The preparation method of hot melt adhesive omentum

A technology of hot-melt adhesive and adhesive mesh film, which is applied in the directions of melt spinning, film/sheet-like adhesive, mesh, etc., can solve the problems of unfavorable development of circular economy, many hot-melt collagen materials, and high cost. To achieve the effect of reducing production cost, low production cost and improving production efficiency

Active Publication Date: 2012-02-22
SHANGHAI TIANYANG HOT MELT ADHESIVE CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen that the hot-melt adhesive film material is commonly used at present, and its grammage is relatively high, which consumes more hot-melt collagen materials, resulting in higher costs, which is not conducive to the development of circular economy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • The preparation method of hot melt adhesive omentum
  • The preparation method of hot melt adhesive omentum

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Weigh a total of 10kg of copolyamide hot melt adhesive (melt index: 15.4g / 10min) model 6120, first dry it at -20°C for 2.0 hours, then enter it into a vacuum drum for drying and water removal for 2.0 hours, then take it out for measurement Moisture content, when the weight content of the water content is less than 0.8%, put it into a single screw and melt it at 215°C, and add the nucleating agent ultra-fine talcum powder with an average particle size of 8μm according to 0.01% of the net weight of the hot melt adhesive, and mix well Then enter the melt pump and pressurize to 10.0MPa, spray out through a nozzle with an aperture of 0.25mm, control the pressure of the compressed air to 0.45MPa, adjust the flow rate so that the spinning line speed is 6.0m / min, and the hot melt adhesive sprayed out The wire swings on the conveyor belt with a moving speed of 4.50m / min to form a mesh membrane, the average pore size of the mesh is 80 mesh, and the average gram weight is 20g / m 2 ...

Embodiment 2

[0029] Weigh 10kg of copolyamide hot-melt adhesive (melt index: 20.3g / 10min) with brand 6200, firstly dry it at -20°C for 2.0h, then put it into a vacuum drum for drying and dehydration for 2.0h, then take it out for measurement Moisture content, when the water weight content is less than 1.0%, put it into a single screw and melt it at 205°C, and add the nucleating agent ultrafine calcium carbonate with an average particle size of 6μm according to 0.05% of the net weight of the hot melt adhesive, and mix it evenly Enter the melt pump and pressurize to 8.0MPa, spray out through a nozzle with an aperture of 0.20mm, control the pressure of the compressed air to 0.45MPa, adjust the flow rate so that the spinning line speed is 8.0m / mim, and the hot melt adhesive sprayed out The silk forms a mesh membrane on a pendulum with a moving speed of 4.0m / h. The average pore size of the mesh is 90 mesh, and the average gram weight is 28g / m 2 .

[0030] The bevel angle of the compressed air ...

Embodiment 3

[0032] Weigh a total of 10kg of copolyamide hot melt adhesive (melt index: 18.6g / 10min) model 6300, first dry it at -20°C for 2.0 hours, then put it into a vacuum drum for drying and water removal for 2.0 hours, then take it out for measurement Moisture content, when the moisture content is less than 0.8%, it can be put into a single screw and melted at 210°C, and the superfine calcium carbonate with a nucleating agent with an average particle size of 10μm is added according to 0.09% of the net weight of the hot melt adhesive, and mixed evenly Enter the melt pump and pressurize to 8.0MPa, spray out through the nozzle, control the pressure of compressed air to 0.5MPa, adjust the flow rate so that the spinning line speed is 12.0m / min, and the jetted hot-melt glue is moving at a speed of 3.8m / min pendulum forms a screen membrane, the average pore size of the mesh is 100 mesh, and the average weight is 50g / m 2 .

[0033] The bevel angle of the compressed air is 20°.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a hot-melt adhesive omentum, which comprises the steps of melting hot-melt adhesive raw materials, adding a crystallization nucleating agent, extruding, spinning, air-flow drafting, spinning and forming a web, and the like. By adding a certain amount of special nucleating agent and controlling the melting temperature and spinning speed of the hot melt adhesive, a hot melt adhesive film with uniform pore size and stable weight is prepared. The above processes are all continuously completed in one production process, the production efficiency is greatly improved, and it is suitable for industrial production.

Description

technical field [0001] The invention relates to a production method of a hot-melt adhesive omentum, in particular to a method for preparing the hot-melt adhesive omentum by using copolyamide hot-melt adhesive and the like as raw materials. Background technique [0002] Hot-melt adhesive film is a material with corrosion resistance, aging resistance, good thermal stability, good tensile resistance, burst resistance, and good water permeability, so it is widely used in clothing industry, filter materials, shoe leather materials , Packaging materials, etc. It is the most promising emerging industry in the textile industry, known as the "new material" in the textile industry. [0003] Chinese patent CN1071679 provides a method for preparing an adhesive film using EVA, polyester, and polyurethane granular hot-melt adhesives as raw materials. Chinese patent CN1129640 proposes a method for manufacturing a far-infrared hot-melt adhesive film. It is characterized in that the adhes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/00D01D5/098B29D28/00
Inventor 李哲龙朱万育李铁山顾延明
Owner SHANGHAI TIANYANG HOT MELT ADHESIVE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com