Oxide ceramic filtering material and preparation method thereof

A technology of oxide ceramics and filter materials, applied in chemical instruments and methods, other chemical processes, etc., can solve problems such as no reports, and achieve the effects of sterilization, algae, decomposition of organic matter, reduction of COD, and resistance to water impact.

Inactive Publication Date: 2011-09-07
GRIMAT ENG INST CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a filter material for water treatment, the treated water can alleviate the corrosion of steel, and there is no report

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A preparation method of an oxide filter material, the steps are as follows:

[0039] (1) Get various related mineral powders or commercially available oxide powders, which are: CaO: 24.8 (parts by weight, the same below), MgO: 8.9, TiO 2 : 4, SiO 2 : 39.9, Fe 2 o 3 : 0.1,K 2 O: 2.7, Na 2 O: 0.6, Al 2 o 3 : 18.6; fully mix, add water to the mixed material and stir, and use a granulator to granulate, so that the particle size of the particles can be distributed in the range of 0.5-5mm according to needs;

[0040] (2) Bake the prepared granules in a muffle furnace, raise the temperature and keep it between 500°C and 1150°C, and keep it warm for 0.5 to 48 hours;

[0041] (3) At the end of the holding time, take a sample after cooling for at least 3 hours;

[0042] (4) Soak the prepared filter material particles in water for 20 hours for cleaning and aging treatment;

[0043] (5) Use an oven to dry the filter material; the temperature of the oven is raised to 110-16...

Embodiment 2

[0045] A preparation method of an oxide filter material, the steps are as follows:

[0046] (1) Get various related mineral powders or commercially available oxide powders, which are: CaO: 33 (parts by weight, the same below), MgO: 13.9, SiO 2 : 23.4, Fe 2 o 3 : 0.1,K 2 O: 1.3, Na 2 O: 0.1, Al 2 o 3 : 7.9; ZnO: 19.5; fully mix, add water to the mixed material and stir, use a granulator to granulate, and the particle size of the resulting particles can be distributed in the range of 0.5-5mm according to needs;

[0047] (2) Bake the prepared granules in a muffle furnace, raise the temperature and keep it between 500°C and 1150°C, and keep it warm for 0.5 to 48 hours;

[0048] (3) At the end of the holding time, take a sample after cooling for at least 3 hours;

[0049] (4) Soak the prepared filter material particles in water for 1 hour for cleaning and aging treatment;

[0050] (5) Use an oven to dry the filter material; the temperature of the oven is raised to 110-160° ...

Embodiment 3

[0052] A preparation method of an oxide filter material, the steps are as follows:

[0053] (1) Get various related mineral powders or commercially available oxide powders, which are: CaO: 60.0 (parts by weight, the same below), MgO: 1, SiO 2 : 10, Fe 2 o 3 : 0.1,K 2 O: 1.3, Na 2 O: 0.1, Al 2 o 3 : 5; fully mix, add water to the mixed material and stir, and use a granulator to granulate, so that the particle size of the particles can be distributed in the range of 0.5-5mm according to needs;

[0054] (2) Bake the prepared granules in a muffle furnace, raise the temperature and keep it between 500°C and 1150°C, and keep it warm for 0.5 to 48 hours;

[0055] (3) At the end of the holding time, take a sample after cooling for at least 3 hours;

[0056] (4) Soak the prepared filter material particles in water for 20 hours for cleaning and aging treatment;

[0057] (5) Dry the filter material in an oven; the temperature of the oven is raised to 110-160° C., and the temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an oxide ceramic filter material and a preparation method. The oxide ceramic filter material comprises the following compositions by weight portion: 10 to 60 portions of CaO, 1 to 60 portions of MgO, 10 to 40 portions of SiO2, 5 to 20 portions of Al2O3, 0 to 15 portions of TiO2, 0 to 25 portions of ZnO and 0.1 to 1 portion of Fe2O3. The basic principle of the filter material is to complete the function of high-efficiency filtration by the function that adsorbed antibacterial materials subjected to physical filtration release active oxygen when reacting with water. The oxide ceramic filter material mainly aims to solve the problem of water quality deterioration caused by various pollutants in water bodies, and simultaneously has strong sterilization and algae removal properties.

Description

technical field [0001] The present invention relates to a filter material for water treatment and its preparation method, in particular to a kind of water treatment which is composed of various oxide ceramic powders and specially treated, and is suitable for water quality of various surface waters and reused reclaimed water. Filter material and its preparation method. The water treatment filter material has the excellent performance of decontamination and deodorization, COD reduction, and sterilization and algae killing performance. Background technique [0002] Filter media play an important role in the water treatment industry. There are many new filter materials reported in the literature, and the general development trend is that more attention is paid to the research and application of oxide ceramic filter materials. However, most of the existing oxide ceramic filter materials mainly solve the effect of physical filtration. The functions of other filter materials foc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/04C04B35/057C04B35/04C04B35/14C04B35/622B01J20/02
Inventor 王振海赵月红林乐耘刘少峰
Owner GRIMAT ENG INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products