Organic silicon rubber water-proof paint special for sheet metal roofing and method for preparing same

A silicone rubber and waterproof coating technology, which is applied in antifouling/underwater coatings, devices for coating liquid on the surface, coatings, etc., can solve problems such as easy water leakage, many human hidden dangers, and low bonding strength, and achieve Prevent joint breakage, good overall performance, and simple construction

Inactive Publication Date: 2008-12-31
青州市利达防水材料有限公司
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The styrene-butadiene rubber sealing adhesive tape has a short service life, is easy to age, and is easy to leak
However, silicone glue has low bonding strength after solidification and is easy to age. There are many hidden dangers in the construction process, and the waterproof quality is unreliable and easy to leak.
[0007] Therefore, these materials cannot be used in the waterproof field of metal roofs for a long time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 15% water, 5.37% silicone rubber emulsion, 0.5% sodium dodecylbenzenesulfonate emulsion, 26.5% phthalic acid, 15% S-100 emulsifier, 2% 5040 dispersant, 0.02% sodium chloride, Vinyl caproate 10%, isooctyl alcohol 0.01%, bentonite 1%, heavy calcium carbonate 12%, wollastonite 10%, iron oxide 0.5%, silicon dioxide 1%, iron oxide yellow 0.1%, defoamer 1%

[0029] The preparation method comprises the following steps:

[0030] (1) Sodium chloride is dissolved with 5% water, for subsequent use;

[0031] (2) Sodium dodecylbenzenesulfonate and silicone rubber emulsion were mixed, mechanically stirred for 5 minutes, and set aside;

[0032] (3) Mix S-100 emulsifier and phthalic acid, add 5% water to disperse for 5 minutes, then add the sodium chloride solution prepared in step (1), stir mechanically for 10 minutes, and place in the suction tank for Suction, after the suction is completed, disperse for 15 to 20 minutes;

[0033] (4) Add vinyl acetate and 5040 dispersant and pla...

Embodiment 2

[0041] Water 12%, silicone rubber emulsion 4.35%, sodium dodecylbenzenesulfonate emulsion 0.4%, phthalic acid 27%, S-100 emulsifier 12%, 5040 dispersant 2.5%, sodium chloride 0.03%, Vinyl caproate 12%, isooctyl alcohol 0.02%, bentonite 2%, heavy calcium carbonate 13%, wollastonite 12%, iron oxide 0.6%, silicon dioxide 0.5%, iron oxide red 0.1%, defoamer 1.5%.

[0042] The preparation method comprises the following steps:

[0043] (1) Sodium chloride is dissolved with 4% water, for subsequent use;

[0044] (2) Sodium dodecylbenzenesulfonate and silicone rubber emulsion were mixed, mechanically stirred for 5 minutes, and set aside;

[0045] (3) Mix S-100 emulsifier and phthalic acid, add 4% water to disperse for 5 minutes, then add the sodium chloride solution prepared in step (1), stir mechanically for 10 minutes, and place in the suction tank for Suction, after the suction is completed, disperse for 15 to 20 minutes;

[0046] (4) Add vinyl acetate and 5040 dispersant and p...

Embodiment 3

[0055] Water 18%, silicone rubber emulsion 3.5%, sodium dodecylbenzenesulfonate emulsion 0.3%, phthalic acid 16%, S-100 emulsifier 7%, 5040 dispersant 1.84%, sodium chloride 0.04%, Vinyl caproate 15%, isooctyl alcohol 0.02%, bentonite 2%, heavy calcium carbonate 17%, wollastonite 17%, iron oxide 0.8%, silicon dioxide 0.3%, iron oxide red 0.2%, defoamer 1%.

[0056] The preparation method comprises the following steps:

[0057] (1) Sodium chloride is dissolved with 6% water, for subsequent use;

[0058] (2) Sodium dodecylbenzenesulfonate and silicone rubber emulsion were mixed, mechanically stirred for 5 minutes, and set aside;

[0059](3) Mix S-100 emulsifier and phthalic acid, add 6% water to disperse for 5 minutes, then add the sodium chloride solution prepared in step (1), stir mechanically for 10 minutes, and place in the suction tank for Suction, after the suction is completed, disperse for 15 to 20 minutes;

[0060] (4) Add vinyl acetate and 5040 dispersant and place...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Low temperature flexibleaaaaaaaaaa
Login to View More

Abstract

The invention relates to a special metal roofing organo-silicone rubber waterproof paint and a preparation method thereof. The paint is prepared from water, organo-silicone rubber emulsion, sodium lauryl benzenesulfate emulsion, phthalic acid, emulsifier, dispersant, sodium chloride, vinyl acetate, isooctyl alcohol, bentonite, heavy calcium carbonate, aedelforsite, ferric oxide, nano silicon dioxide, pigment and defoamer. The paint is nontoxic and tasteless and is ultraviolet radiation resistant, ageing resistant, waterproof, anticorrosion, thermally insulated, environment-friendly and energy-saving; therefore, the paint is suitable for metal roofing of workshops and factories, and the paint has special waterproofing effect as for important waterproofing complicated roofs.

Description

technical field [0001] The invention relates to a waterproof coating, in particular to a special silicone rubber waterproof coating for metal roofs and a preparation method thereof, belonging to the technical field of building materials. Background technique [0002] Metal roofing is one of the fastest growing segments of the roofing market, especially for residential applications. The construction industry expects aesthetics and longevity from metal roofing materials. [0003] For the waterproof treatment of the metal roof, it should be changed according to the temperature difference of the environment, and the hidden danger of water leakage is very easy to occur at the interface of the metal plate. In the steel structure system, due to the structure itself under the action of external forces such as temperature changes, wind loads, and snow loads, displacements occur at the joints, resulting in hidden dangers of water leakage, etc., so a waterproof material that is truly s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D183/04C09D5/16B05D7/14
Inventor 杨鹏
Owner 青州市利达防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com