Rolling technique of lead treated steel

A free-cutting steel and process technology, applied in metal rolling, manufacturing tools, metal rolling, etc., can solve indicators such as head blooming, increase the probability of stacking steel accidents, the yield of lead-containing free-cutting steel, and economic benefits drop and other issues

Inactive Publication Date: 2010-07-21
NANJING NANGANG IND DEV CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the existing rolling process of lead-containing free-cutting steel, due to the temperature difference between the core and the surface of the billet, stress is generated, which will cause the head to bloom during the rolling process, resulting in steel stacking accidents
The standard material type adopted by the rolling mill in the rough rolling area is not suitable for the production of lead-containing free-cutting steel, which increases the probability of pile-up accidents caused by blooming of the head, and reduces the yield rate and economic benefits of lead-containing free-cutting steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] In this embodiment, a square billet with a length of Φ6.5mm, a length of 10-12m, and a billet size of 150mm*150mm is rolled, and a rolling mill is used for rolling. The rolling mill is divided into a rough rolling area, an intermediate rolling area, a pre-finishing rolling area, and a finishing mill. area. There are 8 shifts in the rough rolling area, which are horizontal light-duty rolling mills, numbered 0#~7#; there are 4 shifts in the middle rolling area, which are horizontal light-duty rolling mills, numbered 8#~11#; the pre-finishing rolling area The area of ​​the finishing mill and the finishing mill is a horizontal-vertical alternating rolling mill, with a total of 14 shifts, and the pre-finishing rolling area is numbered 12#~15#. The lead-containing free-cutting steel enters the rolling process after the heating process, and the lead-containing free-cutting steel exits the heating furnace at a temperature of 1140-1190°C. The rolling process includes rough rolli...

Embodiment 2

[0033] In this embodiment, a square billet with a length of Φ8mm, a length of 10-12m, and a billet size of 150mm*150mm is rolled, and a rolling mill is used for rolling. The rolling process includes a rough rolling process, an intermediate rolling process, a pre-finishing rolling process, and a finishing rolling process. .

[0034] Before the rough rolling process, high-pressure water is used to descale the rolled piece. The pressure is 120Mpa, and the scale on the surface of the billet is completely broken. If the scale on the surface of the billet is not cleaned, use a spare rubber water pipe at the 0# rolling mill The surface is descaled with high-pressure water, and a spare rubber water pipe is arranged behind the 4# rolling mill to clean the scale, so that the scale on the surface of the billet is cleaned.

[0035] The rough rolling process is carried out in the rough rolling area of ​​the rolling mill, that is, 0#~7# rolling mill, and the standard material type of 0#~7# ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of metallurgy and relates to rolling process of lead-containing free-machining steel. A rolling mill is used for rolling, in the rough rolling process, the rolling temperature is controlled at 1030-1060 DEG C, the former three-pass material form is reduced 1-3mm based on the standard material form; in the intermediate rolling process, the roll material form is the standard material form, and the rolling temperature is controlled at 980-1030 DEG C; in the pre-finish rolling process, the roll material form is the standard material form, the rolling temperatureis controlled at 1060-1030 DEG C, and the temperature of the rolled piece reaches 1005-1040 DEG C after the pre-finish rolling process; in the finish rolling process, the temperature of the rolled piece in a finishing mill is less than 980 DEG C, the roll material form is the standard material form, and the rolling temperature is controlled at 1020-1050 DEG C. The rolling process can prevent steel heaping caused by the cleavage crack of the cold, hot and frailty susceptible head of the rolled piece, prevent sliding accident caused by the high temperature of the steel, steadily increase the yield of the lead-containing free-machining steel, obviously reduce the waste, and greatly reduce the 100t steel fault time.

Description

technical field [0001] The invention relates to a rolling process in the field of metallurgy, in particular to a rolling process of lead-containing free-cutting steel. Background technique [0002] With the rapid development of industries such as national machining and precision instruments, the requirements for processing materials are constantly increasing, so as to ensure the surface finish of products. The development of lead-containing free-cutting steel satisfies the needs of the processing industry well. In order to smooth rolling The rolling process of lead-containing free-cutting steel wire rod and billet is of great significance to whether the production can be carried out normally. Lead-containing free-cutting steel belongs to S and Pb composite free-cutting steel. The steel contains relatively high S and Pb, and its high-temperature plasticity is poor. Even if the heating process is strictly controlled during production, if the rolling process is not strictly con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21B37/74B21B3/00B21B45/08
Inventor 徐晓春刘文学董洪山林贵明成建兵彭学艺李孝池
Owner NANJING NANGANG IND DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products