Method for preparing white carbon black by using oil shale ash

A technology for oil mother shale and oil shale ash, applied in the field of preparing silica, can solve the problems of long process route, large acid demand and high cost

Inactive Publication Date: 2007-09-19
NORTHEASTERN UNIV
View PDF0 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Tan Xin et al. studied the preparation of silica by using oil shale deoiling residues. Since this process uses calcination and acid leaching to prepare silica, compared with the process of preparing silica by traditional precipitation method, there are some disadvantages in this process. The process route is long, the energy consumption is large, etc. In addition, the preparation of white carbon black by the acid method requires a large amount of acid, the cost is high, and the iron ions are not easy to remove, thus affecting the whiteness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing white carbon black by using oil shale ash

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0030] Example 1: Weigh 10.0g of kerogen shale ash into a three-necked flask, add 50.0mL of 1.66mol / L NaOH solution, start the electric stirrer, heat to 60°C with an electric heating mantle, and keep the temperature constant for 4 hours. hot filter. After the filtrate was left to stand for a certain period of time, 0.5 g of polyethylene glycol 2000 was added, and HCl was slowly added dropwise to adjust the pH value to 8.5, and at the same time, it was stirred with a magnetic stirrer for 1 hour, then the stirring was stopped, and it was left to stand for 8 hours to obtain a flocculent After precipitation, 3.9g of white carbon black product was obtained after filtration and drying.

example 2

[0031] Example 2: Weigh 10.0g of kerogen shale ash into a three-necked flask, add 50.0mL of 3.30mol / L NaOH solution, start the electric stirrer, heat to 60°C with an electric heating mantle, and keep the temperature constant for 4 hours. hot filter. After the filtrate was left to stand for a certain period of time, 0.5 g of polyethylene glycol 6000 was added, and HCl was slowly added dropwise to adjust the pH value to 7.5, and at the same time, it was stirred with a magnetic stirrer for 1 hour, then the stirring was stopped, and it was left to stand for 8 hours to obtain a flocculent Precipitated, filtered and dried to obtain 4.1g of white carbon black product.

example 3

[0032] Example 3: Weigh 10.0g of kerogen shale ash into a three-necked flask, add 50.0mL of 3.30mol / L NaOH solution, start the electric stirrer, heat to 100°C with an electric heating mantle, and keep the temperature constant for 8 hours. hot filter. After the filtrate was allowed to stand for a certain period of time, 0.5 g of polyethylene glycol 6000 was added, and slowly added dropwise with H 2 SO 4 Adjust the pH value to 5.5, and at the same time stir with a magnetic stirrer for 2 hours, then stop the stirring, let stand and age for 16 hours to obtain a flocculent precipitate, which is filtered and dried to obtain 4.7g of white carbon black product.

[0033] Example 4: Weigh 10.0g of kerogen shale ash into a three-necked flask, add 50.0mL of 3.30mol / L NaOH solution, start the electric stirrer, heat to 100°C with an electric heating mantle, and keep the temperature constant for 4 hours. hot filter. After the filtrate was allowed to stand for a certain period of time, 0.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

A method of manufacturing carbon white using bituminous shale ash comprises the steps of: 1)crushing the bituminous shale ash; 2) mixing the crushed bituminous shale ash with NaOH solution to react for 0.5~24 hours at 20~200 DEG C with an agitating speed of 100~800 r / min; 3)dividing the reaction solution into two parts, an alkali solubility part and an alkali insolubility part, by means of vacuum filtration; 4) adding dispersant into the filtrate, adjusting the pH value to 3.0~10.0 using sulfuric acid or chlorine hydride, and agitating for 0.5~4 hours using a magnetic stirrer; 5) standing and aging for 0.5~24 hours, wherein white floc is generated; 6) filtering; 7)vacuum drying of the filter cake at a temperature of 40~80 DEG C. The present invention produces qualified carbon white with a simple technology and realizes the ecology utilization of bituminous shale ash.

Description

technical field [0001] The invention relates to a method for preparing white carbon black by using oil shale ash as a raw material. Background technique [0002] White carbon black, also known as light silica, scientific name precipitated hydrated silica. It is a high-tech inorganic fine chemical product, the main component is SiO 2 , performance is similar to carbon black, the appearance is white amorphous fine powder. The manufacturing methods of white carbon black include gas phase method, precipitation method and non-metallic ore dissociation method. The gas phase method is also called the combustion method, and the product is gas phase silica. The quality of the product is high, but because the raw material uses expensive SiCl 4 , the requirements for equipment and process are harsh, and the SiO of the obtained silica product 2 ≥99.8%, specific surface area> 300m 2 / g, but its price is expensive and its application is limited. Precipitation method The traditio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B33/113C01B33/12C01B33/18
Inventor 薛向欣李勇冯宗玉段培宁杨合姜涛
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products