Method for producing high titanium type acid pellet vanadium titanium by chain grate - rotary kiln

A vanadium-titanium oxide ball and rotary kiln technology, which is applied in the production process of oxide pellets, can solve problems such as unfavorable use of blast furnaces, difficulties in meeting the requirements for drying and preheating of grate machines, and affecting production smoothness and product quality.

Inactive Publication Date: 2007-07-25
攀枝花钢城集团有限公司球团厂
View PDF0 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because there are abundant vanadium-titanium magnetite concentrates and ordinary magnetite concentrates in the Panxi area, the main raw materials for pellet production are vanadium-titanium magnetite concentrates and ordinary magnetite concentrates with high titanium content. The analysis of concentrate and ordinary magnetite concentrate shows that both vanadium-titanium magnetite concentrate and ordinary magnetite concentrate belong to weak ball-forming materials, and TiO in vanadium-titanium magnetite concentrate 2 The content is as high as about 11%, which has a great impact on the quality of the finished pellets and is not conducive to pelletizing. Even if the pellets are formed, the falling strength of the green pellets is also low, and the quality of the pellets is difficult to meet the requirements of grate drying and preheating. Requirements, resulting in a low burst temperature of green pellets, resulting in a large amount of powder, affecting the smooth flow of production and product quality, and is not conducive to the use of blast furnaces. Therefore, exploring a method for producing high-titanium vanadium-titanium oxide pellets will be conducive to the production of Vanadium-titanium oxide pellets whose quality meets the requirements ensure smooth and stable production of Panzhihua Iron and Steel Blast Furnace

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing high titanium type acid pellet vanadium titanium by chain grate - rotary kiln

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] Examples are given below, and the present invention is further described in conjunction with the examples.

[0009] If a 1.2 million tons / year chain grate-rotary kiln is used to produce high-titanium vanadium-titanium oxide pellets, the physical and chemical indicators of the vanadium-titanium magnetite concentrate and the ordinary magnetite concentrate are first tested, and then the tested vanadium-titanium magnetite concentrate is Ore (the main components are, TFe: 56.5%; TiO 2 : 10.4%; V 2 o 5 : 0.63%; S: 0.29%; P: 0.01%) and ordinary magnetite concentrate (mainly composed of TFe: 60.5%; S: 0.13%; P: 0.05%) are respectively grabbed into the mine bin by a crane, and adjusted The size and speed of the gate valve of the disc feeder control the feeding amount of the magnetite concentrate. The ratio is vanadium-titanium magnetite concentrate: ordinary magnetite concentrate = 7:3, and the amount of bentonite is based on vanadium-titanium magnetite concentrate and ordinar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention discloses a method for producing Ti-rich V-Ti oxidized pellets by chain grate and rotary kiln. The method comprises: mixing vanadic titanomagnetite concentrate with common magnetite concentrate at a weight ratio of 7:3, adding 2.0 wt. % of bentonite, palletizing to obtain 8-16 mm pellets by a disc pelletizer, drying (50-350 deg.C) and pre-heating (500-1000 deg.C) by a chain grate for 12 min, sending dried pellets into a rotary kiln, torrefying at 1150-1300 deg.C and 1.0 r / min for 30-35 min, and cooling torrefied pellets. The obtained Ti-rich V-Ti oxidized pellets have compression strength higher than 1800 N, and TiO2 content of 7.0%, thus can meet the requirement of blast furnace smelting.

Description

technical field [0001] The invention relates to a production process of oxidized pellets, in particular to a method for producing high-titanium vanadium-titanium oxidized pellets by using a grate machine-rotary kiln. Background technique [0002] Pellet is one of the main raw materials in ironmaking production. According to the needs of ironmaking, its shape is mostly spherical with a diameter of 8mm to 16mm. Because there are abundant vanadium-titanium magnetite concentrates and ordinary magnetite concentrates in the Panxi area, the main raw materials for pellet production are vanadium-titanium magnetite concentrates and ordinary magnetite concentrates with high titanium content. The analysis of concentrate and ordinary magnetite concentrate shows that both vanadium-titanium magnetite concentrate and ordinary magnetite concentrate belong to weak ball-forming materials, and TiO in vanadium-titanium magnetite concentrate 2 The content is as high as about 11%, which has a gre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B1/14C22B1/16C22B1/24
Inventor 范云东李坚覃金平汪智德程林森黄璞任朝成
Owner 攀枝花钢城集团有限公司球团厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com