Method of manufacturing large-diameter seamless steel tube

A technology of seamless steel pipes and manufacturing methods, applied in the manufacture of steel pipes and the field of manufacturing large-diameter seamless steel pipes

Inactive Publication Date: 2009-02-04
潘克云
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no large-diameter seamless steel pipe with a diameter greater than Φ1016mm produced by thermal expansion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Example 1 Manufacture of a seamless steel pipe with an outer diameter of Φ1219mm, a wall thickness of 16mm, and a length of 12000mm

[0018] (1) Selection and treatment of the main pipe: select a medium-diameter straight seam welded steel pipe with an outer diameter of Φ610mm, a wall thickness of 17.5mm, and a length of 22000mm as the main pipe, and remove internal and external burrs, intermediate frequency weld annealing, pipe body and welding seam flaw detection;

[0019] (2) Thermal expansion: adopt the push-type expansion method, heat the mother pipe to 940°C with intermediate frequency induction, place an expansion mandrel inside, fix the intermediate frequency heating induction coil and the expansion mandrel, and push the host Push the steel pipe through the diameter-expanding mandrel to realize the diameter expansion of the steel pipe. After the first pass of intermediate frequency induction heating, the diameter is expanded to become an intermediate pipe with an...

Embodiment 2

[0022] Example 2 Manufacture of a seamless steel pipe with an outer diameter of Φ1240mm, a wall thickness of 20mm, and a length of 12000mm

[0023] (1) Selection and treatment of the main pipe: select a medium-diameter straight seam welded steel pipe with an outer diameter of Φ610mm, a wall thickness of 17.5mm, and a length of 22000mm as the main pipe, and remove internal and external burrs, intermediate frequency weld annealing, pipe body and welding seam flaw detection;

[0024] (2) Thermal expansion: adopt the pull-type expansion method, heat the main pipe with intermediate frequency induction to above 945°C, place an expansion mandrel inside, keep the steel pipe fixed, and move the intermediate frequency heating induction coil at the same time as the expansion mandrel Move and expand the mandrel under the pull of the drawing machine to expand the diameter of the steel pipe body. After the first pass of intermediate frequency induction heating and heating, the expansion dia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Outer diameteraaaaaaaaaa
Outer diameteraaaaaaaaaa
Wall thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a manufacture method for a seamless steel pipe of a large caliber. In the method, a straight-seam welding steel pipe with an outer diameter of Phi 508mm to Phi610mm is selected as a main pipe, is processed into a main pipe without defects, becomes a crude tube with outer diameter of Phi 620mm to Phi1400mm through at least one thermal diameter expanding, becomes a crude steel pipe an outer diameter of Phi 630mm to Phi1422mm through cold diameter expanding and straightening and finally the finished product of the seamless steel pipe of a large caliber is obtained by carrying out the fine processing like pipe end processing, water pressure test, pipe end flaw detection, pipe body flaw detection, length detecting, weighting as well as spraying, printing and oil coating on the crude steel pipe. The method not only can produce the seamless steel pipe of a large caliber without welding lines, replace UOE and JCOE, but also has a lower cost and a high production efficiency; the product of the invention can be directly used for conveying oil and gas.

Description

technical field [0001] The invention relates to a method for manufacturing a steel pipe, in particular to a method for manufacturing a large-diameter seamless steel pipe, and belongs to the field of iron and steel metallurgy. Background technique [0002] Large-diameter seamless steel pipes refer to steel pipes with an outer diameter of Φ630mm~Φ1422mm, a wall thickness of 6mm~25.4mm, and a length of 6000mm~12000mm, mainly including spiral submerged arc welded pipes, straight seam submerged arc welded pipes, and butt welded pipes for plate rolling machines. . Among them, the forming quality of the butt welded pipe of the plate rolling machine is poor, the precision of the outer diameter of the steel pipe is poor, there are many welds and the efficiency is low, and it is not suitable for mass production. The production efficiency of the spiral submerged arc welded pipe is 1.0-2.0 m / min, but because the length of the weld is 1.5-2.5 times that of the straight seam submerged ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): F16L9/02
Inventor 潘克云
Owner 潘克云
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com