Ink-jet printing high luster casting-coating photographic paper

An inkjet printing, high-gloss technology, applied in coatings, pigmented coatings, etc., can solve the problems of unsuitable pigment ink printing, reduced pore openness in coatings, etc., and achieve reliable printing performance and bright colors.

Active Publication Date: 2008-03-26
乐凯胶片股份有限公司
View PDF2 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although the above-mentioned cast-coated photo paper has good gloss, it is suitable for printing high-gloss photos, but because the coating is cast-coated, the openness of the pores in the coating is reduced, and the glossy layer on the surface forms a denser layer due to the drying of the press cylinder. surface, not suitable for printing with pigment ink machines

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ink-jet printing high luster casting-coating photographic paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The lower coating solution of cast-coated photo paper consists of 100 parts of silicon dioxide (SD-640, Beijing Aerospace Saide Powder Material Technology Co., Ltd.), 22 parts of polyvinyl alcohol, 28 parts of polyethylene / vinyl acetate, 8 parts of quaternary ammonium Salt polymer, 3 parts of polypolyol amine, made into a water-based coating solution with a concentration of 20%, coated on photographic base paper by doctor blade coating, and dried to form the lower layer of cast-coated photographic paper.

[0037] Top layer coating liquid formula:

[0038] Aluminum oxide 90 parts

[0039] 5 parts polyvinyl alcohol

[0040] Styrene / maleic anhydride / acrylic acid copolymer emulsion 5 parts

[0041] Polydimethyldiallyl ammonium chloride 3 parts

[0042] BYK-022 0.3 copies

[0043] QT-1 0.2 parts

[0044] 580 parts of deionized water.

[0045] In a container equipped with a stirring device, add 580 parts of water, 90 parts of aluminum oxide and 3 parts of polydimethyldi...

Embodiment 2

[0048] The coating formulation and process of the lower layer of cast-coated photographic paper are the same as in Example 1.

[0049] Top layer coating liquid formula:

[0050] Aluminum oxide 95 parts

[0051] 3 parts polyvinyl alcohol

[0052] Styrene / maleic anhydride copolymer emulsion 5 parts

[0053] Polydimethyldiallyl ammonium chloride 4 parts

[0054] 0.2 parts of isopropanol

[0055] QT-1 0.2 parts

[0056] 600 parts of deionized water.

[0057] In a container equipped with a stirring device, add 600 parts of water, 95 parts of alumina and 4 parts of polydimethyldiallylammonium chloride, stir and disperse to obtain an alumina dispersion with an average particle size of 0.2 μm, and then Add 5 parts of styrene / maleic anhydride copolymer emulsion, stir and mix evenly, add 3 parts of polyvinyl alcohol (10% aqueous solution), 0.2 parts of defoamer BYK-022, 0.2 parts of stripping agent QT-1, and mix well The upper layer coating liquid was obtained.

[0058] Apply th...

Embodiment 3

[0060] The coating formulation and process of the lower layer of cast-coated photographic paper are the same as in Example 1.

[0061] Top layer coating liquid formula:

[0062] Silicon oxide 94 parts

[0063] 4 parts polyvinyl alcohol

[0064] Acrylate / maleic anhydride copolymer emulsion 15 parts

[0065] Polytrimethacrylamide Chloride 3 parts

[0066] 0.8 parts of n-butanol

[0067] QT-1 0.3 parts

[0068] 658 parts of deionized water

[0069] In a container equipped with a stirring device, add 658 parts of water, 94 parts of silicon oxide and 3 parts of polytrimethacrylamide chloride, stir and disperse to obtain a silicon oxide dispersion with an average particle size of 0.25 μm, and then add 15 1 part of acrylate / maleic anhydride copolymer emulsion, stir and mix evenly, add 3 parts of polyvinyl alcohol (10% aqueous solution), 1 part of defoamer n-butanol, 0.2 part of stripping agent QT-1, mix evenly to obtain the upper layer Coating solution.

[0070] Apply the obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The high luster painted photographic paper for ink jet printing is formed through painting two layers of coating fluid containing ink absorbing pigment and passing through metal mirror casting jar. The upper layer of the coating fluid consists of inorganic pigment 90-100weight portions, PVA 3-5weight portions, polymer emulsion 5-30weight portions, assistant 3.5-6weight portions, and deionized water 580-780 weight portions. The high luster painted photographic paper is applied in printing photos with water soluble dye ink and water soluble pigment ink, and has reliable printing performance and capacity of obtaining printed photos with bright colors.

Description

technical field [0001] The invention relates to an ink-jet printing consumable, in particular to a high-gloss cast-coated photographic paper for ink-jet printing. Background technique [0002] Inkjet printing is widely used in various fields because of its fast recording speed, easy colorization, convenient application and no pollution. In the field of imaging, inkjet printing technology has developed rapidly and has become a substitute or complementary material for traditional silver salt photos. Inkjet printing photo paper can be divided into three categories according to the coating process and coating materials: swelling type, microporous type and cast coating type. Swelling type photo paper is coated with water-swellable polymer as the main film-forming material on RC paper (coated with waterproof PE coating on both sides of the base paper) to form a high-gloss swelling type coating. The photo paper is mainly suitable for water-based dyes. Ink printing; microporous in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B41M5/52D21H19/36
Inventor 季玉秋秦长喜冯秀荣
Owner 乐凯胶片股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com