Chemical coprecipitation preparation of nano-rave-earth blend AgSnO2 electric contacting alloy

A technology of chemical co-precipitation and nano-rare earth, which is applied in circuits, electrical switches, electrical components, etc.

Inactive Publication Date: 2009-04-22
XI'AN POLYTECHNIC UNIVERSITY
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above technologies have certain limitations in terms of electrical properties of electrical contact materials, contact burnout rate and service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chemical coprecipitation preparation of nano-rave-earth blend AgSnO2 electric contacting alloy
  • Chemical coprecipitation preparation of nano-rave-earth blend AgSnO2 electric contacting alloy
  • Chemical coprecipitation preparation of nano-rave-earth blend AgSnO2 electric contacting alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Example 1, preparation of SnO by co-precipitation 2 / MgO / La precursor, at 400 ° C, 1 h to prepare nano-amorphous SnO with a weight ratio of 10:1:2 2 / MgO / La chemical co-precipitation mixed oxide powder. Silver powder (Ag) with a weight ratio of 88%, SnO with 12% 2 / MgO / La hybrid powders were high energy ball milled in air environment. Vibration ball mill is adopted, the ratio of ball to material is 20:1, the ball milling time is 1 hour, and the vibration frequency is 200s -1 . The ball-milled powder is cold-pressed at 200MPa to form an embryo, hot-pressed and sintered at 550°C and 200MPa, and then re-pressed and annealed to shape. Prepared AgSnO 2 / MgO / La contact alloy is nano-amorphous SnO 2 / MgO / La particles are uniformly distributed in the Ag matrix.

Embodiment 2

[0026] Embodiment 2, coprecipitation prepares SnO 2 / MgO / La precursor, fired at 550°C for 1h to prepare SnO with a weight ratio of 7:2:5 and a nanocrystalline particle size of 1-20nm 2 / MgO / La chemical co-precipitation mixed oxide powder. The weight ratio of 88% Ag powder and 12% SnO 2 / MgO / La hybrid powders were high-energy ball milled in a nitrogen atmosphere. A stirring high-energy ball mill is used with a ball-to-material ratio of 40:1 and a speed of 300 rpm. The ball milling time was 0.5 hours. The ball-milled powder is cold-pressed at 400MPa to form an embryo, sintered at 750°C, and then re-pressed and annealed to shape. Nanoscale SnO 2 AgSnO / MgO / La particles uniformly distributed in Ag matrix 2 / MgO / La contact alloy.

Embodiment 3

[0027] Embodiment 3, coprecipitation prepares Ag, SnO 2 , MgO / Ce precursor, fired at 450°C for 1h to obtain a weight ratio of 88% Ag, 10% SnO 2 , 0.1% MgO, 1.9% Ce oxide is nano-amorphous mixed powder, which is cold-pressed at 400MPa to form an embryo, hot-pressed and sintered at 600°C and 200MPa, and then annealed by multiple pressure to prepare Ag / SnO 2 / MgO / Ce homogeneously blended nano-amorphous contact alloy.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is relates to components of electric contact material and fabricating technique. Weight percentage of each component is a following: 70-95% Ag, 2.5-20% stannic oxide, 0.025-1% magnesia and 0.025-9% lanthanum or cerium. Compound powder of Ag, SnO2, MgO, La or Ce in Nano amorphous or crystalloid is prepared through high-octane ball milling. Structure, decentrality and dimensional stability of Nano granules are improved by adding lanthanide series into material. Thus, formability and electrical property of electric contact alloy are improved as well as ablation rate of contact is reduced and service life is increased.

Description

technical field [0001] The invention belongs to silver-based electrical contact materials, in particular to preparation of nano rare earth blended AgSnO by chemical co-precipitation of electrical contact materials 2 electrical contact alloys. Background technique [0002] At present, the known silver-based electrical contact materials: 1. Prepare nano-SnO by high-energy ball milling 2 Silver-based electrical contact alloy (patent application number 00135475.2); 2. Nano SnO 2 / Fe 2 o 3 Blend-doped silver-based electrical contact alloy and its preparation method (patent application number 2003101222631): 3. Preparation of nano-SnO by sol-gel method 2 , ZnO, TiO 2 and rare earth components to prepare nano-silver-based electrical contact alloys (patent application number 02146696.3): 4. Use doped metal oxides (including SnO 2 , ZrO, ZnO, TiO, MnO, WO, etc.) silver-based electrical contact alloys (patent application number 03100430.X), and silver-based electrical contact ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01H1/02H01H11/04
Inventor 王俊勃杨敏鸽陈立成张燕李英民丁秉钧王鹏飞
Owner XI'AN POLYTECHNIC UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More