09D5/00
Inventor 葛大海彭永泓
Owner 广东大中三联科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap