Composite calcium sulphonate lubricating grease

A technology for compounding calcium sulfonate and synthesizing calcium sulfonate, applied in the field of lubricating grease, can solve the problems of easy lubrication accidents, short service life, thinning, etc., and achieve excellent water resistance, high extreme pressure performance and less loss. Effect

Active Publication Date: 2008-01-02
辽宁海华科技股份有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the lubricating grease used for bearings of steel rolling equipment is mainly based on extreme pressure lithium base grease or extreme pressure lithium complex grease, but due to the limitation of the structure of this kind of grease soap, the grease is often lost or thinned by water washing during use , This brings a lot of inconvenience to the user, such as short service life, frequent greasing and maintenance, bearings are prone to wear due to lack of sufficient grease, or rust due to the entry of a large amount of water, so lubrication accidents are prone to occur
This affects normal production, and the economic losses caused by accident maintenance are staggering in rolling mills.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Composite calcium sulfonate grease, based on high-viscosity mineral oil, composite soap composed of high-alkaline value synthetic calcium sulfonate and other high and low molecular acid thickeners, and added with antioxidants, extreme pressure agents, and oily agents , wherein the proportioning by weight of each component is as follows:

[0032] 150BS: 34

[0033] 400SN: 36

[0034] High base number synthetic calcium sulfonate: 10

[0035] 12 hydroxystearic acid: 10

[0036] Glacial acetic acid: 3

[0037] Boric acid: 4

[0038] Calcium Hydroxide: 6

[0039] Diphenylamine: 1

[0040] Phosphite compounds: 3

[0041] Benzotriazole fatty amine salt compounds: 2

[0042] The production process of complex calcium sulfonate grease is as follows: add base oil, high alkali value synthetic calcium sulfonate, glacial acetic acid, boric acid and calcium hydroxide at 100°C for conversion and saponification reaction according to the specified weight ratio, and then add fatty...

Embodiment 2

[0044] Composite calcium sulfonate grease, based on high-viscosity mineral oil, composite soap composed of high-alkaline value synthetic calcium sulfonate and other high and low molecular acid thickeners, and added with antioxidants, extreme pressure agents, and oily agents , wherein the proportioning by weight of each component is as follows:

[0045] 150BS: 36

[0046] 400SN: 20

[0047] High base number synthetic calcium sulfonate: 15

[0048] 12 hydroxystearic acid: 12

[0049] Glacial acetic acid: 4

[0050] Boric acid: 4

[0051] Calcium Hydroxide: 7.0

[0052] Diphenylamine: 0.5

[0053] Phosphite compounds: 4

[0054] Benzotriazole fatty amine salt compounds: 3

[0055] The production technology of composite calcium sulfonate grease is the same as embodiment 1.

Embodiment 3

[0057] Composite calcium sulfonate grease, based on high-viscosity mineral oil, composite soap composed of high-alkaline value synthetic calcium sulfonate and other high and low molecular acid thickeners, and added with antioxidants, extreme pressure agents, and oily agents , wherein the proportioning by weight of each component is as follows:

[0058] 150BS: 20

[0059] 400SN: 27

[0060] High base number synthetic calcium sulfonate: 20

[0061] 12 hydroxystearic acid: 16

[0062] Glacial acetic acid: 5

[0063] Boric acid: 3

[0064] Calcium hydroxide: 7.5

[0065] Diphenylamine: 0.8

[0066] Phosphite compounds: 6

[0067] Benzotriazole fatty amine salt compounds: 4

[0068] The production technology of composite calcium sulfonate grease is the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A composite lubricating oil with high-temp performance, shearing stability, water-proofing nature, extreme-pressure performance and viscosity is prepared through proportionally mixing high-viscosity mineral oil with calcium sulfonate, glacial acetic acid, boric acid and calcium hydroxide, convension and saponifying reaction, adding fatty acid, high-temp (180 deg.C) reaction, cooling to 110 deg.C, adding antioxidizing agent, extreme-pressure agent and oily agent, homogenizing and filter.

Description

technical field [0001] The invention relates to a kind of lubricating grease which takes high-viscosity mineral oil as base oil and uses synthetic calcium sulfonate with high alkali value, fatty acid, boric acid, glacial acetic acid and calcium hydroxide as thickeners, and the compound calcium sulfonate lubricating grease. Background technique [0002] With the rapid development of the metallurgical industry, the working conditions of equipment in rolling mills are becoming more and more harsh. Most of the equipment bearings in medium-sized factories, bar factories, medium plate factories, and hot-rolled strip mills operate under high temperature, high speed, heavy load, water, Running in a dusty environment puts forward higher requirements on the performance of the grease used in the rolling equipment bearings. [0003] At present, the lubricating grease used for bearings of steel rolling equipment is mainly based on extreme pressure lithium base grease or extreme pressure ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M135/10
Inventor 刘鹏
Owner 辽宁海华科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap