Low temperature heat processing method of single feeder head eutectic Al-Si alloy piston material
A low-temperature heat treatment and piston technology, which is applied in the heat treatment process of alloy casting parts, can solve problems such as the inability to guarantee the uniformity of piston hardness, increase production costs, and large temperature field differences, so as to reduce equipment maintenance time and maintenance costs. The effect of reducing production energy consumption cost and heat treatment cost
Inactive Publication Date: 2009-06-03
成都银河动力有限公司
View PDF0 Cites 7 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
In order to reduce the weight of medium and large ordinary piston blanks, the piston blank can be changed from the original two-side riser to a single-side riser. However, the design of the single riser makes the temperature field on both sides of the piston blank quite different. Cast quenching, can not guarantee the uniformity of piston hardness
If the conventional T6 heat treatment process is still used, the energy consumption is high, the production cycle is long, the production efficiency is low, and the production cost is increased; in this way, in order to ensure the implementation of the design measures of the single riser piston for weight reduction, it is urgent to find a way to ensure that the piston A new heat treatment process that reduces production costs and improves production efficiency
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0050] Embodiment 1, the composition of each component (%) in the described alloy is as follows:
[0051] Si: 12.18; Cu: 1.15; Mn: 0.16; Mg: 1.10; Ni: 0.86; Fe: 0.49;
Embodiment 2
[0052] Embodiment 2, the composition of each component (%) in the alloy is as follows:
[0053] Si: 12.62; Cu: 1.12; Mn: 0.15; Mg: 1.09; Ni: 0.88; Fe: 0.39;
Embodiment 3
[0054] Embodiment 3, the composition of each component (%) in the alloy is as follows:
[0055] Si: 12.60; Cu: 1.14; Mn: 0.15; Mg: 1.10; Ni: 0.85; Fe: 0.43;
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
tensile strength | aaaaa | aaaaa |
hardness | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Login to view more
Abstract
A low temperature heat processing method of single feeder head eutectic Al-Si alloy piston material is processed according to following steps: heating a cast piston in a well-type furnace to 480+(-)5 degrees centigrade, keeping the temperature for 1.5 h, then taking out from the furnace; using the water of 50 to 80 degrees centigrade to quench and cool; after quenching, heating the well-type aging furnace to 160+(-) degrees centigrade along the furnace, performing manual aging after keeping temperature for 5 , then taking out from the furnace and performing air cooling, finishing the whole process of heat process of the piston material. Each performance index of the eutectic Al-Si alloy piston material after the low temperature heat processing exceeds the each performance index order by the internal-combustion engine piston technical condition GB / T1148-93. This technical method can guarantees the piston quality and can reduce the manufacturing cost.
Description
technical field [0001] The invention relates to a heat treatment process for alloy casting parts, in particular to a heat treatment method for eutectic Al-Si alloy piston materials. Background technique [0002] The heat treatment of internal combustion engine pistons generally adopts casting waste heat quenching + artificial aging heat treatment process or conventional T6 heat treatment process. In order to reduce the weight of medium and large ordinary piston blanks, the piston blank can be changed from the original two-side riser to a single-side riser. However, the design of the single riser makes the temperature field on both sides of the piston blank quite different. Cast quenching cannot guarantee the uniformity of piston hardness. If the conventional T6 heat treatment process is still used, the energy consumption is high, the production cycle is long, the production efficiency is low, and the production cost is increased; in this way, in order to ensure the implemen...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22F1/043C22C21/02
Inventor 杨庆年何光驰彭明诚徐昌友夏小兵任德忠
Owner 成都银河动力有限公司
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap