Hot-dip galvanizing method for steel products

A technology of hot-dip galvanizing and products, applied in hot-dip galvanizing process, coating, metal material coating process, etc., can solve the problems of excessive consumption of zinc and low efficiency of heating system, so as to reduce zinc consumption and stabilize heat. Loss and effect of reducing the amount of dross

Active Publication Date: 2010-09-15
SHANGHAI YONGFENG HOT DIP GALVANIZING
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a hot-dip galvanizing method for iron and steel products that is applied to defects such as excessive consumption of zinc and low efficiency of the heating system in the conventional process of hot-dip galvanizing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Zinc pot volume: 16.2×2.5×3.6m 3 , Heating method: electric heating on both sides Steel products: 80kg / piece

[0026] 1) Cleaning of black parts: degrease steel products and remove pollutants;

[0027] 2) pickling: immerse the cleaned iron and steel products into the pickling tank, the pickling solution is hydrochloric acid aqueous solution, the working concentration is 10%, the working temperature is room temperature, and the weight ratio of ferric chloride in the pickling solution is controlled to be 150 grams per liter , pickled for 35 minutes, rinsed into ready-made products;

[0028] 3) Helper treatment: the helper solution is an aqueous solution of ammonium chloride and zinc chloride, and its mass ratio is

[0029] Ammonium Chloride 15%

[0030] Zinc Chloride 11%

[0031] Aqueous solution 74%

[0032] The working temperature is 65°C, the pH value is 5, and the content of ferric chloride in the plating flux is controlled at 2.5 g / L.

[0033] Immerse the produ...

Embodiment 2

[0037] Zinc pot volume: 16.2×2.5×3.6m 3 , Heating method: Gas heating on both sides Steel products: 400kg / piece

[0038] 1) Cleaning of black parts: degrease steel products and remove pollutants;

[0039] 2) pickling: immerse the cleaned iron and steel products into the pickling tank, the pickling solution is hydrochloric acid aqueous solution, the working concentration is 12%, the working temperature is room temperature, and the weight ratio of ferric chloride in the pickling solution is controlled to be 180 grams per liter , pickled for 50 minutes, rinsed into ready-made products;

[0040] 3) Helper treatment: the helper solution is an aqueous solution of ammonium chloride and zinc chloride, and its mass ratio is

[0041] Ammonium Chloride 18%

[0042] Zinc Chloride 13%

[0043] Aqueous solution 69%

[0044] The working temperature is 75°C, the pH value is 4.5, and the content of ferric chloride in the plating flux is controlled at 4 g / L.

[0045] Immerse the product t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a hot dip galvanizing method for the steel product, which belongs to the hot dip galvanizing engineering in the metallurgy field. The invention mainly solves the technical problem that the hot dip galvanizing method which is utilized for the steel product for directly aiming at the faults of excessive consumption of the zinc and low efficiency utilization of the heating system in the normal hot dip galvanizing process is provided. The heating way of the dip galvanizing kettle of the invention is side surface heating, thus, the temperature of the liquid zinc can be conveniently controlled, the deposition of the zinc dross can be accelerated, and the zinc quantity taken away by the galvanizing piece can be reduced; because the ferric salt content inside the assistant galvanizing tank is controlled, the zinc dross quantity inside the zinc kettle is reduced; simultaneously, the output per hour is controlled to stabilize the heat loss and reduce the increased zinc consumption caused by temperature variation. Through the progress of the process, the zinc consumption is reduced, the heat energy is fully utilized, the faults of excessive zinc consumption and low efficiency utilization coefficient of the heating system caused by normal process are overcome, the quality is ensured, simultaneously, the resources are saved.

Description

technical field [0001] The invention relates to hot-dip galvanizing in the field of metallurgy, in particular to a hot-dip galvanizing method for iron and steel products. Background technique [0002] The anti-corrosion coating of steel products includes electroplating, hot-dip galvanizing and other methods. The hot-dip galvanizing process of steel products has been a conventional and commonly used method. The energy consumption in the process has also been paid attention to. Because the conventional process is too old, it has caused defects such as excessive consumption of zinc and low efficiency of the heating system. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a hot-dip galvanizing method for iron and steel products that is applied to defects such as excessive consumption of zinc and low utilization of heating systems caused by conventional hot-dip galvanizing processes. [0004] The technical solution pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C2/06C23C2/02
Inventor 朱林龙杨永兴甘富泉张明忠李晋年方振荣陈元祖俞国贞
Owner SHANGHAI YONGFENG HOT DIP GALVANIZING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com