Addition-crosslinking silicone resin compositions

A technology of siloxane resin and composition, which is applied in the direction of instruments, optical components, optics, etc., and can solve the problems of not being able to use heat-sensitive components at the same time

Inactive Publication Date: 2009-05-27
WACKER CHEM GMBH
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, heat-sensitive components such as electronic components or molds of organic polymer materials cannot be used at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0136] Put 100 parts with (PhSiO 3 / 2 ) 0.43 (MeViSiO) 0.14 (MeHSiO) 0.18 (Me 3 SiO 1 / 2 ) 0.25 Composition of polysiloxane with 20 parts (MeViSiO) 0.9 (Me 2 SiOH) 0.1 Composition of polysiloxane, 6 parts with (MeHSiO) 4 Composition of polysiloxane and 0.04 parts (based on platinum), platinum-1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex as a hydrosilylation catalyst Mix together. A mixture with a viscosity of 520 cSt at a temperature of 25°C was prepared, and the mixture was cured in a mold at a temperature of 150°C for 1 hour. The formed molded product is transparent like glass, and its Shore D hardness is 64.

Embodiment 2

[0140] Put 100 parts with (PhSiO 3 / 2 ) 0.43 (MeViSiO) 0.14 (MeHSiO) 0.18 (Me 3 SiO 1 / 2 ) 0.25 Composition of polysiloxane with 30 parts (MeViSiO) 0.9 (Me 2 SiOH) 0.1 Composition of polysiloxane, 6 parts with (MeHSiO) 4 Composition of polysiloxane and 0.04 parts (based on platinum), platinum-1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex as a hydrosilylation catalyst Mix together. A mixture with a viscosity of 450 cSt at a temperature of 25°C was prepared. The mixture was cured in a mold at a temperature of 150°C for 1 hour. The resulting molded product is transparent like glass, and its Shore D hardness is 52.

Embodiment 3

[0142] Put 100 parts with (PhSiO 3 / 2 ) 0.43 (MeViSiO) 0.14 (MeHSiO) 0.18 (Me 3SiO 1 / 2 ) 0.25 Composition of polysiloxane with 36 parts (MeViSiO) 0.9 (Me 2 SiOH) 0.1 Composition of polysiloxane, 6 parts with (MeHSiO) 4 Composition of polysiloxane and 0.04 parts (based on platinum), platinum-1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex as a hydrosilylation catalyst Mix together. A mixture with a viscosity of 390 cSt at a temperature of 25°C was prepared. The mixture was cured in a mold at a temperature of 150°C for 1 hour. The resulting molded product is transparent like glass, and its Shore D hardness is 40.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

Addition crosslinking siloxane resin composition, which comprises (1) 100 parts by weight of general formula R 1 a R 2 b R 3 c SiO (4-a-b-c) / 2 (1) polyorganosiloxane, (2) 50 to 200 parts by weight of general formula R 1 d h 2 e R 3 f SiO (4-d-e-f) / 2 The polyorganosiloxane of (II), or (3) 200 parts by weight of general formula R of (substituting components (1) and (2)) 1 g R 2 h R 3 i h k SiO (4-g-h-i-k) / 2 (III) polyorganosiloxane, (4) 1 to 100 parts by weight of general formula R 1 l R 2 m R 3 n SiO (4-l-m-n) / 2 (IV) Alkenyl-rich polyorganosiloxane, and (5) 1 to 100 parts by weight hydrogen-rich formula R (additionally or in place of component (4)) 1 o h p R 3 q SiO (4-o-p-g) / 2 (V) a polyorganosiloxane, and (6) a sufficient amount of catalyst.

Description

Technical field [0001] The present invention relates to addition-crosslinking silicone resin compositions. Background technique [0002] Add-crosslinking siloxanes have long been known in the elastomer industry, such as RTV-2 rubber, liquid rubber, and addition-crosslinking thermal rubber. The characteristics of these materials are: after curing, their hardness is in the range of Shore A or in the range of <20 Shore D. [0003] The corresponding cross-linkable material is a product including at least two components, which always contain cross-linking functional groups Si-H and Si-vinyl groups, respectively. [0004] US 2002 / 0161140 A1 describes an addition-crossover biphenyl siloxane resin composition, the hardness of the cured siloxane resin is in the range of Shore D>60. However, in order to avoid too long curing time, the curing temperature must be 200°C. Therefore, heat-sensitive components, such as electronic components or molds made of organic polymer materials, canno...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/04C08J3/24C08J5/00C08L83/07C08G77/12C08L83/05G02B1/04
CPCC08G77/70C08G77/18G02B1/04C08G77/16C08G77/20C08G77/12C08L83/04C08L83/00
Inventor 格哈德·施泰格沃尔夫冈·沙滕曼
Owner WACKER CHEM GMBH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com