Production technology for T-shaped screen cloth

A production process and catalyst technology, which is applied in the field of polyester fabric processing, can solve the problems of warp and weft bending, poor machinability in the back channel, and cloth surface deformation, and achieve the effects of small warp and weft shrinkage, improved production efficiency and stable style.

Active Publication Date: 2009-04-08
CHANGZHOU HONGFA ZONGHENG ADVANCED MATERIAL TECH
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, similar T-shaped mesh fabrics on the market are generally low-stretch products, with surface deformation, serious warp and weft bending, and poor processability in the downstream.
Our company used to weave ordinary polyester filament as the raw material, which has a large shrinkage rate and low strength. The main raw material resin for shaping is also ordinary resin (melamine). It is easy to tear; due to the large shrinkage rate of polyester filament and the loose shape, the weft of the cloth surface is seriously skewed and the cloth surface is loose

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production technology for T-shaped screen cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment one: the process of producing T-shaped cloth or large mesh cloth base cloth

[0015] First of all, the raw materials have passed the inspection and are put into the warehouse. The raw material warehouse requires drying, ventilation, and humidity less than or equal to 80%. The raw material is polyester filament. The strength is greater than or equal to 3.8cN / dtex, the coefficient of variation of the breaking strength is less than or equal to 5.0%, the elongation at break is 24% to 32%, the coefficient of variation of the elongation at break is less than or equal to 12.0%, and the degree of network is 2 to 12 per meter. The boiling water shrinkage rate is 6% to 8%, and the oil content is 0.3% to 1.3%.

[0016] Followed by warping, the warping workshop requires constant temperature and humidity. Silk plate porcelain eye, yarn dividing needle, tension roller, wool meter, yarn dividing needle, storage yarn dividing needle, oiler, herringbone reed dividing needle,...

Embodiment 2

[0020] Embodiment two: the technique of producing green mesh cloth or small mesh cloth:

[0021] This embodiment is all the same as Embodiment 1 in material selection, warping and weaving process, just add specific dyestuff when finalizing and squeegeeing, preheating setting machine oven, batching according to technological requirement: resin, catalyst, dyestuff A, Dye B, dye C, degreaser and water are mixed and stirred in a specific proportion, and put into the slurry tank after stirring evenly. While preparing the slurry, place the base fabric that needs to be shaped on the unwinding machine, install the winding paper tube at the winding place, and guide the base fabric to the slurry slot with the pre-prepared guide cloth. After the oven temperature reaches the specified requirements, Start production, the base fabric passes through the slurry tank for sizing, and then passes through the roller with an air pressure of 0.5KG. During the process of unwinding and sizing, the ba...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention discloses a technology for manufacturing T-shaped mesh fabrics, which comprises the procedures of sorting, warping, and fabric manufacture. The technology also comprises the procedures of: starching by using sizing mixture of resin, accelerant, deoiling agent and water; parching; draw-off and shaping; rolling and warehousing. After the technology is adopted, the manufactured T-shaped mesh fabric has high intensity, little longitude and latitude shrinkage, good verticality, even and well-pressed cloth cover, stable style, and easier rolling; and the warp winding can be up to 1.5 meter, thus being beneficial to transportation and improving manufacturing efficiency.

Description

technical field [0001] The invention relates to a polyester fabric processing technology, in particular to a polyester fabric production and processing technology. Background technique [0002] At present, similar T-shaped mesh fabrics on the market are generally low elastic yarn products, with surface deformation, serious warp and weft bending, and poor processability in the downstream. Our company used to weave ordinary polyester filament as the raw material, which has a large shrinkage rate and low strength. The main raw material resin for shaping is also ordinary resin (melamine). It is easy to tear; due to the large shrinkage rate of polyester filament and the loose shape, the weft of the cloth surface is seriously skewed and the cloth surface is loose. Contents of the invention [0003] The object of the present invention is to provide a production process of T-shaped mesh cloth with stable style and crisp cloth surface. [0004] In order to achieve the above objec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D06C7/02D02G3/22D06M15/00D06M101/32D03D15/283
Inventor 谈亚飞何亚勤季建强刘黎明管朝阳
Owner CHANGZHOU HONGFA ZONGHENG ADVANCED MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com