A technology of magnetic flux density and sintering method, which is applied in the sintering field of MnZn ferrite with high saturation magnetic flux density, can solve the problems of insufficient, unpublished oxygen partial pressure, and high price of NiO, so as to reduce costs and increase saturation magnetic flux density , The effect of simple sintering process

Active Publication Date: 2009-03-04
HENGDIAN GRP DMEGC MAGNETICS CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, with the miniaturization of electronic equipment and high output power of power supplies, and in order to be used normally under high temperature conditions, the saturation magnetic flux density (Bs) of ordinary MnZn ferrite materials, especially high temperature Bs, is not enough; So more and more people come to research and develop MnZn ferrite with high saturation magnetic flux density (Bs)
[0004] Chinese patent application (CN1294099A) discloses a kind of ferrite material, it improves the Bs of MnZn ferrite by adding NiO in the material, but because the price of NiO is relatively high, greatly improves the manufacture of MnZn ferrite material cost, thereby reducing the market competitiveness of the product
[0005] Another example is Chinese patent application (CN1224224A) discloses a kind of ferrite material, by Fe 2 o 3 , MnO, ZnO raw material composition is limited to a certain range, by controlling the oxygen partial pressure of the molded body N 2 -O 2 Under the atmosphere of mixed gas, a kind of MnZn ferrite with high Bs was prepared by sintering at the sintering temperature of 1300°C for 5 hours, but the patent application did not disclose the specific value of the oxygen partial pressure during sintering, but the oxygen partial pressure It plays a key role in sintering MnZn ferrite with high saturation magnetic flux density, so those skilled in the art cannot obtain MnZn ferrite with high saturation magnetic flux density according to the content recorded in this patent application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] will consist of 53mol% Fe 2 o 3 , 11mol% ZnO, 36mol% MnO raw materials were mixed in a sand mill for 1 hour, and then pre-fired at 800°C for 2 hours. Add auxiliary component in above-mentioned calcined material, the auxiliary component (wt%) that adds is: the CaCO of 0.1wt% 3 , 0.03wt% Nb 2 o 5 , 0.03wt% ZrO 2 , 0.1wt% SnO 2 . Then carry out secondary sand grinding for 2 hours, spray granulation after adding PVA, and shape it into a standard annular magnetic core of Φ25 for sintering. In the sintering process, the first heating stage is from room temperature to 600°C, the heating time is 4 hours, and the heating is carried out in the atmosphere; the second heating stage is from 600°C to 1300°C , the heating time is 6 hours, and the oxygen partial pressure in the heating stage is maintained at 0.5%; at 1300°C for 5 hours, the oxygen partial pressure is maintained at 6%; The process maintains an equilibrium oxygen partial pressure.

[0023] The Bs of the sample w...

Embodiment 2

[0027] will consist of 53.8mol% Fe 2 o 3 , 7mol% ZnO, 39.2mol% MnO raw materials were mixed in a sand mill for 1 hour, and then pre-fired at 850°C for 2 hours. Add auxiliary component in above-mentioned calcined material, the auxiliary component (wt%) that adds is: the CaCO of 0.12wt% 3 , 0.02wt% Nb 2 o 5 , 0.04wt% ZrO 2 . Then carry out secondary sand grinding for 2 hours, spray granulation after adding PVA, and shape it into a standard annular magnetic core of Φ25 for sintering. In the sintering process, the first heating stage is from room temperature to 800°C, the heating time is 5 hours, and the heating is carried out in the atmosphere; the second heating stage is from 800°C to 1320°C , the heating time is 5 hours, and the oxygen partial pressure in the heating stage is maintained at 0.1%; at 1320°C for 3 hours, the oxygen partial pressure is maintained at 8%; finally, the temperature is lowered from 1320°C to 100°C, and the cooling time is 11 hours. The process ma...

Embodiment 3

[0032] will consist of 53.2mol% Fe 2 o 3 , 9mol% ZnO, 37.8mol% MnO raw materials were mixed in a sand mill for 1 hour, and then pre-fired at 900°C for 2 hours. Add auxiliary component in above-mentioned calcined material, the auxiliary component (wt%) that adds is: the CaCO of 0.13wt% 3 , 0.015wt% Nb 2 o 5 , 0.05wt% ZrO 2 . Then carry out secondary sand grinding for 2 hours, spray granulation after adding PVA, and shape it into a standard annular magnetic core of Φ25 for sintering. In the sintering process, the first heating stage is from room temperature to 600°C, the heating time is 1 hour, and the heating is carried out in the atmosphere; the second heating stage is from 600°C to 1150°C , the heating time is 3 hours, and the oxygen partial pressure in the heating stage is maintained at 2%; at 1150°C for 8 hours, the oxygen partial pressure is maintained at 10%; The process maintains an equilibrium oxygen partial pressure.

[0033] The Bs of the sample was tested wit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention provides a sintering method for a high-saturated flux density MnZn ferrite including the following steps: a, a first temperature-rising stage, b, a second temperature-rising stage, c, a heat preservation stage, d, temperature-reducing, which can increase the saturated flux density of MnZn ferrite greatly by controlling the temperature and oxygen partial pressure during the sintering process, besides, no expensive asistant components are needed in the preparation process.

Description

technical field [0001] The invention relates to a sintering method of MnZn ferrite, in particular to a sintering method of MnZn ferrite with high saturation magnetic flux density. Background technique [0002] MnZn ferrite can be used as a soft magnetic material and is widely used in power transformers, choke coils and other communication equipment and household appliances industries. When used in the power transformer core used in the frequency range of 100kHz to hundreds of kHz, compared with other ferrite materials and metal soft magnetic materials, MnZn ferrite has small power consumption and large saturation flux density, so MnZn ferrite Oxygen is an important material as a transformer core. [0003] However, with the miniaturization of electronic equipment and high output power of power supplies, and in order to be used normally under high temperature conditions, the saturation magnetic flux density (Bs) of ordinary MnZn ferrite materials, especially high temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/10H01F1/34
Inventor 颜冲吕东华包大新何时金
Owner HENGDIAN GRP DMEGC MAGNETICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com