Dacron glass fiber dipped canvas and its preparation method

A glass fiber, dipped canvas technology, applied in the direction of fabrics, textiles, textiles and papermaking, can solve the problems of poor flexural properties of inorganic glass fibers, and achieve the effects of low price, improved heat resistance and reduced cost

Inactive Publication Date: 2008-12-31
刘显宝
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flexibility of inorganic glass fibers is worse than that of synthetic fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dacron glass fiber dipped canvas and its preparation method
  • Dacron glass fiber dipped canvas and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0052] Below in conjunction with specific example the present invention is described in further detail, the preparation method of a kind of 200 type polyester fiberglass dipped canvas (hereinafter represented by EG200 code name) among the present invention is as follows:

[0053] Preparation of warp and weft materials:

[0054] 1. Warp material: 1100dtex-3300dtex polyester industrial filament can be used. According to the variety requirements of customers, ordinary type, high-strength type, low-shrinkage type and high-modulus low-shrinkage type can be used for twisting production.

[0055] Type EG200 uses 1100dtex high-modulus low-shrinkage polyester industrial filament. According to the strength requirements of type 200, it needs to use 2 strands, that is, 1100dtex×2, and the twist range is 100±15 twists / m;

[0056] 2. Weft material: 150tex-2000tex modified glass fiber filaments. When spinning glass fiber, the following requirements are put forward. It is glass fiber of alk...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polyester glass fiber dipped canvas and a preparation method thereof. Silk is woven into canvas. The single fiber diameter of glass fiber filaments in weft direction is ≤12μm. The glass fiber is a modified glass fiber filament, based on the total weight of the modified glass fiber filament, it consists of: SiO 2 : 50%~56%, Al 2 o 3 : 12%~16%, B 2 o 3 : 6%~9%, MgO: 2%~4%, CaO: 16%~20%, Na 2 O or / and K 2 O: 0.15% to 0.4%, Fe 2 o 3 : 0.1%~0.4%, TiO 2 or / and ZrO 2 : 0~0.1%, F 2 : 0.1% to 0.3%. The raw material cost is low, the preparation process is simple and reasonable, and the product has high heat resistance and dimensional stability.

Description

technical field [0001] The invention relates to a rubber conveyor belt frame material dipped canvas and a manufacturing process thereof, in particular to a polyester glass fiber dipped canvas and a preparation method thereof. Background technique [0002] With the rapid development of the world's industry, it has also brought about the shortage of resources. As the main energy source, oil is an important material that countries all over the world attach importance to. Nylon and polyester synthetic fibers are the end products of petroleum, and their prices are also relatively high. The main skeleton material used in the rubber conveyor belt industry is exactly the dipped canvas interwoven with nylon, polyester, and polyester-nylon. [0003] Existing nylon, polyester, and nylon dipped canvases are produced from industrial filaments through twisting, weaving, and dipping. They have the advantages of high strength and good flexibility, but they also have heat resistance and sta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06N3/18D03D15/02D03D15/267D03D15/283D03D15/50D03D15/513
Inventor 刘显宝
Owner 刘显宝
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com