Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Method for modifying nano calcium carbonate and polyolefin master batch containing nano calcium carbonate

A nano-calcium carbonate and polyolefin technology, which is applied in the direction of fibrous fillers and dyed low-molecular organic compounds, can solve the problems of nano-calcium carbonate-filled polyolefin products, different product performance requirements, and poor temperature resistance of stearic acid. , to achieve the effect of improving mechanical properties, improving dispersion properties, and good temperature resistance

Active Publication Date: 2008-09-10
SHANXI LANHUA HUAMING NANO MATERIALS
View PDF5 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Although the above patented methods have improved the dispersion performance of calcium carbonate in polyolefin, but because the application fields of polyolefin products are not the same, the performance requirements of the products are also different, so it is difficult to have a general-purpose nanometer that can meet the requirements of various application fields. Calcium carbonate filled polyolefin products must be improved according to the specific requirements of the application field
The method adopted by most patents is to dry-modify commercial calcium carbonate in a high-speed mixer. Since nano-calcium carbonate is easy to form agglomerates, the effect of this modification method is not obvious
[0007] In addition, the surface of commercially available nano-calcium carbonate is mostly coated with stearic acid or fatty acid salt (such as Chinese patent 01126405.5 or 03817235.6 or 200310122700.X), but the temperature resistance of stearic acid is poor. When it is higher than 180°C, it is easy to turn yellow and change color, and the temperature usually used in plastic processing is more than 200°C, so the nano-calcium carbonate coated with fatty acid or fatty acid salt is not suitable for filling polyolefin products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Get 20L of nano-calcium carbonate slurry (120g / L) whose carbonized average particle diameter is 2nm, adjust the pH to be 8, heat up to about 80 degrees, add 10L distearoyloxyisopropoxyaluminate aqueous solution ( 10g / L), stirred for 4 hours. The calcium carbonate slurry is precipitated and filtered, dried at 80 degrees, and moisture is removed to obtain aluminate-modified nano-calcium carbonate powder.

Embodiment 2

[0035] Get 20L of nano-calcium carbonate slurry (50g / L) whose carbonized average particle diameter is 120nm, adjust the pH to be 10, and heat up to about 80 degrees. 10L of triethanolamine borate solution (5g / L) was added, and the reaction was stirred for 1.5 hours. The calcium carbonate slurry is precipitated and filtered, dried at 80 degrees, and moisture is removed to obtain borate-modified nano-calcium carbonate powder.

Embodiment 3

[0037] Get 10 parts by weight of nano-calcium carbonate powder in Example 1, melt index is 90 parts by weight of polyethylene resin of 0.5, antioxidant 10100.06 parts by weight, polyethylene grafted acrylic acid 0.5 parts by weight (grafting rate 1%) , 1 weight part of polyethylene wax.

[0038] First, put the nano-calcium carbonate, antioxidant and polyethylene wax into the high-mixer and mix them. When the material temperature rises to 120 degrees, mix for another 5 minutes. Then add polyethylene grafted acrylic acid and polyethylene resin, and mix at low speed for 5 minutes. The mixed material is extruded and granulated through a twin-screw extruder to obtain a nano calcium carbonate polyethylene composition.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a modification method of nano calcium carbonate and polyolefin master batch containing the nano calcium carbonate. The modification method comprises the following steps: coupling agent (a boric acid ester or an ester aluminate) is added in nano calcium carbonate slurry at 70 DEG C to 90 DEG C, and the pH value of the system is controlled within 8 to 10 so as to carry out the surface treatment of nano calcium carbonate; and then the nano calcium carbonate is collected after surface treatment. The modification method, which selects novel coupling agent and adopts wet-way coating modification, solves the problem that nano calcium carbonate agglomeration is easy to occur in polyolefin product, thereby making full use of the performance of nano calcium carbonate; moreover, the modification method improves the mechanical property of calcium carbonate-filled polyolefin product and the adaptability to the manufacturing temperature of polyolefin so as to avoid the problem of material surface yellowing caused by the addition of nano calcium carbonate at a higher manufacturing temperature.

Description

technical field [0001] The invention relates to a surface-modified nano-calcium carbonate, a polymer composition containing the nano-calcium carbonate and a preparation method thereof. Background technique [0002] Polyolefin is a general-purpose synthetic resin product widely used at present, and its output ranks first among all kinds of general-purpose plastics. Polyolefin can be used to make various packaging films, agricultural films, heat shrinkable films, cables, pipes, packaging containers, etc. Among them, film products are used in the largest amount. [0003] Calcium Carbonate (CaCO 3 ) is a widely used inorganic filler that can be applied to polyethylene (PE) and polypropylene (PP) products. Due to its small particle size and high surface activity, compared with traditional calcium carbonate, when it is used in polyolefin products, it has little effect on the overall performance of the material. In some cases, it can even improve the material's Certain aspects o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/02C09C3/08C08L23/00C08K9/04
Inventor 杨景辉余蓉蓉陈刚吴秋芳马新胜
Owner SHANXI LANHUA HUAMING NANO MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com